The predisposing factors and their effect on the increasing of vulvovaginal Candidiasis have been studied in this research. The result indicated that the highest of infection with vaginal Candidias was in the age of women with age of (21-30years) with vaginal itching and discharge, also the results revealed that the pregnancy was the main predisposing factor. The percentage of the infected pregnant Ladies was 33.7% followed by the women who used the IUCD and OCP 22.1%, those who used steroids 5.2% comparing with control women (without predisposing factors).The results also indicated that the most cases of infection were during the third trimester of pregnancy (where the rate of infedion) was 53.9%.-OCP- Oral Contraceptive Pills-IUCD- Intrr

Objective:Fluorid-containing dental alginate impression materials can exert a considerable reduction in
enamel solubility. The objective was to evaluate the effect of fluoride addition on the setting time and
compressive strength of alginate impression materials.
Methodology: 60 samples were constructed from alginate impression material (30 samples for setting
time test and 30 samples for compressive strength test).Specimens of each test divided into three
subgroup. Group A: 10 specimens of alginate were mixed with distilled water [control], Group B: 10
specimens of alginate were mixed with100-ppm fluoride and Group C:10 specimens of alginate were
mixed with 2%Naf.
Results: the result of setting time test showed t

During the last quarter century, many changes have taken place in the tanks industry and also in the materials that used in its production، while concrete is the most suitable material where concrete tanks has the benefits of strength, long service life and cost effectiveness. So, it is necessary improvement the
conventional concrete in order to adapt the severe environment requirements and as a result high
performance concrete (HPC) was used. It is not fundamentally different from the concrete used in the past, although it usually contains fly ash, ground granulated blast furnace slag and silica fume, as well as
superplasticizer. So, the content of cementitious material is high and the water/cement ratio is low. In this
stu

    Many studies have been made and still concerning the field of translation. Since the mid-90's a considerable amount of researches has tackled the problem of gender and its effect on the process and the product of translation. Simon (1996, p 508) points out that when comparing women and men as translators and writers through history, women seem to be the weaker side. This paves the way to feminist movements which produce prominent studies concerning gender as a concept and translator's gender as practice on the quality and the accuracy of the translation.           

     Flotow (in Meschia, 2012, p 1-4) outlines several issues that can be

In this paper, the effect of changes in bank deposits on the money supply in Iraq was studied by estimating the error correction model (ECM) for monthly time series data for the period (2010-2015) . The Philips Perron was used to test the stationarity and also we used Engle and Granger to test the cointegration . we used cubic spline and local polynomial estimator to estimate regression function .The result show that local polynomial was better than cubic spline with the first level of cointegration.

Porcelain is one of the most important ceramic materials with a wide range of traditional and technical applications. Since most mixtures of porcelain have a high sintering temperature, bentonite has been added in this research to improve the characteristics of sintering and burning. The porcelain mixture consisted of the following Iraqi raw materials: 30% wt kaolin, 30 wt% non-plastic clay (grog), 10% wt sodium feldspar, 10 wt% potassium feldspar and 20 wt% flint. After the mechanical mixing process and transfer the powder mixture to the slurry by adding distilled water, then different weight percentage of the sodium bentonite(0, 2.5, 5, 7.5 and 10) wt% was added. The specimens were prepared by using the solid casting m

Alginate from Large brown seaweeds act as natural polymer has been investigated as polymer and has been added to concrete in different percentages ( 0% , 0.5% , 1% and 1.5% ) by the cement weight and the study show the effect of using alginate biopolymer admixtures on  some of the fresh properties of the concrete (slump &  the density  fresh) also in the hardened state (  Compressive strength , Splitting tensile strength  and Flexural strength ) at 28 days. The mix proportion was (1:2.26:2.26) (cement: sand: gravel) respectively and at constant w/c equal to 0.47. The results indicate that the use of alginate as a percent of the cement weight possess a positive effect on fresh properties of co

Background: Pain is one of the most postoperative complications of surgical wound especially within first 24 hrs. leading to delay hospital discharge, stress gastritis and increasing blood pressure. As wound infiltration with long acting local anesthetic (bupivacaine) has been proved to be effective after orthopedic surgeries especially total hip and knee replacements.Objective: our study was designed to determine theeffectiveness of local infiltration of 0.5% of bupivacainebefore closure of surgical wounds in controllingpostoperative pain and improve patient’s outcome after totalhip and knee replacement surgeries in first 24hrspostoperative period.Methods: Twenty patients from class I (healthy patients) and class II (patients mild sys

The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn

Nanocrystalline TiO 2 and CuO doped TiO 2 thin films were successfully deposited on suitably cleaned glass substrate at constant room temperature and different concentrations of CuO (0.05,0.1,0.15,0.2) wt% using pulse laser deposition(PLD) technique at a constant deposition parameter such as : (pulse Nd:YAG laser with λ=1064 nm, constant energy 800 mJ, with repetition rate 6 Hz and No. of pulse (500). The films were annealed at different annealing temperatures 423K and 523 K. The effect of annealing on the morphological and electrical properties was studied. Surface morphology of the thin films has been studied by using atomic force microscopes which showed that the films have good crystalline and homogeneous surface. The Root M