Background: Thermocycling simulates the temperature dynamics in the oral environment. This in vitro study done to measure and compare the effect of thermocycling on the shear bond strength of stainless steel and sapphire brackets bonded to human enamel teeth using light cured orthodontic adhesive and debonded at various time, and to measure adhesive remnant index after debonding. Materials and Methods: one-hundred-twenty extracted upper first premolars for orthodontic reason were used in this study; depending on weather thermocycled or not, the sample was divided into two main groups, then within each group 30 teeth were used for stainless-steel brackets (Bionic®) and for sapphire brackets (Pure®). Both groups were subdivided into three groups (n = 10) according to the debond times: I: debond after 24 hour, II: debond after 7 days and III: debond after 30 days. Within 24 hr, half of the sample was thermocycled manually for 500 complete cycles between 5/55°C and the remaining sample was stored in distilled water at room temperature and water was changed daily until debond time for each group was performed. The adhesive remnant index was tested under 20X magnification lens using stereomicroscope. Results and Conclusions: Both bracket types demonstrated high shear bond strength values before thermocycling (P?0.05), whereas after 500 thermocycles, there were significant changes in shear bond strength resulted in marked reduction in the stainless steel brackets than in the sapphire brackets (P?0.05). Shear bond strength values increased with time for both stainless steel and sapphire brackets with and without thermocycling (P?0.05). The tendency of bond failure was increased at the bracket/adhesive interface rather than enamel/bracket interface in the stainless steel brackets whereas at the enamel/bracket interface rather than bracket/adhesive interface in the sapphire brackets.
The shear strength of soil is one of the most important soil properties that should be identified before any foundation design. The presence of gypseous soil exacerbates foundation problems. In this research, an approach to forecasting shear strength parameters of gypseous soils based on basic soil properties was created using Artificial Neural Networks. Two models were built to forecast the cohesion and the angle of internal friction. Nine basic soil properties were used as inputs to both models for they were considered to have the most significant impact on soil shear strength, namely: depth, gypsum content, passing sieve no.200, liquid limit, plastic limit, plasticity index, water content, dry unit weight, and initial
... Show More
(3)
Background: Metal ions can be released from metallic orthodontic appliances due to corrosion in the oral cavity; prophylactic mouthwashes may have an effect on ion release from orthodontic wires. Materials and Methods: Thirty six orthodontic sets of half maxillary fixed appliance with 2 types of arch wires SS and NiTi(Morelli) were constructed and immersed in 2 types of mouthwashes; Claradone (non-fluoridated) and Silver Care (fluoridated) for 28 days at 37°C, then the released Ni and Cr ionswere measured using atomic absorption spectrophotometer and compared statistically. Results: Ni ion release was higher from NiTi wire group than SS wire group for both mouthwashes and also was higher for Silver Care group than for Claradone group.
... Show More
(3)
The present investigation considers the effect of curing temperatures (30, 40, and 50˚C) and curing compound method on compressive strength development of high performance concrete, and compares the results with concrete cured at standard conditions and curing temperature (21˚C). The experimental results showed that at early ages, the rate of strength development at high curing temperature is greater than at lower curing temperature, the maximum increasing percentage in compressive strength is 10.83% at 50C˚ compared with 21C˚ in 7days curing age. However, at later ages, the strength achieved at higher curing temperature has been less, and the maximum percentage of reduction has been 5.70% at curing temperature 50C˚ compared with 21
... Show More
(1)
Orthodontic tooth movement is characterized by tissue reactions, which consist of an inflammatory response in periodontal ligament and followed by bone remodeling in the periodontium depending on the forces applied. These processes trigger the secretion of various proteins and enzymes into the saliva. The purpose of this study was to evaluate the activity of the lactate dehydrogenase (LDH) in saliva during orthodontic tooth movement using different magnitude of continuous orthodontic forces. Thirty orthodontic patients (12 males and 18 females) with ages 17-23 years with class II division I malocclusion all requiring bilateral maxillary first premolar extractions. Those patients were randomly divided into 3 groups according to the magnitude
... Show More
(2)
(1)
An investigation was conducted for the determination of the effects of the forming conditions in the production of Gamma Alumina catalyst support on the crushing strength property. Eight variables were studied , they are ;binder content which is the sodium silicate , Solvent content which is the water, speed of mixing , time of mixing, drying temperature , drying time , calcinations temperature and the calcinations time
Design of the experiments was made by using the response Surface method in Minitab 15 software which supply us 90 experiments .
The results of this investigation show that the crushing strength for the dried Gamma alumina extrudate was affected by the drying temperature and the drying time only and there is no inter
Background: The present in-vitro study was undertaken to evaluate and compare fracture resistance of weakened endodontically treated premolars with class II MOD cavities restored with different bulk fill composite restorations (EverX posterior, Alert, Tetric EvoCeram Bulk Fill, and SDR). The type and mode of fracture were also assessed for all the experimental groups. Materials and Method: Forty-eight human adult maxillary premolar teeth were selected for this study. Standardized extensive class II MOD cavities with endodontic treatment were prepared for all teeth, except those that were saved as intact control. The teeth were divided into six groups of eight teeth each (n=8): (Group 1) intact control group, (Group 2) unrestored teeth with