The catalytic cracking of three feeds of extract lubricating oil, that produced as a by-product from the process of furfural extraction of lubricating oil base stock in AL-Dura refinery at different operating condition, were carried out at a fixed bed laboratory reactor. The initial boiling point for these feeds was 140 ºC for sample (1), 86 ºC for sample (2) and 80 ºC for sample (3). The catalytic cracking processes were carried out at temperature range 325-400 ºC and initially at atmospheric pressure after 30 minutes over 9.88 % HY-zeolite catalyst load. The comparison between the conversion at different operating conditions of catalytic cracking processes indicates that a high yield was obtained at 375°C, according to gasoline pr

Existence of these soils, sometimes with high gypsum content, caused difficult problems to the buildings and strategic projects due to dissolution and leaching of gypsum by the action of waterflow through soil mass. In this research, a new technique is adopted to investigate the performance of replacement and geosynthetic reinforcement materials to improve the gypseous soil behavior through experimential set up manufactured loaclally specially for this work. A series of tests were carried out using steel container (600*600*500) mm. A square footing (100*100) mm was placed at the center of the top surface of the bed soil. The results showed that the most effective thickness for the dune sand layer with geotextile at the interface, within

Background and Aim: due to the rapid growth of data communication and multimedia system applications, security becomes a critical issue in the communication and storage of images. This study aims to improve encryption and decryption for various types of images by decreasing time consumption and strengthening security. Methodology: An algorithm is proposed for encrypting images based on the Carlisle Adams and Stafford Tavares CAST block cipher algorithm with 3D and 2D logistic maps. A chaotic function that increases the randomness in the encrypted data and images, thereby breaking the relation sequence through the encryption procedure, is introduced. The time is decreased by using three secure and private S-Boxes rather than using si

Background: The ideal force-delivery system must: provide optimal tooth moving forces that elicit the desired effects, be comfortable and hygienic for the patient, require minimal operator manipulation and patient cooperation and provide rapid tooth movement with minimal mobility during orthodontic therapy, the elastomeric chains have the greatest potential to fulfill these requirements. Materials and Methods: This in vitro study was designed to determine the effect of three different mechanisms for canine retraction : (6-3 , 6-5-3 and chain loop ) on the load relaxation behavior of three types of elastomeric chains : (maximum clear , maximum silver and extreme silver) from the same company (Ortho Technology company) with two different bran

An oil spillage has been a great threat to human life in parts of Koya district, especially through the contamination of domestic water. An attempt was made to find and map the extent of pollution in the area. According to a field survey, more than 17 springs and 34 hand-dug and artesian wells have been contaminated with crude oil. The contamination was recorded recently after loading began of tens of oil tankers in the Taq-Taq oil field, and as a result hundred barrels of oil have spilled into the creeks and soil daily. Hence, 2D resistivity imaging was adopted via four laid-out traverses running normal to the strike of the outcrops. A Wenner-Schlumberger array configuration was used to achieve both vertical and lateral resistivity dist

The pollution of aquatic ecosystems with toxic heavy metals is representing a major environmental issue, as a result of releasing these metals to ecological ambient without treatment, leading to their persistence and non-biodegradation in the environment. Various traditional methods are utilized as an attempt to remove heavy metals from waste water but still without making any actual progress. This study hypothesizes that Eichhornia crassipes (water hyacinth) dried leaves powder is potential in removing some of these heavy metals (HM), including lead, copper, cadmium and chrome from aqueous solutions via biosorption influenced by some variable experimental factors. This aim was approached by using two different experimental conditions: (

In this research, porous silicon (PS) prepared by anodization etching on surface of single crystalline p-type Si wafer, then Gold nanoparticle (AuNPs) prepared by pulsed laser ablation in liquid. NPs deposited on PS layer by drop casting. The morphology of PS, AuNPs and AuNPs/PS samples were examined by AFM. The crystallization of this sample was characterized by X-ray diffraction (XRD). The electrical properties and sensitivity to CO2 gas were investigated to Al/AuNPs/PS/c-Si/Al, we found that AuNPs plays crucial role to enhance this properties.

Aspergillus niger is one of the most important filamentous fungi that used in the fermentation industry. Aspergillus niger isolate was cultured on potato-dextrose agar (PDA) for activation, and the optimum conditions for xylanase production from this local isolate were studied by solid state fermentation, using a medium composed of wheat bran moisten with corn steep liquor at ratio 1:0.5 (v:w) at initial pH 5.5, inoc-ulated with 1.6 × 106 spores/ml, and incubated at 30ᵒC for 5 days.

Aim: surface modification of titanium using fiber laser 1064 nm to enhance the bond strength to resin cement. Material and Methods: thirty titanium discs of 0.6 cm x 0.3 cm (diameter and thickness respectively) were categorized after preparation into three groups (n=10) as follows: control group with no surface treatment and two test groups were treated with fiber laser after estimation the appropriate parameters in the pilot study which are 81 ns pulse duration, 30,000 Hz frequency, 50 µm spot size and 10,000 mm/s scanning speed and different average power values (10 W and 20 W) depending on the tested group. Titanium discs surface characterization was performed by scanning electron microscope (SEM), a