Background: Calcium hydroxide and calcium-silicate materials used as direct pulp capping materials. The aims of this in vitro study is to compare among these materials in, the calcium ion release and pH change in soaking water after immersion of materials’ specimens in deionized water. Also Solubility and water sorption of materials’ specimens measured after soaking time. Calcium-silicate materials used were Biodentine, TheraCal and MTA Plus. Materials and methods: Four materials used in this study; Urbical lining (as control group), Biodentine, TheraCal and MTA Plus. Ten discs fabricated from each tested material, by using plastic moulds of 9 mm diameter and 1 mm thickness. Each specimen was immersed in 10 ml of deionized water and stored at 37ºC using incubator for 3 hr, 24hr, 14 days and 30 days as a sequence. The amount of calcium ion (Ca+2) released in soaking water was measured in each tube using atomic absorption spectrophotometer. Also pH analysis for soaking water measured by using pH meter. For solubility and water sorption measurement, the specimen (n=10) weighed with precision weighing scale before immersion in deionzed water to determine the initial Weight (W1) and immediately after weighing immersed in 10 mL of deionized water at 37 °C for 1 week using an incubator, then removed and weighing again (W2). The samples blotted dry using filter paper and dehydrated in an oven at 37 °C for 24 hr. and weighed again (W3). Then percentage of solubility and water sorption were determined. Data obtained were analyzed using one-way ANOVA and Tukey tests at 0.05 significant levels. Results: Statistical analysis showed highly significant differences (P<0. 05) among tested materials and in all tests (Ca+2 release, pH change, solubility and water sorption). Biodentine showed higher calcium ion released at four soaking time (3 hr, 24hr, 14 days and 30 days), with non significant difference with TheraCal and highly significant difference with MTA Plus and control group at 24 hr. immersion time; While MTA Plus showed non significant difference with control group at 24 hr. Less amount of calcium released was in control group. All tested materials induced alkalization of the soaking water that decreased with time. Means of solubility and water sorption showed that MTA Plus and biodentine had higher solubility in comparison with control group, while TheraCal showed less solubility than control group. The results of water sorption showed that less sorption percentage occurred in control group in comparison with other groups. Conclusion: calcium-silicate materials released more Ca+2 with time than calcium hydroxide. TheraCal showed less solubility and higher water sorption in comparison with control group. Biodentine and MTA Plus showed higher solubility and water sorption in comparison with TheraCal and control group.
The current research aims to identify the level of strategic orientation and its dimensions (vision, mission, goals, and values) in the Iraqi National Security Service (INSS). The researchers followed the descriptive analytical approach as one of the forms of analysis and organized scientific interpretation to describe a specific phenomenon or problem, adopting the form questionnaire being the main source in collecting data and preparing for this. Based on the program of the Statistical Package of Social Sciences (SPSS 26) to analyze the data and come up with the final research results to identify the opinions of the intended sample on the subject of research, and the questionnaire of (20) paragraphs included the search variable, and was
... Show MoreThe compound chalcon originally is extracted form some plant and herbs, the studies of the antiviral activity of this compound were done in two cell line cultures the L2OB and RD, the compound relatively non toxic to both cell lines of the concentration of 32?g/ml or less ,the compound have significantly anti poliovirus activity in both L2OB cell line and RD cell line, we find that the concentration of 0.03 ?g/ml or more inhibit the 100TCDID50 of the poliovirus .The therapeutic index(TI)used in this study to evaluate the drug activity ,( TI is the ratio of dose of drug which is just toxic to the cells to the does which is just inhibit the viral multiplication, if this index more than one the margin of safety of drug is according great ) .In
