Background: the aim of this study was to evaluate the effect of different surface acids treatments (37%phospjoric acid, 5%hydrofluoric acid, 1.23 acidulated phosphate fluoride) of feldspathic ceramic VITA 3D MASTER , and the effect of thermocycling on shear bond strength using a ceramic repair kit (ivoclar/vivadent). Material and Methods: sixty Nickel-Chromium metal base plates were prepared(9mm diameter,3mm depth) using lost wax technique, 2mm thick layer of ceramic(VITA 3D MASTER) fused to metal plates, all specimens were embedded in acrylic resin blocks except their examined surfaces and divided into 3 main groups 20 specimens each, Grp A: treatment with 37%phosphoric acid for 2 mins, Grp B: etching with 5% hydrofluoric acid for 2mins, Grp C: etching with 1.23% acidulated phosphate fluoride for 10 mins; monobond-plus, heliobond, resin composite(Tetric EvoCeram) were applied to each specimen according to manufacturer's instruction using transparent split mold(5mm diameter, 4 mm height); specimens were stored in 37OC distilled water for 12 weeks, 10 specimens of each group were subjected to thermocycling between 5 oC and 55 o C for 800 cycles with 30s dwell time; shear bond strength was determined by a universal testing machine (instron 1122) at a cross head speed 0.5mm/min; One way ANOVA test, LSD test and student-t test were used to analyze shear bond strength. Results: Mean shear bond strength values for the tested groups were: A1= 11.65±0.68 Mpa, A2=10.88±0.58 Mpa, B1=17.93±0.41 Mpa, B2=17.42±0.35 Mpa, C1=15.17±0.61 Mpa, C2=14.51±0.48 Mpa ; one way ANOVA test showed highly significant difference among groups; LSD test revealed that the use of 5% HF for ceramic surface treatment(GB) was highly significant than the treatment with 37%PA(GA) or 1.23%APF(GC) respectively and the use of 1.23%APF(GC) was highly significant than the use of 37%PA(GA); Student t- test showed a significant difference between subgroups of the same group with and without thermocycling. Conclusion: ceramic surface treated with 5% HF acid for 2 mins recorded the highest shear bond strength, followed by surface treatment with 1.23% APF for 10 mins, most specimens treated with 5%HF showed cohesive failure with in ceramic while specimens treated with 1.23%AFP showed more (adhesive/cohesive) failure than adhesive or cohesive alone, and specimens treated with 37% PA showed nearly 50:50 adhesive and combination failure, thermocycling reduced the bond strength of each group significantly
Magnesium aluminum silicate of glass ceramic having different amounts of magnesium fluoride in the range (0-13.2)%. Thermal expansion coefficient and micro hardness of the base glass and glass ceramic samples are seen to be interdependent but due to the multi – component system, the behaviour is seen to be somewhat complex, with an increase in Mg F2 content. The thermal expansion coefficient increase and micro harness decrease, numerical simulation of thermal expansion and hardness is useful in this study, L2 – regression is used to calculate the two parameters associated with each glass component, by comparing the measured parameters and the calculated parameters ,it is useful to use such a method to calculate the quantity
... Show MoreThe current study, which extended from February 2020 to June 2021 at the University of Thi- Qar\ College of Education for Pure Sciences, aimed to follow the changes in external morphological features at different Embryonic Developmental stages in pregnant mice treated with different doses of Rapamycin (Rapa). Use In this study, 32 pregnant mice were divided randomly into four groups, each of which had eight pregnant mice. Each group received different dose of Rapa via intraperitoneally injection at different gestation days until the end of the specified periods, whereas the control group received a DMSO. Mice were administered under the same circumstances and dosages were determined based on body weight, as specified in pharmaceutical const
... Show MoreRoller-Compacted Concrete is a no-slump concrete, with no reinforcing steel, no forms, no finishing and wet enough to support compaction by vibratory rollers. Due to the effect of curing on properties and durability of concrete, the main purpose of this research is to study the effect of various curing methods (air curing, 7 days water curing, and permanent water curing) and porcelanite (local material used as an Internal Curing agent) with different replacement percentages of fine aggregate (volumetric replacement) on some properties of Roller-Compacted Concrete and to explore the possibility of introducing practical Roller-Compacted Concrete for road pavement with minimum requirement of curing. Specimens were sawed fro
... Show MoreThe corrosion inhibition of low carbon steel in1N HCl solution in the presence of peach juice at temperature (30,40,50,and 60)°C at concentration ( 5, 10, 20, 30, 40and 50 cm3/L)were studied using weight loss and polarization techniques. Results show that the inhibition efficiency was increased with the increase of inhibitor concentration and increased with the increase of temperature up to 50ºC ,above 50ºC (i.e. at 60 ºC) the values of efficiency decreases. Activation parameters of the corrosion process such as activation energies, Ea, activation enthalpies, ΔH, and activation entropies, ΔS, were calculated. The adsorption of inhibitor follows Langmuir isotherm. Maximum inhibition efficiency obtained was a bout 91% at 50ºC in the
... Show MoreBackground: Change in palatal vault shape and Reinforcement of high impact acrylic denture base resin may in turn affect the dimensional accuracy of acrylic resin and affecting the fitness of the denture. The aim of study is to evaluate the effect of fiber reinforcement for high-impact acrylic resin denture base with different palatal vault shapes on linear dimensional change and effect of palatal vault shapes on linear dimensional changes of non-reinforced and fiber reinforced high impact denture base acrylic resin Material and method: Three different palatal vault shapes were prepared on standard casts using CNC (computer numerical control) machine. 60 samples of heat polymerized high impact acrylic resin maxillary denture base were fabri
... Show MoreABSTRACT Background: This study measured the effects of three parameters pH value, length of immersion and type of archwire on metal ions released from orthodontic appliances. Materials and Methods: Ninety maxillary halves simulated fixed orthodontic appliances that were immersed in artificial saliva of different pH values (6.75, 5 and 3.5) during 28 day period. Three types of archwires were used: stainless steel, nickel titanium and thermal activated nickel titanium. The quantity of nickel and chromium ions was determined with the use of atomic force spectrophotometer while iron ions by spectrophotometer. Each orthodontic set was weighted two times, before the ligation and immersion in the artificial saliva and after 28 days at the end of
... Show MoreBackground: Change in palatal vault shape and Reinforcement of high impact acrylic denture base resin may in turn affect the dimensional accuracy of acrylic resin and affecting the fitness of the denture.This study evaluated tostudy the effect of fiber reinforcement for high-impact acrylic resin denture base with different palatal vault shapes on adaptation or gap space between the denture base and the stone cast and compare with non-fiber reinforcement and effect of palatal vault shapes on adaptation of non-reinforced and fiber reinforced high impact denture base acrylic resin Material and method: Three different palatal vault shapes were prepared on standard casts using CNC (computer numerical control) machine. 60 samples of heat polymeri
... Show More
(5)
(3)
The Moisture damage is considered as one of the main challenge for the experts in the field of asphalt pavement design. The aims of the present study is to modify moisture resistance of the asphalt concrete by utilizing ceramic fibers as a type of reinforcement incorporated with hydrated lime. For this purpose, a penetration grade of the asphalt cement (40-50) was utilized as a binder with an aggregate of the maximum nominal size of 12.5mm and mineral filler limestone dust. A series of specimens has been fabricated by utilizing 0.50, 1.0, 1.5, and 2.0 percentages of ceramic fibers. For each of these contents, another subsequent group of specimens with hydrated lime with 0.0, 1.0, 1.5, and 2.0 percentages were moulded. For the additi
... Show More
(1)