Introduction: This study aimed to evaluate the impact of ozonated water on water sorption and solubility of heat-cure acrylic resin. Methods: Thirty-three samples of heat-cured acrylic resin were manufactured and divided into three groups: control, immersion for 10 and 20 minutes in ozonated water. Water sorption and water solubility tests were carried out in line with ADA Standard No. 12 for denture-base acrylic resin. Data were analyzed using one-way ANOVA at a significance level of 5%. Results: There was a nonsignificant difference between the control and experimental groups regarding water sorption (P

The research aims to study the effect of adding (Li2O) to an alkaline glaze containing (K2O, Na2O). Although all the alkaline oxides have common properties, each oxide has something that distinguishes it. The molecular weight of (Li2O) is two times less than that of (Na2O) and three times that of (K2O). Therefore, it is added in small proportions. In addition, it is a very strong flux, so it is not used alone, but rather replaces a part of other alkaline oxides. It was added to an alkali glass that matured at a temperature of 980CO in proportions (2.0,1.4,1.2,0.8,0.4%) instead of (Na2O), using lithium carbonate (Li2CO3) as an oxide source. The glazes mixtures were applied to a white pottery body, and the samples were fired and cooled acc

Objective This study evaluated the effects of adding titanium oxide (TiO2) nanofillers on the tear strength, tensile strength, elongation percentage, and hardness of room-temperature-vulcanized (RTV) VST50F and high-temperature-vulcanized (HTV) Cosmesil M511 maxillofacial silicone elastomers. Methods Two types of maxillofacial elastomers, VST50F RTV and Cosmesil M511 HTV, were used. Nano-TiO2 powder was applied as a nanofiller. A total of 120 specimens were fabricated, 60 each of VST50F and Cosmesil M511. The specimens of each type of elastomer were divided into three equal groups on which tests were conducted for tear strength, tensile strength, and hardness i.e., 20 specimens were used for each test. Each group of 20 specimens was further

Gestational Diabetes Mellitus (GDM) is the most common metabolic disorder that found during gestation and is define as hyperglycemia of variable severity with onset or first recognition during gestation that does not clearly characterize any form of the preexisting diabetes (American Diabetes Association [1]). It affects approximately 16.5% of pregnancies worldwide (Plows, et al.[2]). The placenta is an organ that connects the mother and her fetus during pregnancy (Gul, et al.[3]). In the placenta, glucose can be transformed into glycogen for storage by either glycogen synthase or using glycogenin as a prime. However, the function of glycogen deposition stays a matter of debate, it may be the source of fuel for placenta itself or the storag

Background: One of the drawbacks of vital teeth bleaching is color stability. The aim of the present study was to evaluate the effects of tea and tomato sauce on the color stability of bleached enamel in association with the application of MI Paste Plus (CPP-ACPF). Materials and Methods: Sixty enamel samples were bleached with 10% carbamide peroxide for two weeks then divided into three groups (A, B and C) of 20 samples each. After bleaching, the samples of each group were subdivided into two subgroups (n=10). While subgroups A1, B1 and C1 were kept in distilled water, A2, B2, and C2 were treated with MI Paste Plus. Then, the samples were immersed in different solutions as follow: A1 and A2 in distilled water (control); B1 and B2 in black

Background: The Initial (primary) stability is one of the factors that play an important role in the success of the dental implants. The purpose of this study was to evaluate the initial stability of dental implant with horizontal plate by using five analytical tests: insertion torque, removal torque, resonance frequency analysis, push-in test and pull-out test. Materials and methods: Two different lengths of dental implants (5mm and 10mm) were tested in this study; each dental implant was 4mm in diameter with a square threads shape of 1mm pitch and 0.5mm depth. The crestal area was 4.2mm diameter contained a right angle margin circumferential ring while the apical area was tapered with two self-tapping grooves. In this study, the initial s

In recent years, there has been growing interest in using Nanosystems in different biomedical applications. Among all metal nanoparticles, selenium nanoparticles have attracted the attention of many researchers due to its low toxicity and nutritional supplementation value. The purpose of the current study was designed to examine the possible effect of selenium nanoparticles in combination with fenugreek leaves extract (an edible herb with good medicinal properties) in the treatment of oxidative stress status-related to polycystic ovary syndrome in letrozole-induced PCOS (an imbalance of reproductive hormones that causes infertility) in adult female rats. Cold plasma was used in the preparation of selenium nanoparticles subsequently the prod

Zinc Oxide nanoparticles were prepared using pulsed laser ablation process from a pure zinc metal placed inside a liquid environment. The latter is composed of acetyltrimethylammonium bromide (CTAB) of 10−3 molarity and distilled water. A Ti:Sapphire laser of 800 nm wavelength, 1 kHz pulse repetition rate, 130 fs pulse duration is used at three values of pulse energies of 0.05 mJ, 1.11 mJ and 1.15 mJ. The evaluation of the optical properties for the obtained suspension was applied through ultraviolet–visible absorption spectroscopy test (UV/VIS). The result showed peak wavelengths at 210 nm, 211 nm and 213 nm for the three used pulse energies 0.05 mJ, 1.11 mJ and 1.15 mJ respectively. This indicates a blue shift,

ABSTRACT Background: Diabetes and periodontitis are complicated prolonged disorders through a recognized two-way association. There is elongated-conventional mark that hyperglycaemia in diabetes is affected on immune-inflammatory response and disturb the action of osteoclast and in balance bone turnover, which might rise the person vulnerability to the progress of prolonged periodontitis. Osteocalcin is one of the greatest plentiful matrix proteins originate in bones and produced absolutely there. Small osteocalcin crumbles are noticed in regions of bone remodeling and are in fact degradation products of the bone matrix, that is released outside cells into the Gingival Crevicular Fluid (GCF) and saliva after destruction of periodontal tissu