Background: Polymethyl methacrylate (PMMA) is used in denture fabrication and considered as the most reliable material for the construction of removable prosthodontic appliances. The material is far from ideal in fulfilling the mechanical requirements and the effect of autoclave processing has not been fully determined. The purpose of this study was to evaluate the effect of addition of salinized (ZrO2) Nano fillers in percentages 3%, 5% and 7% by weight on some properties of heat cured acrylic processed the by autoclave and compare it with 0% (control) group . Materials and methods: The silanized(ZrO2) Nano-particles was added to PMMA powder by weight in three different percentages 3%, 5% and 7%, mixed by probe ultra-sonication machine.

Background: Polishing technique for acrylic resin material have great effect on properties of acrylic material and bacterial colonization such as staphylococcus aurous, which are responsible for many acrylic prosthetic infections such as the commonly ocular infections. Ineffective polishing technique could affect roughness and subsequently porosity of acrylic materials.So, a new effective method for polishing acrylic was used depending on the use of optiglaze coating material. So, this study aimed to evaluate the effect of optiglaze polishing on porosity of acrylic resin material and staphylococcus aurous activity in comparison to conventional polishing technique. 

Materials and methods: Specimen(n=120) were prepared :20 spe

Background: Polymethylmethacrylate (PMMA) has relatively unsatisfactory mechanical properties such as low flexural strength and impact strength also dimensional instability. Material and method: Zirconium silicate nanoparticles were coated with a layer of trimethoxysilylpropylmethacrylate (TMSPM) before sonication in monomer (MMA) with the percentages 1% and 1.5% by weight then mixed with powder using conventional procedure, (150) samples were prepared and divided into three groups, each group consisted of (50) samples, the first group prepared from PMMA without addition (control), another group with the addition of 1% wt Zrsio4 nanoparticles (experimental) and the third one with 1.5% wt Zrsio4 nanoparticles (experimental). Each group

Introduction: We aimed to evaluate the shear bond strength of acrylic denture teeth to flexible and heat-cured denture base material after surface treatments with argon plasma, chemical bonding agent (PALFIQUE universal), and combination. Methods: A total of 80 incisor acrylic denture teeth were treated with a argonplasma, chemical bond (PALFIQUE universal bond), and a combination with 10 samples for each group. The neck (gingival portion) of teeth was cut at a 45° angle, and the teeth were attached to heat-cured acrylic resin and flexible denture base material. All the specimens were stored in artificial saliva for 7 days in an incubator (37 °C). A shear

Objective(s): The aim of this study is to compare the impact strength of a heat cured denture-base acrylic resin
reinforced with metal wire and glass fibers.

Methodology: Forty five specimens were prepared from pink heat cure acrylic resin. Specimens were grouped into;
group-I (control group) which consists of 15 specimens with no reinforcement, group-II which consists of 15 specimens
reinforced with metal wire, and group-III consists of 15 specimens reinforced with glass fibers. Specimens were tested
by using charpy impact machine.

Results: The result showed that there was a highly significant difference in impact strength value among the testing
groups at (P < 0.001).

Conclusion: The impact str

Objective: One of the most important practical deficiencies of present denture base materials is fracture, therefore many
attempts have been made to reinforce of the repaired denture base resin. A desirable objective for this service is to obtain
optimum strength for repairs, which can be achieved by making available a good bond between original and repaired
materials.
Methodology: The present study was carried out to evaluate and compare the transverse strength of acrylic specimens
repaired by two different materials (hot-cure and cold-cure acrylic resin). A total of 50 specimens were prepared by hot
(40) repair: (10) by hot with retention bead, (10) by cold with retention bead and (10) repair by hot only, (10) repair

   A reseach is carried out by using Alumina material type α-Al2O3 which has partical size 63μm doped with different percentage weight of MgO (0.1%,0.3%and0.5%) and by using dry press method to prepare the samples ,A force press 50KN used and sintering to 1500oC with   soaking time  of  6 hours.        The physical properties were studied such as "Bulk density ,Porosity and water absorption "also the mechanical properties such as (hardness,compressive strength ), the result shows that the best ratio of maginsa(MgO) added to Alumina (Al2O3)is 0.5%and this  worked to improve   Physical and mechanical properties .

Background: Acrylic resin dentures are susceptible to fracture; it is unresolved problem in prosthodontics. The repair procedure should be simple, strong, and accurate. This study evaluated the transverse and impact strength of autopolymerizing acrylic resin, the repair material was modified with kraft lignin as a new enforcement material and compared with the commercially available self cured acrylic resin.
Materials and Methods: The addition of kraft lignin to the acrylic resin were done in percentages of 0.25%, 0.5%, 0.75%, 1.0%, 1.25%, and 1.5% (wt%). Seventy specimens were made according to the ADA specification No 12 for transverse strength using three point bending test and Impact strength tes

ABSRTACT Background: Soft liner material is become important in dental prosthetic treatment. They are applied to the surface of the dentures to achieve more equal force distribution , reduce localized pressure and improve denture retention by engaging undercut . So the aim of the study is to evaluate the effect of different surface treatment by air-abrasion AL2O3 and laser treatment with CO2 laser on improving the shear bond strength of the denture liner to acrylic denture base material . Materials and methods: the 30 specimens of heat cured acrylic denture base material (high Impact acrylic )and heat cured soft liner (Vertex ,Nether Lands )were prepared for this study .They were designed and divided according to type of the s