Background: Denture fracture is one of the most common problems encountered by the patients and prosthodontists. The objective of present study was to evaluate the transverse strength of nylon denture base resin repaired by using conventional heat polymerized, autopolymerized and visible light cure {VLC} resins, surface treatment that used for repair and adjustment of insufficient nylon denture bases and in case of addition of artificial teeth. As these corrective procedures are common chair side procedures in dental clinic. Materials and methods: One hundred twenty nylon specimens were prepared by using metal patterns with dimension of (65x10x2.5 mm) length, width, and thickness respectively for transverse strength test while for tensile bond strength a dumbbell-shaped with measurement (65x12.5x25mm) length, width, and thickness respectively were flasked with stone. The nylon specimens were molded by reflasked with dental stone that used as an index for these specimens in the repair procedure and repaired with 45 degree bevel joint by using metal holding device. The two parts of nylon specimen to be repaired were realigned in its repair index and adhere with special adhesive material to stabilize the combination during repair procedure. The dough of heat and cold cure resin was packed into the joint and then cured. The specimen repaired with cold cure resin was placed in the Ivomat containing water at (40°C) and pressure (30IB/inch²) for 15 minutes. The specimen repaired with {VLC} was placed in the light cure unit for 4 minutes following manufacturer’s instruction. The fractured nylon specimens were divided according to the type of repaired materials into (40) specimens received heat cure acrylic and the (40) specimens received cold cure acrylic and the other 40 specimens received {VLCR}. Each 40 specimens were subdivided according to the type of surface treatment received into 20 specimens were treated with coarse stone bur (control), 20 specimens were treated with combination of coarse stone bur and monomer of the heat cure acrylic. After that the specimens were subjected to transverse {Tr} and tensile bond {TB} strength tests. For each test 10 specimens. Results and conclusions: This study showed that specimens treated with combination of coarse stone bur and monomer of the acrylic (heat, cold or VL cure) had the highest transverse and tensile strength values, followed by the specimens treated with coarse stone bur. The results showed that the specimens repaired with heat cure acrylic had transverse and tensile strength values higher than the specimens repaired with cold and VL cure acrylic when compared between subgroups of heat, cold and VL cure acrylic that received the same treatments.
This is prospective study began in Jan. 2003 and concluded in April 2004, was undertaken to examine the benefits of 810 nm diode laser in treatment of four patient with bilateral vocal cord paralysis also to compare the results with conventional treatment Material and methods: 810 nm diode laser 15 watts was used in these cases under general anesthesia, and induction of anesthetic drug done through tracheostomy tube in all patients. All patients were decanulated “Tracheostomy tube removed”, the voice of all preserved within normal. Laser surgery in this case has more benefit and advantage than conventional methods even if the patient need more than on session of laser operation because of high success rate, less complication and easy
... Show MoreDifferent bremsstrahlung spectra from tungsten anode x-ray tube generated at 30, 40 and 50 kV have been examined theoretically and experimentally for an attempt to find a most suitable spectrum to radiograph a test object of 0.01 cm thickness of Cu and Ag. The high contrast using this suitable spectrum is demonstrated and the possible effects of fluorescent radiation are discussed.
(1)
In this research, geopolymer mortar had to be designed with 50% to 50% slag and fly ash with and without 1% micro steel fiber at curing temperature of 240℃. The molarity of alkaline solution adjusted with 12 molar sodium hydroxid to sodium silicate was 2 to 1, reaspectivly. The heat of curing increased the geopolymerization proceses of geoplymer mortar, which led to increasing strength, giving the best result and early curing age. The heat was applied for two days by four hours each day. It was discovered in the impact test that the value first crack of each mix was somewhat similar, but the failure increased 72% for the mixture that did not contain fiber. For the energy observation results it was shown that the mixt
... Show More
(2)
This research aimed to examine the effect of concentration of dyes stuff, contact time, temperature and ratio of adsorbent weight in (gm) to volume of solution in (ml) on the percentage removal. Two dyes were used; direct blue 6 and direct yellow and the adsorbent was the maize cob. Batch experiments were performed by contacting different weights of adsorbent with 50 ml of solution of desired concentration with continuous stirring at various temperatures. The percentage of removal was calculated and the maximum percentage of removal was 80%. And as the concentration of solution, contact time, temperature and the ratio of adsorbent to volume of solution increase the percentage of removal increase.
In this paper, the experiments were carried out in laboratory flotation cell treating solid fines. The effect of variables such as collector oil dosage, pine oil dosage and solid content of the feed slurry have been investigated on the flotation characteristics of low rank coal. Attempts have also been made to develop some empirical Eq. to predict the yield and ash content of concentrate with the operating variables, solids concentration, collector oil dosage, and pine oil dosage, to estimate the recovery at any operating conditions. The calculated results obtained from regression equation by correlating the variables with the yield and ash content of concentrate have been compared to study whether calculated values match closely with th
... Show MoreA variety of oxides were examined as additives to a V2O5/Al2O3 catalyst in order to enhance the catalytic performance for the vapor phase oxidation of toluene to benzoic acid. It was found that the modification with MoO3 greatly promoted the little reaction leading to improve catalyst performance in terms of toluene conversion and benzoic acid selectivity. The effect of catalyst surface area, catalyst promoters, reaction temperature, O2/toluene, steam/toluene, space velocity, and catalyst composition to catalyst performance were examined in order to increase the benzoic acid selectivity and yield.
This research deals with the effects of welding variables using MIG/MAG spot by using Argon (Ar) gas and CO2 to show their effect on the mechanical characteristics and microstructure of low alloy steel type DIN15Mo3 and determine the optimum condition for the process of welding ; current & time. The results show the possibility of using CO2 and also Ar in low alloy steel welding with a little decrease in the shear force of not more than 13% for 4mm thickness and time 2sec. The shear force increased when using Ar instead of CO2 to be , The shear force reach 36KN when using Ar at 2mm thickness time of 8 sec and current of 220 Amp. , when used CO2 instead of Ar d
... Show MoreThe Wheat husk is one of the common wastes abundantly available in the Middle East countries especially in Iraq. The present study aimed to evaluate the Wheat husk as low cost material, eco-friendly adsorbents for the removal of the carcinogenic dye (Congo red dye) from wastewater by investigate the effect of, at different conditions such as, pH(3-10), amount of adsorbents (1-2.3gm/L),and particle size (125-1000) μm, initial Congo red dye concentration(10, 25 , 50 and 75mg/l) by batch experiments. The results showed that the removal percentage of dye increased with increasing adsorbent dosage, and decreasing particle size. The maximum removal and uptake reached (91%) , 21.5mg/g, respectively for 25 initial concent
... Show More
(3)