AA3003-H14 aluminum alloy plates were welded by friction stir welding and TIG welding.
Fatigue properties of the welded joints were evaluated based on the superior tensile properties for
FSW at 1500 rpm rotational speed and 80 mm/min welding speed. However, there is not much
information available on effect of welding parameters with evolution of fatigue life of friction stir
welds. The present study experimentally analyzed fatigue properties for base, FSW, and TIG welds
of AA 3003-H14 aluminum alloy. Fatigue properties of FSW joints were slightly lower than the
base metal and higher than TIG welding.

Aim: surface modification of titanium using fiber laser 1064 nm to enhance the bond strength to resin cement. Material and Methods: thirty titanium discs of 0.6 cm x 0.3 cm (diameter and thickness respectively) were categorized after preparation into three groups (n=10) as follows: control group with no surface treatment and two test groups were treated with fiber laser after estimation the appropriate parameters in the pilot study which are 81 ns pulse duration, 30,000 Hz frequency, 50 µm spot size and 10,000 mm/s scanning speed and different average power values (10 W and 20 W) depending on the tested group. Titanium discs surface characterization was performed by scanning electron microscope (SEM), a

This paper describes a practical study on the impact of learning's partners, Bluetooth Broadcasting system, interactive board, Real – time response system, notepad, free internet access, computer based examination, and interaction classroom, etc, had on undergraduate student performance, achievement and involving with lectures. The goal of this study is to test the hypothesis that the use of such learning techniques, tools, and strategies to improve student learning especially among the poorest performing students. Also, it gives some kind of practical comparison between the traditional way and interactive way of learning in terms of lectures time, number of tests, types of tests, student's scores, and student's involving with lectures

An experimental model is used to simulate the loss of soil lateral confinement due to excavation nearby an individual axially loaded pile. The effects of various parameters, such as the horizontal distance of excavation, depth of excavation and pile slenderness ratios are investigated. The experimental analysis results showed the effect of excavation is more remarkable as the horizontal distance of excavation becomes closer to the pile than half pile length. The effect of excavation diminishes gradually as the horizontal distance increases beyond that distance for all the investigated pile slenderness ratios and depths of excavation. The pile head deflection, settlement and bending moments along pile increase with decreasing horizontal d

The experiment was conducted to investigate the effect of prey type (Artemia nauplii, mosquito larvae and paramecium) on some reproductive aspects in crustacean zooplankton M. albidus which included reproductive period, post reproductive period, period spend to egg appearance and the period from appearance of egg to nauplii releasing. Results revealed that females fed on mosquito larvae had the highest mean of postreproductive period and lowest mean of the period spend to egg appearance, which differed significantly (P < 0.05) compared with the means of females who fed on Artemia nauplii and paramecium on the other hand the differences were not significant in reproductive period and the period from appearance of egg to nauplii releasing.

This study was conducted to evaluate the efficacy of Saccharomyces cerevesiae as a growth promoting agent in tomato. Soaking the seeds in yeast suspension at 5 g/L for 12h increased germination percentage, root length, root fresh and dry weight, plant height, foliage fresh and dry weight, attained 88.5% ; 8.1 cm ; 84.3 mg ; 7.03 mg ; 10.75 cm ; 839 mg and 37.75 mg compared with 80% ; 5.33 cm ; 39 mg ; 4.8 mg ; 7.35 cm ; 608 mg and 25.5 mg in seedlings grown from non treated seeds respectively. Similar results were obtained with seedling from seeds soaked in S. cerevesiae filtrate for 12 hrs. with values of 77.5% ; 6.875 cm ; 91.5 mg ; 7.5 mg ; 9.5 cm ; 777 mg and 40.35 mg compared to 66% ; 5.8 cm ; 57.7 mg ; 5.03 mg ; 5.9 cm ; 493 mg

The compressive residual stresses generated by shot peening, is increased in a direct proportional way with shot peening time (SPT). For each metal, there is an optimum shot peening time (O.S.T) which gives the optimum fatigue life. This paper experimentally studied to optimize shot peening time of aluminium alloy 6061-T651 as well as using of and analysis of variance (ANOVA).

Two types of fatigue test specimens’ configuration were used, one without notch (smooth) and the other with a notch radius (1,25mm), each type was shot peened at different time. The (O.S.T) was experimentally estimated  to be 8 minutes reaching the surface stresses at maximum peak of -184.94 MPa.

A response surface methodology (RSM) is presen