Background: Sealers should demonstrate adhesive properties to dentin, decreasing the chance of endodontic treatment failure. Increased adhesive properties to dentin may lead to greater strength of the restored tooth, which may provide greater resistance to tooth fracture and clinical longevity of an endodontically treated tooth. The aim of this study was to evaluate the shear bond strength of Bioceramic iRoot SP sealer, AH plus sealer and Apexit plus sealer in absence or presence of smear layer using push out bond strength test. Materials and Methods: Sixty straight single roots of the mandibular premolars were selected for this study. All canals were instrumented using ProTaper rotary instruments to achieve tapered canal walls, instrumentation was done with copious irrigation of 5.25% sodium hypochlorite. Roots were randomly divided into three groups according to the type of sealer used (twenty teeth for each group): Group A: Apexit plus + gutta percha, Group B: AH plus sealer + gutta percha, Group C: iRoot SP sealer + gutta percha .Then groups were subdivided according to types of final irrigation into two subgroups. Groups (A1, B1, and C1) were irrigated with 5 ml of 5.25% NaOCl for 1 minute while Groups (A2, B2, and C2), the smear layer was removed with 5 ml of 17% EDTA for 1 minute. All groups were rinsed with distilled water and then obturated with cold lateral condensation technique, the roots then stored in moist environment at 37°C for one week. The roots were embedded in clear acrylic resin and three horizontal sections were prepared at a thickness of 1 mm ±0.1 in the apical, middle and coronal parts of each root. The test specimens were subjected to the push-out test method using a Universal Test Machine that carried 1-mm, 0.5- mm and 0.3-mm plungers for coronal, middle and apical specimens, respectively. The loading speed was 0.5 mm/ min. The computer showed the higher bond force before dislodgment of the filling material. These forces were divided by the surface area to obtain the bond strength in MPa. Results: The results showed that the bond strengths of iRoot SP and AH Plus were significantly higher than those of Apexit plus, but there was no significant difference between the bond strength of iRoot SP and AH Plus.In terms of root segments, the bond strengths in the middle specimens and the apical specimens were higher compared with the bond strengths in the coronal specimens. Conclusion: The presence or absence of smear layer did not significantly affect the bond strength of Bioceramic filling materials.
The aim of this research is to find out the influence of Daniel's model on the skills of the twenty-first century among the students of the scientific-fifth grade at the secondary and preparatory government morning schools for the academic year 2022- 2023. Two groups were chosen out of five groups for the fifth-scientific grade, one of which represents the experimental group that is taught by the Daniel model, and the other is the control group that is taught in the traditional method. The equivalence of the two research groups was verified with a set of variables. As for the research tool, a scale was developed by the researchers for the skills of the twenty-first century, in which they adopted the framework of the Partnership Organizat
... Show MoreThis research study the effect of Titanium dioxide on the tensile properties of
Polystyrene (PS) and Polycarbonate (PC) polymers. The stress – strain curve for pure PS
and pure PC, shows that Young modulus for PS is higher than Young modulus for PC,
because PS have higher ultimate strength than PC.
The addition of TiO2 to PS and PC will reduce the Young modulus and ultimate stress,
because the TiO2 particles will reduces or freeze the orientation of these molecular chain
and reduced the toughness of PC, while when the TiO2 were added to PS, the value of
toughness will be stabilized because TiO2 particles make these chains interlocked and the
mobility of the chains will be restrict.
(10)
(3)
The first studies on shocks and vibrations were carried out at the beginning of the 1930s to improve the behavior of buildings during earthquakes. Vibration tests on aircraft were developed from 1940 to verify the resistance of parts and equipments prior to their first use. Flutter is a well-known example of dynamic aero elasticity, where when oscillation of structure interacted with unsteady aerodynamic forces the flutter will occur. Vibration on any structure without damping means that self-harmonic oscillation will occur, and in most cases the oscillation may start to increase until structural failure. This behavior is very similar to resonance phenomena if only the oscillation is being studied as a vibration case. In vibration suppre
... Show More
(1)
Nano gamma alumina was prepared by double hydrolysis process using aluminum nitrate nano hydrate and sodium aluminate as an aluminum source, hydroxyle poly acid and CTAB (cetyltrimethylammonium bromide) as templates. Different crystallization temperatures (120, 140, 160, and 180) 0C and calcinations temperatures (500, 550, 600, and 650) 0C were applied. All the batches were prepared at PH equals to 9. XRD diffraction technique and infrared Fourier transform spectroscopy were used to investigate the phase formation and the optical properties of the nano gamma alumina. N2 adsorption-desorption (BET) was used to measure the surface area and pore volume of the prepared nano alumina, the particle size and the
... Show MoreVisceral leishmaniasis (VL) is a parasitic disease that affects public health. It is described by weight reduction, irregular fever bouts, anemia, and amplification of the spleen and liver.
Three concentrations (15.6, 31.2, and 62.5 μg/mL) were used to find the potency of an aqueous extract of
(1)
(1)
The work concerned with studying the effect of (SiO2) addition as a
filler on the adhesive properties of (PVA). Samples were prepared as
sheets by using casting method. The mechanical properties showed
that increase in tensile strength from (34MPa) to (68MPa) when
(SiO2) added to (PVA). The adhesive strength showed that joint
properties depend upon specific adhesive characteristic of material
(PVA) and (SiO2\PVA)composites at different concentrations (1.5%,
2.5%, 3.5%, 4.5wt%), the cohesive strength of the adhesive material,
the joint design, and adherent type (Sponge Rubber(SR), Natural
leather (NL), Vulcanized Rubber(VR), and Cartoon). The results
proved the tensile strength increased with (SiO2) ratio, so
The research aim to measure the impact of the Industry specialization of the auditors on the quality in audit in Iraqi auditing firms, as well as measuring the factors of Industry specialization in the Iraqi audit companies by measuring the market shares of Iraqi audit firms that audit the companies listed on the Iraqi Stock Exchange For 2010 to 2016, by surveying the opinions of (35) Audit firm on the impact of the Industry specialization of auditing firms in audit quality factors, The effect of the variables was revealed through the use of the survey form Distributed to Iraqi audit companies, The industry speci
... Show More
CuInSe2(CIS) thin films have been prepared by use vacuum thermal evaporation technique, of thickness750 nm with rate of deposition 1.8±0.1 nm/sec on glass substrate at room temperature and pressure (10-5) mbar. Heat treatment has been carried out in the range (400-600) K for all samples. The optical properties of the CIS thin films are been studied such as (absorption coefficient, refractive index, extinction coefficient, real and imaginary dielectric constant) by determined using Measurement absorption and transmission spectra. Results showed that through the optical constants we can make to control it are wide applications as an optoelectronic devices and photovoltaic applications.