Background: This study aimed to evaluate the effect addition of polyester fibers on the some mechanical properties of heat cured acrylic resin (implant strength, flexural strength and hardness) Materials and methods: Ninety specimens were used in the study. Thirty specimens were used for impact strength measurements (80mm X 10mm X 4mm) length, width and thickness respectively. The specimens divided into three test groups (n=10), first group formed from heat cure acrylic resin without fiber reinforcement. Second group was formed from heat cure acrylic resin was reinforced with 2 mm length polyester fiber and third group was formed from heat cure acrylic resin reinforced with 4mm length polyester fiber, impact strength measured by impact testing device. 30 specimens with (65 mm X 10mm 2.5mm) length, width and thickness respectively were used in 3 groups (n=10) flexural strength test. The flexural strength was measured by using flexural testing device. 30 specimens with (65mm X 10m X 2.5mm) length width and thickness respectively were used for hardness test. The specimens were divided into 3 group (n=10) as in impact strength and flexural strength. Hardness measured by using (shore D hardness tester TH210). Results: revealed statistically significant increase on impact strength especially on 4mm length when compared to control group. Significant decreases in flexural strength of PMMP. When compared to control group with 4mm length fiber reinforcement. Non significant decrease when compared control group with 2mm length fiber reinforced PMMA. Significant decrease in hardness of PMMA resin after reinforcement with 2mm, 4mm lengths polyester fibers. Conclusions: Strengthening with the polyester fiber decreased the flexural strength and hardness of the resin, but increased impact strength. Thus when high impact acrylic resins are needed, fiber reinforced resins may be the material of choice.
Abstract
The research the impact of the application of some of the production system tools in the specified time, which can be adapted in the service sectors (banking sector) over the improvement and increase the quality of banking services, and highlights the research problem in the low quality of banking services provided to customers because of the reliance on traditional banking systems in the provision of services Because of the lack keep pace with global developments in the banking industry, and the goal of research is to clarify the applicability of the production system in the time specified in the service sector and th
... Show More
The aim of this paper is to demonstrate the effect of Na2[Fe(CN)5.NO].2H2O impurity (0.1 M) concentration on the dielectrical properties of poly (P-Aminobenzaldehyde) terminated by pheneylenediamine in the frequency and temperature ranges (1-100)KHz and (283-348) K respectively.These properties include dissipation factor, series and parallel resistance, series and parallel capacitance, real and imaginary part of the dielectric constant, a.c conductivity and impedance (real and imaginary) part, that have been deduced from equivalent circuit. The investigation shows that adding Na2[Fe(CN)5.NO].2H2O as additive to the polymer lead to increase of the dielectric constant with increasing temperature and it is decreasing with increasing the freq
... Show More
The change in the optical band gap and optical activation energy have been investigated for pure Poly (vinyl alcohol)and Poly (vinyl alcohol) doped with Aluminum sulphate to proper films from their optical absorption spectra. The absorption spectra were measured in the wave range from (200-700) nm at temperature range (25-140) 0C. The optical band gap (Eg) for allowed direct transition decrease with increase the concentration of Aluminum sulphate. The optical activation energy for allowed direct transition band gap was evaluated using Urbach- edges method. It was found that ?E increases with increasing the concentration of Al2 (SO4)3 and decreases when temperature increases.
Irinotecan induced-mucositis is an inflammatory event of intestine caused by an increase in concentration of active metabolite 7ethyl10-hydroxycamptothecin (SN38) in the intestine. Irinotecan must first be converted by a carboxylesterase (CES) to the active metabolite (SN38), which is subsequently glucuronidated by the hepatic enzyme to SN38G. The SN-38G is deconjugated in the intestine to SN-38 via ?-glucuronidase produced by the intestinal bacterial flora, which accounts for SN-38 delayed intestinal mucositis of irinotecan. To study the protective effect of mentha in irinotecan-induced mucositis, intestinal mucositis induced by I.P injection of irinotecan (75mg/Kg/day) for 4 days. Mentha ethanolic extract orally administered to
... Show More
(14)
(1)
The aim of the present study is to investigate and compare the efficacy of L-carnitine, multivitamins and their combination therapies on semen characteristics in idiopathic male infertility. Idiophathic infertile patients were randomly divided into three groups who had received three different treatment regimens for three months: group A (45 patients) has received 2 grams daily of L-carnitine alone; group B (55 patients) had received the combination of L-carnitine (2 grams daily) plus one tablet daily of multivitamins (Stresstabs®); and group C (29 patients) had received one tablet daily of multivitamins alone. The study was started on 1/11/2009 and completed on 31/3/2010 and performed at Rizgari Teaching Hospital in
... Show More
(2)
This study was conducted to study the cytogenetic effect of both alcoholic and water extracts of propolis on mice. Three different samples of propolis were collected from three different regions of Iraq (Najaf, Arbil and Baghdad) to be used in this study. The cytotoxic effect of two different doses of each extracted sample was measured by employing cytogenetic analysis which included (mitotic index (MI), chromosomal aberrations (CAs), micronucleus index (MN) and sperm abnormalities). Results showed that significant increase in MI and significant reduction in MN, CAs and sperm abnormalities percentage were seen after treatment with both alcoholic and water extract of the three samples when compared with negative control, and alcoholic extrac
... Show MorePotentiostatic polarization and weight loss methods have been used to investigate the corrosion behavior of carbon steel in sodium chloride solution at different concentrations (0.1, 0.4 and 0.6) M under the influence of temperatures ( 293, 298, 303, 308 and 313) K. The inhibition efficiency of the amoxicillin drug on carbon steel in 0.6 M NaCl has also been studied based on concentration and temperature. The corrosion rate showed that all salt concentrations ( NaCl solution) resulted in corrosion of carbon steel in varying ratio and 0.6 M of salt solution was the highest rate (50.46 g/m².d). The results also indicate that the rate of corrosion increases at a temperature of 313 K.. Potentiodynamic polarization studi
... Show More
(13)
(8)
(3)
(2)