Background: The fracture of instruments within root canal during endodontic treatment is a common incidence, fracture because of fatigue through flexure occurs due to metal fatigue, this study aimed to assess the effect of curvature angle and rotational speed on the cyclic fatigue of different type of Endodontic NiTi Rotary Instruments and compare among them. Materials and method: Three types of rotary instruments with tip size 0.25: ProTaPer F2 (Densply, Malifier) Revo-S SU( 0.06 taper, MicroMega) and RaCe system (0.06 taper, FKG, Dentaire), Forty file of each instrument were used within two canals with angle of curvature (40 &60 )at two speed (250&400)RPM, twelve group were formed for all instruments(total number=120),ten file for each group. The testing canals customized within stainless steel block covered with glass face, the time to fracture recorded and the mean of cycles to fracture (MCF) detected for each instrument. Data were analyzed statistically by ANOVA, LSD and Independent T-test at 5% significant level. Result: there was a highly significant difference of curvature angle and significant difference of rotational speed on the fracture resistance of instruments. RaCe revealed the best fracture resistance followed by ProTaper then Revo-S that showed the less resistance. Conclusion: The rotary instruments more prone to fracture when used at more curvature angle and higher rotational speed, as well as the rotary instruments differ from each other according to manufacturing process, taper, cross section and other factors.
Fatigue failure is almost considered as the predominant problem affecting automotive parts under dynamic loading condition. Thus, more understanding of crack behavior during fatigue can strongly help in finding the proper mechanism to avoid the final fracture and extent the service life of components. The main goal of this paper is to study the fracture behavior of low carbon steel which is used mostly in automotive industry. For this purpose, the fractography of samples subjected to high and low stress levels in fatigue test then was evaluated and analyzed. Hardness and tensile tests were carried out to determine the properties of used steel. Also, the samples were characterized by microstructure test and XRD analysis to examine the con
... Show MoreGA Al Omran, AA Noaimi, Z Al Madfai, H Al Hamamy, Journal of the Faculty of Medicine Baghdad, 2012
Background: Even the wide use of dental implants, still there is a proportion of implants are failed due to infection. Much considerable attention has been paid to modify the implant surface. Coating of dental implant with a biocomposite material of suitable properties can improve osseointegration. And this is the main concern of this study. The aim of present study was to evaluate the use of a biocomposite coating of dental implant with (ceramic nano Al2O3 and metalic AgNo3) on the bond strength at bone – implant interface and tissue reaction. Materials and methods: A total number of forty-eight screws, CpTi dental implant used in this study. Half of these screws were coated with a biocomposite material of nano (Al2O3and AgNo3), thi
... Show MoreThis research include the designation of newly instrument (Turbidmeter) depending on using photo voltaic detector (8.5mm.*8.5mm.).These dimensions have large area which increases the scattering rays with a variable intensity. The properties of this design are local mode and the used tools are a available in the local markets as well as its less cost light weight system. It is worth mentioning that the possibility of its application in many fields such as: Clinical, Laboratory, Industrial and Fuel fields. This designation, applied to estimate Barium Sulphate in turbidity method. The analytical results show high accuracy and repetition, also the linearity ranges from (4-180) ppm. At the detection limit (0.05) ppm. With correlation coefficient
... Show MoreOxidative stress is oxidative damage caused by free radicals and reactive oxygen species (ROS). These ROS can cause oxidative damage to cellular components, including membrane lipids, receptors, enzymes, proteins, and nucleic acids. It would eventually lead to cell apoptosis and the appearance of certain pathological conditions. This work investigates the antioxidant potentials of chamomile extract in vitro by evaluating the extract activity to scavenge 2,2-Diphenyl-1-picrylhydrazyl (DPPH), also in vivo by investigating its effects on oxidative stress-induced rats by assessing the total oxidant status (TOS) and total antioxidant capacity in the radiation exposed rats with and without the treatment with chamomile extract. The results
... Show MoreOne of the most popular causes for implant infection is dental plaque bacteria. Previous studies have shown the bactericidal effect of CO2 laser irradiation on bacteria associated with soft tissue surrounding the implant materials. No published studies have examined the effect of irradiation by CO2 laser on Streptococcus oralis and Staphylococcus aureus.The aim of this study was to evaluate the bactericidal effect of CO2 laser on bacteria that are causing dental implant infections. This study was carried out on two isolates of bacterial species out of 25 samples, isolated from patients having soft tissue infections around the dental implant. These two pure isolates including Streptococcus oralis and Staphylococcus aureus were identified
... Show MoreBackground: Many types of instruments and techniques are used in the instrumentation of the root canal system. These instruments and techniques may extrude debris beyond the apical foramen and may cause post-instrumentation complications. The aim of this study was to evaluate the amount of apically extruded debris resulted by using 4 types of nickel-titanium instruments (WaveOne, TRUShape 3D conforming files, Hyflex CM, and One Shape files) during endodontic instrumentation. Materials and methods: Forty freshly extracted human mandibular second premolar with straight canals and a single apex were collected for this study. All teeth were cut to similar lengths. Pre-weighted glass vials were used as collecting containers. Samples were randoml
... Show MoreObjective. This study aimed to evaluate and compare the force degradation of two types of elastomeric chains following different periods of immersion in zinc-containing mouthwashes. Materials and Methods. Four hundred and forty pieces of Elasto-Force and Super Elasto-Force elastomeric chains were divided into two control and eight experimental groups. The pieces were stretched to 25 mm on pins mounted on an acrylic block and stored in distilled water at 37°C. The experimental groups were immersed in four different types of mouthwash for one minute twice a day throughout the test period. Ten continuous thermocycles per day between cold and hot water baths (5–55°C) were carried out. Forces were measured at six-time intervals (in
... Show MoreAllah Almighty has aggrandized the position of orphans and elevated their status in the society and has given the graces for those who sponsor the orphan and care for and protecting them, even those who rub their heads. The divine care is manifested in the verses of the Holy Bible and the Holy Quran. Therefore, the whole world cared for the orphan, and called for the rights of the orphans in the conferences and the channels. But all that was little effort that does not meet what the orphan need and some were only ink on paper that were not applied. All that mentioned above is necessary in dealing with the study (the rights of orphans in the Old Testament and Islam, a Comparative Study). The study was divided into a Preface and four inquirie
... Show More