The corrosion behavior of low carbon steel in washing water of crude oil solution has been studied potentiostatically at five temperatures in the range ( 303 –343 )K, at pH ( 4 ) and at pH (4,6,7,9,11 ) at (343K)..The corrosion potential shifted to more negative values with increasing temperature and the corrosion current density increased with increasing temperature, the corrosion current density (icorr) decreased with increasing pH in the rang ( 4 – 7 ) and it increased with increasing pH in the rang ( 9 – 11 ) at ( 343 K ), while the corrosion potential generally variation with increasing pH in the rang (4-11)at(343K. From the general results for this study can be seen that thermodynamic and kinetic function were

The mutagenic effect of some crucifers widely consumed Lepiduim sativum (Garden cress) and Arugula (Eruca sativa) was studied in comparison to carrot (Daucus carota), using bacterial mutagenic system composed of three bacterial isolates; (Bacillus spp)G3 (Arthrobacter spp)G12, and (Brevibacterium spp)G27 ,. Treatment of isolates with plant extracts led to reduction in survival fraction (Sx)at different levels except that Aurgula extract did not show any inhibitory effect in isolates G12 and G27. Crucifers extracts induced streptomycin resistant mutants in G12 at higher level than G3 , but not in G27. No resistance to rifimpacin was detected in all isolates.

Films of CdSe have been prepared by evaporation technique with thickness 1µm. Doping with Cu was achieved using annealing under argon atmosphere . The Structure properties of these films are investigated by X-ray diffraction analysis. The effect of Cu doping on the orientation , relative intensity, grain size and the lattice constant has been studied. The pure CdSe films have been found consist of amorphous structure with very small peak at (002) plane. The films were polycrystalline for doped CdSe with (1&2wt%) Cu contents and with lattice constant (a=3.741,c=7.096)A°, and it has better crystallinty as the Cu contents increased to (3&5wt%) Cu. The reflections from [(002), (102). (110), (112), and (201)]planes are more prominen

The CdSe pure films and doping with Cu (0.5, 1.5, 2.5, 4.0wt%) of thickness 0.9μm have been prepared by thermal evaporation technique on glass substrate. Annealing for all the prepared films have been achieved at 523K in vacuum to get good properties of the films. The effect of Cu concentration on some of the electrical properties such as D.C conductivity and Hall effect has been studied.
It has been found that the increase in Cu concentration caused increase in d.c conductivity for pure CdSe 3.75×10-4(Ω.cm)-1 at room temperatures to maximum value of 0.769(Ω.cm)-1 for 4wt%Cu.All films have shown two activation energies, where these value decreases with increasing doping ratio. The maximum value of activation energy was (0.319)eV f

n-Hexane conversion enhancement was studied by adding TCE (Trichloro-ethylene) on feed stream using 0.3%Pt/HY zeolite catalyst. All experiments were achieved at atmospheric pressure and on a continuous laboratory unit with a fixed bed reactor at a temperature range 240-270◦C, LHSV 1-3h-1, H2/nC6 mole ratio 1-4.
By adding 435 ppm of TCE, 49.5 mole% conversion was achieved at LHSV 1h-1, temperature of 270ºC and H2/nC6 mole ratio of 4, while the conversion was 18.3 mol% on the same catalyst without adding TCE at the same conditions. The activation energy decreased from 98.18 for pure Pt/HY zeolite to 82.83 kJ/mole by adding TCE. Beside enhancement the activity, selectivity and product distribution enhanced by providing DMB (Dimethyl b

            This study tests the effect of a large number of independent variables that control the growth of the total productivity, which amounted to 112 variables, gathered from what is mentioned in the specialized theoretical and applied literature. The data for these variables were taken from global reports of sound international organizations and reliable databases covering the period 1991-2016. The data of the dependent variable, the growth of the total factor productivity, were taken from the database of the world development indicators. The study covered 61 countries for which data were available. The study included three regression models to explain

في الدراسة الحالية، تم تصنيع جسيمات ZrO2 النانوية باستخدام مستخلص نباتي مشتق من نبات Vitex agnus castus، ووسط قلوي مثل هيدروكسيد الصوديوم. تم استخدام أسلوب التخليق الحيوي لتحضير جزيئات أوكسيد الزركونيوم النانوية لهذا المشروع البحثي. تتميز هذه الطريقة عن غيرها بسبب فعاليتها من حيث التكلفة وبساطتها وقلة المخاطر المحتملة. وتم تشخيص العينات المحضرة باستخدام المجهر الإلكتروني النافذ TEM، المجهر الإلكتروني الماسح SEM،

    The research specified with study the relation  between the market share for the sample research banks and the amount of the achieved revenues from the investment, where the  dominated belief  that there potentiality enhancing the revenue on investment with the increase of the banks shares in their markets after their success in achieving rates of successive growth in their sales of sales and to a suitable achieve  market coverage for their products and they have dissemination and suitable  promotion activity, the  market share represented the competition  for the banks, and the markets pay attention to the  market share as a strategic objective and to maintain them also increasi