... Show MoreThe protozoan parasite Entamoeba histolytica is a causative agent of amoebiasis, where it causes millions of cases of dysentery and liver abscess each year. Metronidazole is a drug of choice against amoebiasis. The drug is a choice because of its efficacy and low cost, but at the same time it causes several adverse side effects; therefore, it is important to find effective medications to treat amoebiasis without any complications or any side effects. The aim of this study is to evaluate the effectiveness of different concentrations (50, 75 and 100 µg/ml) of silver nanoparticle (AgNPs) against trophozoites stages of E. histolytica in vitro. The results showed a significant decrease (p ? 0.05) in numbers of trophozoites stages after treated
... Show MoreIn vitro antifungal susceptibility test of itraconazole was carried out against 38 isolates from nails, skin, oral cavity, vagina and wounds, This study was done in Ramadi Teaching Hospital in period from January to August 2010. According to the National Committee for Clinical Laboratory Standard (NCCLS ) M 27- A by using the broth dilution method. Inoculum size was 1-5X103 CFU/ ml, while final concentrations of itraconazole ranged from 0.025 – 6.4 μg / ml by using RPMI – 1640 broth media and the fungus was incubated at 35 oC. No resistant stain was recorded. MIC ranged from 0.05 – 6.4 μg / ml and the Mean ± SEM was 0.89 ± 0.28. MIC for nail isolates was 0.05 –
... Show MoreConducted the study of the experimental conditions of the interaction of glass the visual Alpmuth containing 15% Mall of zinc with phosphoric acid ????? various degrees of thermal and clip areas prone to interact different way turntable
The objective of this study was to investigate the drought stress and plant density possibility on water productivity and grain yield of maize (Zea mays L.) (Planting Baghdad 3 synthetic varieties), Field experiment was conducted at Abu Ghraib Research Station (Baghdad) during spring and Autumn seasons of 2016 using a randomized complete block design arranged in split plot with three replications. Three irrigation treatment included: irrigation after depletion 50% of available water (T1), irrigation after depletion 75% of available water (T2) and irrigation after depletion 90% of available water (T3) in the main plots and three plant density which were: 1 seeds hill-1 (D1) giving a uniform plant density of 66666 plants ha-1 , 2 seeds hill1
... Show MoreSix house-hold Abyssinian pumps distributed in different villages of Mansoura (Mans-I, Mans-II and Mans-III) and Talkha (Talk-I, Talk-II and Talk-III) cities, Egypt, have been selected for regular seasonal water quality assessment during 2017. Water samples have been collected within the mid-periods of four seasons Standard assessment tools were employed for the integrated water quality assessment including Water Quality Index (WQI) and ISO standard algal toxicity test. WQI displayed remarkable local and seasonal variations with excellent (≥ 90) and good (70 - 89) only recorded for water samples collected from Mans-I pump located in sparsely populated area and far 50 meters only from the eastern (Damietta) branch of Nile River. WQI of
... Show MoreCeramic body as a refractory was prepared by using shamoot, which is prepared by firing kaolin Duekhla at 1450 ºC at 2hr ,Flint clay ,Asbestos fiber(Anthophylite type)and Sodium silicts,Phosphoric acid solution as a binder . After miling, siving ,and mixing ,samples were formed, followed that drying, firing at different temperature. Phyical ,thermal and mechanical properties were measured .The conclusion behind the results that the refractory prepared from; 37.5% shamoote,25% Asbestos ,37.5% Flint clay and Phosforic acid solution fired at 1300 ºC gave a refractory material having melting temperature ;1490 ºC, thermal shock resistance 7 cycle, thermal conductivity 2.1w/m2.K, apperan
... Show MoreABSTRACT Background: Color changes that are detectable to human eye can affect the esthetic appearance of ceramic veneers. The purpose of this study was to evaluate and compare the effect of artificial accelerated aging on the color of ceramic veneers cemented with different resin cements. Materials and Methods: Sixty discs were prepared with 0.5 mm thickness, 30 discs made from IPS e.max press (Ivoclar Vivadent) and 30 discs were made from VITA Enamic (VITA Zahnfabrik). The discs were cemented with three resin cements: Variolink Veneer MV 0 shade (Ivoclar Vivadent), Rely X veneer Translucent shade (3M ESPE) and NX3 Nexus Clear shade (Kerr Corporation) with 0.1 mm thickness. The spectrophotometer Easyshade Advance was used to measure the co
... Show More