In this research thin films of (CdTe) have been prepared as pure and doped by Zn
with different ratios (1,2,3,4,5)% at thickness (400+25)nm with deposition rate (2±0.1)nm,
deposited on glass substrate at R.T. by using thermal evaporation in vacuum . All samples
were annealed at temperature (523,573,623,673)K at 1h.
The structural prop erties of all prepared thin films, doped and undoped have been
studied by using XRD. The analysis reveals that the structures of the films were
polycrystalline and typed cubic with a preferred orientation along (111) plane for the
undoped films with (2,3)% of zinc , and shifting (2ÆŸ) for doped films . The annealing films
at temperature 573 K and Zn:3% show decreasing in

Purepolyaniline and doped with hydrochloric acid was prepared in different molarities at room temperature. The a.c electrical properties were stadied.AC conductivityσac (ω), is found to vary as ωS in the frequency range (100Hz-10MH), S< 1and decreases indicating a dominate hopping process. Thedielectric constant ε1and dielectric loss ε2 have been determined for bulk polyaniline. ε1 decrease with the increase frequency. Electrical conductivity measurements increase with the increases both of the amount of HCl and the dose of radiation. The dielectric investigations show decrease with dose radiation.

Sorghum seeds suffer from a low germination ratio, so a factorial experiment was carried out in the Seed Technology Laboratory, Department of Field Crops, College of Agricultural Engineering Sciences, University of Baghdad during 2022 according to a Completely Randomized Design with four replications to study the effect of stimulating seeds with aqueous extract of banana peels with a concentration of (0, 15, 25 and 35%) and citric acid at concentrations (0, 50, 100 and 200 mg L-1) on viability and vigour of seed properties. Seeds that soaked with banana peel extract at a concentration of 25% outperformed in first count (79.8%), final count (85.0%), radicle length (13.2 cm), plumule length (11.6 cm), and seedling vigour index (2109), noting

This study was conducted in Animal Resources Department , College of Agriculture to estimate the effect of chemical and biological treatments to improve the nutritive value of poor quality roughages ( corn cobs and wild reed ) . The feeds were treated chemically with 4% NaoH solution ,whereas Aspergillus niger was used to ferment corn cobs and wild reed samples . The chemical analysis showed that protein percentages of corn cobs and wild reed was increased significantly (P<0.05) from 6.05% to 10.51% and 17.70% and from 3.10 %to 6.50% and 9.96% for both chemical and biological treatments respectively. The crude fiber percentages decreased significantly (P<0.05) from 29.19% and 26.10% to 23.60% and 20.10% for chemical treatment and was 20

DBN Rashid, International Journal of Development in Social Sciences and Humanities, 2020

Research in Iraq has expanded in the field of material technology involving the properties of the lightweight concrete using natural aggregate. The use of the porcelinate aggregate in the production of structural light concrete has a wide objective
and requires a lot of research to become suitable for practical application. In this work metakaolin was used to improve compressive strength of lightweight porcelinate concrete which usually have a low compressive strength about 17 MPa . The effect of metakaolin on compressive, splitting tensile, flexure strengths and modulus of elasticity of lightweight porcelinate concrete have been investigated. Many experiments were carried out by replacing cement with different percentages of
met

This study investigates the ionic conduction dependence on the size of alkaline cations in gel polymer electrolytes based on double iodide can enhance by incorporating a salt having a bulky cation.

This study was conducted according to contract with the North Refineries Company-Baiji and deals with the hydrodesulphurization of vacuum gas oil of Kirkuk crude oil, boiling range 611-833 K. A trickle bed reactor packed with a commercial cobalt-molybdenum on alumina catalyst was used. The operating conditions were: temperature range 583-643 K, liquid hourly space velocity range 1.50-3.75 1/h, hydrogen to oil ratio about 250 l/l and pressure kept constant at 3.5MPa.
The results showed that the aromatic content decreased and sulfur removal increased with increasing temperature and decreasing space velocity. The properties (viscosity, density, flash point and carbon residue) of the products decrease with temperature increasing, but the