Hydrogen sulfide (H₂S) gas sensor based on cobalt–manganese spinel oxide MnCo₂O₄ thin films that were prepared by chemical precipitation and green synthesis methods. Structural, morphological, and compositional characterizations of MnCo₂O₄ thin films were performed using XRD, FE-SEM, EDS, and AFM. It was found through XRD patterns that MnCo₂O₄ was formed in a cubic spinel structure for both methods; however, the chemically precipitated thin films possessed better crystallinity and larger crystallite sizes, whereas the green-synthesized films exhibited slightly lower crystallinities and smaller sizes, as evidenced by the broader peaks observed. In addition, FE-SEM and AFM images revealed that the MnCo₂O₄ films prepared by

ABSTRACT This study presents an efficient approach for the separation and preconcentration of norepinephrine (NOR) from pharmaceutical formulations, environmental water, and human urine samples using a dispersive micro – solid phase extraction (DμSPE) technique employing magnetic nanoadsorbents. Two adsorbents, Fe3O4@TTAB and Fe3 O4@SiO2@TTAB, were prepared by functionalising iron oxide and silicacoated iron oxide nanoparticles with the cationic surfactant tetradecyltrimethylammonium bromide (TTAB). NOR was first converted into a sensitive diazonium dye via reaction with diazotised sulphamethazine and then extracted using mixed ademicelle – hemimicelle magnetic solid-phase extraction, followed by spectrophotometric quantification. Key

Phosphorus‐based Schiff base were synthesized by treating bis{3‐[2‐(4‐amino‐1.5‐dimethyl‐2‐phenyl‐pyrazol‐3‐ylideneamino)ethyl]‐indol‐1‐ylmethyl}‐phosphinic acid with paraformaldehyde and characterized as a novel antioxidant. Its corresponding complexes [(VO)₂L(SO₄)₂], [Ni₂LCl₄], [Co₂LCl₄], [Cu₂LCl₄], [Zn₂LCl₄], [Cd₂LCl₄], [Hg₂LCl₄], [Pd₂LCl₄], and [PtL

Objective: This research aimed to study the relation between maximal bite force (MBF) and maximum mouth opening among 12-year-old school children. Methods: In this cross-sectional study, a total of 400 children aged 12 years (194 boys and 206 girls) were examined. The MBF for the right and left side, as well as the anterior region, were evaluated for all children. The MMO was measured using an electronic digital caliper. To analyze the data path analysis method was used. Results: Boys showed a higher MMO of 48.797 ± 6.500 than girls (46.710 ± 5.926 mm). The MMO increased with increasing MBF, with significant differences between females and males. Conclusion: The MMO was higher in boys than in girls. Gender plays a significant ro

Background: In this study we evaluate the effect of plasma treatment (oxygen and argon) gas in two different exposure times on the surface of heat cure and light cure acrylic resin. Materials and method: 100 specimens of heat cure and light cure acrylic resin were fabricated. The measurements of the samples were (75mm, 25mm and 4.5mm) length, width and depth respectively with stopper of 3mm depth. Two types of gas used oxygen and argon in (5,10) min by using (DC-glow discharge plasma device) then we apply cold cure soft lining material, with the help of Instron machine we test the shear stress value. Results: A highly significant effect after argon and oxygen gases treatment in both 5 and 10 min exposure times on shear bond strength to soft

Background: Although bleaching is typically considered a safe procedure, various investigations have found minor negative effects and changes in mineral composition. The aim was to Evaluate and compare the efficacy of using Nanohydroxyapatite serum on surface microhardness of enamel surface before and after bleaching with chemically cured Boost bleaching. Material and methods: ten sound human permanent upper and lower premolar teeth were used and their roots were removed 2 mm apically to the cementoenamel junction, the crowns were sectioned mesiodistally into two halves buccal and lingual/palatal, the buccal surface was further subdivided into two halves. The samples were embeded in an acrylic resin, resulting in 30 specimens divide

In this study, composite materials consisting of Activated Carbon (AC) and Zeolite were prepared for application in the removal of methylene blue and lead from an aqueous solution. The optimum synthesis method involves the use of metakaolinization and zeolitization, in the presence of activated carbon from kaolin, to form Zeolite. First, Kaolin was thermally activated into amorphous kaolin (metakaolinization); then the resultant metakaolin was attacked by alkaline, transforming it into crystalline zeolite (zeolitization). Using nitrogen adsorption and SEM techniques, the examination and characterization of composite materials confirmed the presence of a homogenous distribution of Zeolite throughout the activated carbon.