Internal curing is a method that has been advised to decrease the primary age cracking, mainly of concrete mixes using low (water to cementitious materials - w/cm) ratios corresponding to the self-compacting concrete-(SCC). This research aims to study the effect of the internal curing using saturated lightweight aggregate- (LWA) on the steel reinforcing corrosion in SCC. In this research, crushed bricks or thermostone were partially replaced by (20%) by the weight of sand and volumetrically measured. The results showed that the steel reinforcement of internally cured concrete showed a slight increase in corrosion up to 300 days of exposure to the saline solution (containing 3.5% NaCl). The ability of using the crushed bricks or thermostone

Unsaturated soil can raise many geotechnical problems upon wetting and drying resulting in swelling upon wetting and collapsing (shrinkage) in drying and changing in the soil shear strength. The classical principles of saturated soil are often not suitable in explaining these phenomena. In this study, expansive  soil (bentonite and sand) were tested in different water contents and dry unit weight chosen from the compaction curve to examine the effect of water content change on soil properties (swelling pressure, expansion index, shear strength (soil cohesion) and soil suction by the filter paper method). The physical properties of these soils were studied by conducting series of tests in laboratory. Fitting methods

Roller Compacted Concrete (RCC) is a mass concrete with zero slump consisting of well-graded aggregate, cementitious materials and water. RCC has many advantages over other pavement types, particularly cost and speed of construction. However, it also presents difficulties with high-speed applications related to surface texture and surface evenness. These difficulties have so far restricted the use of RCC to the lower layers of normal roads. This study investigates the possibility of expanding the application of RCC for normal roads and highways by using a two-layer system of roller compacted concrete. The suitability of RCC for such an application depends fundamentally on bond strength between the layers. The bond strength measured by shear

Experimental research was carried out to investigate the effect of fire flame (high temperature) on specimens of short columns manufactured using SCC (Self compacted concrete). To simulate the real practical fire disasters, the specimens were exposed to high
temperature flame, using furnace manufactured for this purpose. The column specimens were cooled in two ways. In the first the specimens were left in the air and suddenly cooled using water, after that the specimens were loaded to study the effect of degree of
temperature, steel reinforcement ratio and cooling rate, on the load carrying capacity of the reinforced concrete column specimens. The results will be compared with behaviour of columns without burning (control specime

Roller compacted concrete (RCC) is a type of rigid pavement that is designed in a similar way to conventional concrete pavements reflecting its mode of failure. The thickness design of RCC pavements is based on keeping the flexural stresses and fatigue damage in the pavement caused by wheel loads within allowable limits. As in all jointed concrete pavements, there is a greater effect from loads placed along edges and less at interior locations in the pavement. Joints in RCC pavement are clearly critical areas and form weak points. RCC is typically constructed with saw-cut joints to prevent random cracking, improve the appearance of the pavement surface, and maintain the highest possible load transfer across the joints. This paper pr

Roller compacted concrete (RCC) is a form of plain concrete pavement (JPCP). RCC is a zero-slump concrete consisting of well-graded aggregate, cement and water. RCC has many advantages over other pavement types, particularly cost and speed of construction. Recently, RCC has undergone many developments mostly directed towards improving quality, including smoothness and durability. RCC now has the potential to combine the performance of concrete with the low cost of asphalt installation. A two-layer system of RCC with different aggregate types and sizes was utilized in this study. This paper presents the determination of load transfer stiffness across induced joints in a two-layer RCC system based on a cyclic shear test. The test was

The main objectives of this study were investigating the effects of the maximum size of coarse Attapulgite aggregate and micro steel fiber content on fresh and some mechanical properties of steel fibers reinforced lightweight self-compacting concrete (SFLWSCC). Two series of mixes were used depending on maximum aggregate size (12.5 and 19) mm, for each series three different steel fibers content were used (0.5 %, 1%, and 1.5%). To evaluate the fresh properties, tests of slump flow, T500 mm, V funnel time, and J ring were carried out. Tests of compressive strength, splitting tensile strength, flexural tensile strength, and calculated equilibrium density were done to evaluate mechanical properties. For reference mixes, the