Background: Cleaning and shaping of root canals successfully requires high volumes of irrigation solutions that can only be applied to the apical third of root canal after enlargement with instrument, so the aim of this study was to evaluate and to compare the efficiency of Maxi-I-probe (side-vented needle), in the amount of root canal irrigant penetration for five different master apical file sizes (MAF) and four different degrees of coronal and middle thirds flaring. Materials and Methods: Two hundred resin blocks with simulated root canals were used in this study and divided into 5 major groups (40 for each) based on the size of master apical files (#20, #25, #30, #35, and #40). Each major group was subdivided into 4 subgroups depending on different sizes and depth of flaring (10 for each).The instrumentation and flaring techniques were used as following: 1. without flaring group, root canal shape resembles shape of the master apical K-file, 2. flaring I group, flaring done with Gates Glidden I for 2 mm coronally, 3. flaring II group, flaring was done with Gates Glidden I for 4 mm coronally, Gates Glidden II for 2 mm, 4. flaring III group, flaring was done with Gates Glidden I for 6mm,Gates Glidden II 4mm and Gates Glidden III for 2 mm coronally. Irrigation was done with Max-i-probe gauge 28. Results: By comparing the five different master apical file sizes at four different degrees of flaring, there was an increase in the amount of irrigant penetration with increase MAF size, taper had more effect in small canals size and decreased with further enlargement of master apical file size until no benefit was achieved in large canals size. Conclusions: It was shown that, Max-i-probe had a limited amount of irrigant entrance. Flaring was more effective in small canals than the larger canals in an amount of irrigant entrance; increasing MAF size was effective in an increase amount of irrigant entrance.
Ceramic coating compose from a ceramic mixture (MgO, Al2O3) and metall (Al-Ni) were produced by Thermal Spray Technique. The mixed ratio of used materials Al:Ni (50%) and 40% of Al2O3 and 10% MgO. This mixture was spray on a stainless steel substrate of type (316 L) by using thermal spray with flame method and at spraying distances (8, 12, 16 and 20) cm, then the prepared films were treated by laser and thermal treatment. After that performing a hardness and adhesion tests were eximined. The present study shows that the best value of the thermal treatment is 1000 ℃ for 30 mint; the optimum spray distance is 12 cm and most suitable laser is 500 mJ where the microscopic and mechanical character
... Show More
(1)
(7)
(5)
(1)
Silver selenide telluride Semiconducting (Ag2Se0.8Te0.2) thin films were by thermal evaporation at RT with thickness350 nm at annealing temperatures (300, 348, 398, and 448) °K for 1 hour on glass substrates .using X-ray diffraction, the structural characteristics were calculated as a function of annealing temperatures with no preferential orientation along any plane. Atomic force microscopy (AFM) and X-ray techniques are used to analyze the Ag2SeTe thin films' physical makeup and properties. AFM techniques were used to analyze the surface morphology of the Ag2SeTe films, and the results showed that the values for average diameter, surface roughness, and grain size mutation increased with annealing temperature (116.36-171.02) nm The transm
... Show MoreSilver selenide telluride Semiconducting (Ag2Se0.8Te0.2) thin films were by thermal evaporation at RT with thickness350 nm at annealing temperatures (300, 348, 398, and 448) °K for 1 hour on glass substrates .using X-ray diffraction, the structural characteristics were calculated as a function of annealing temperatures with no preferential orientation along any plane. Atomic force microscopy (AFM) and X-ray techniques are used to analyze the Ag2SeTe thin films' physical makeup and properties. AFM techniques were used to analyze the surface morphology of the Ag2SeTe films, and the results showed that the values for average diameter, surface roughness, and grain size mutation increased with annealing temperature (116.36-171.02) nm The transm
... Show MoreIn this study, active knife and fixed knife of single-row disc silage machine has three different clearance C1, C2 and C3 (1, 3 and 5 mm) and it is tried in three different working speed V1, V2 and V3 (1.8, 2.5 and 3.7 km / h) and PTO speed (540 min-1) and machine's fuel consumption (l/h), average power consumption (kW), field energy consumption (kW/da), product energy consumption (kW/t), field working capacity (da/h), product working capacity (t/h) and Chopping size distribution characteristics of the fragmented material were determined. It has been found that knife-counter knife clearances smaller than 3 mm (1 mm) and larger (5 mm) have a negative effect on machine performance in general. In terms of fuel and power consumptions, the m
... Show More
This study presents the effect of laser energy on burning loss of magnesium from the holes' drilled in aluminum alloy 5052. High energy free running pulsed Nd:Glass laser of 300 µs pulse duration has been used to perform the experiments. The laser energy was varied from 1.0 to 8.0 Joules, The drilling processes have been carried out under atmospheric pressure and vacuum inside a specially designed chamber. Microhardness of the blind drilled holes has been investigated .The results indicated that the magnesium loss could be manipulated by adjusting the focusing conditions of the laser beam. Almost, the obtained holes were free of cracks with low taper and low sputter deposition. .The holes performed under atmospheric conditions have high
... Show MoreThe present study aims at finding out the (effect of the Caroll’s pattern on the second intermediate class pupils' achievement in geography)
The partial experimental design of two groups, experimental and control, with pre-post tests is used. The sample is represented in (74) female pupils. The sample is divided into two groups (38) experimental group and (36) control one. The sample is selected from first intermediate class pupils ( Am Salama Secondary School for girls) \ Baghdad\ Al-karkh-1, for academic year 2015-2016.
The researcher has equalized the two groups in several variables: the previous achievement tests, intelligence, age in months, the scor
... Show MoreIn this work, varying compositions of SiO2 micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO2/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.
This work describes the effect of temperature on the phase transformation of titanium dioxide (TiO2) prepared using metal organic precursors as starting materials. X-ray diffraction (XRD) was used to investigate the structural properties of TiO2 gels calcined at different temperatures (300, 500, 700) ?C. the results showed that the samples have typical peaks of TiO2 polycrystalline brookite nanopowders after calcined at (300 ?C), which confirmed by (111), (121), (200), (012), (131), (220), (040), (231), (132) and (232) diffraction peaks. Also, XRD diffraction spectra showed the presence of crystallites of anatase with low proportion of rutile phase where calcined at (500 ?C), while rutile phase domains at (700 ?C). The crystallite size of
... Show More
(1)