Objective:Fluorid-containing dental alginate impression materials can exert a considerable reduction in
enamel solubility. The objective was to evaluate the effect of fluoride addition on the setting time and
compressive strength of alginate impression materials.
Methodology: 60 samples were constructed from alginate impression material (30 samples for setting
time test and 30 samples for compressive strength test).Specimens of each test divided into three
subgroup. Group A: 10 specimens of alginate were mixed with distilled water [control], Group B: 10
specimens of alginate were mixed with100-ppm fluoride and Group C:10 specimens of alginate were
mixed with 2%Naf.
Results: the result of setting time test showed that addition of 2% Naf to alginate impression materials
were delayed the setting reaction while the results of compressive strength test showed that high mean
values were obtained from control group while group mixed with 2%Naf had lower compressive
strength.
Recommendation: it can be concluded that addition of 100-ppm fluoride were affect on the
properties of alginate impression materials while addition of 2% Naf was deteriorated the properties of
alginate impression materials. So recommends the effect of fluoride addition in other concentration
Abstract
This study aimed to survey fungi associated with the product Indomie and Chips being the trades Iargely by a very important segment of society who are the children, beside consumed by adults, but less so, as the survey results to accompany some fungui samples sterile showed proportions presence included various fungi like. Aspergillus flavus, Aspergillus niger, Penicillium Spp., Fusarium graminearum, F.moniliforme, Alternaria alternate and Rhizopus Spp., and other fungi sterile are not diagnosed. The results showed large dominion fungi A. niger by presence sterile samples of both producers, followed by infection in Fusarium Spp., Penicillium Spp., and A. alternata by infection percentage 55, 20 and 17% respectively for the pr
In this work, (CdO)1-x (CoO)x thin films were prepared on glass slides by laser-induced plasma using Nd:YAG laser with (λ=1064 nm) and duration (9 ns) at different laser energies (200-500 mJ) with ratio (x=0.5), The influence of laser energy on structural and optical properties has been studied. XRD patterns show the films have a structure of polycrystalline wurtzite. As for AFM tests results for the topography of the surface of the film, where the results showed that the grain size and the average roughness increase with increasing laser energy. The optical properties of all films were also studied and the results showed that the absorption coefficient for within the wavelength range (280-1100 nm), The value of the optical power gap fo
... Show More
(4)
(2)
(2)
(1)
(1)
(1)
(1)
(2)
(2)
(6)
(6)
Thin films of (CdO)x (CuO)1-x (where x = 0.0, 0.2, 0.3, 0.4 and 0.5) were prepared by the pulsed laser deposition. The CuO addition caused an increase in diffraction peaks intensity at (111) and a decrease in diffraction peaks intensity at (200). As CuO content increases, the band gap increases to a maximum of 3.51 eV, maximum resistivity of 8.251x 104 Ω.cm with mobility of 199.5 cm2 / V.s, when x= 0.5. The results show that the conductivity is ntype when x value was changed in the range (0 to 0.4) but further addition of CuO converted the samples to p-type.
(9)
(10)
Electronic properties including (bond length, energy gap, HOMO, LUMO and density of state) as well as spectroscopic properties such like infrared, Raman scattering, force constant, reduced mass and longitu- dinal optical mode as a function of frequency are based on size and concentration of the molecular and nanostructures of aluminum nitride ALN, boron nitride BN and AlxB7-XN7 as nanotubes has calculated using Ab –initio approximation method dependent on density functional theory and generalized gradient approximation. The geometrical structure are calculated by using Gauss view 05 as a complementary program. Shows the energy gap of ALN, BN and AlxB7-XN7 as a function of the total number of atoms , start from smallest molecule to reached
... Show More
(2)
(2)