Petrography and physicomechanical characteristics of Iyuku granite from southwestern Nigeria were investigated. Rock and aggregate samples were obtained from five different quarry sites for thin-sectioning and physical and mechanical tests. The rock slides were subjected to petrographic analysis, while the aggregates were tested for the parameters of specific gravity (S.G), water absorption, aggregate impact value (AIV), aggregate crushing value (ACV), Los Angeles abrasion value (LAAV), and flakiness and elongation indices in accordance with the British Standards (B.S), American Standards for Testing Materials (ASTM) and Federal Ministry of Works Standards (FMWS). The petrographic, physical, and mechanical characteristics were described

Magnetic plaster kiln dust (MPKD) was synthesized as a unique, low-cost composite reused of byproduct plaster kiln dust (PKD), which is considered a source of air pollution. The FESEM, EDS, XRD, FTIR, VSM, and BET tests were used to characterize the MPKD. The characterization revealed that the MPKD was nanotubes non-agglomerated and super-paramagnetic with a high specific surface area (102.7 m²/g). Compared with the specific area of other materials (composites), the MPKD could be considered a promising substance in the field of water/wastewater treatment.

Silver nanoparticles (Ag-NPs) have been prepared using the electro-chemical
method. The experimental setup of this technique consist of two electrodes of pure
silver (99.2 %), the applied voltage on the electrodes is 20 V and the current through
the colloidal was about 0.4 Amp. The silver nanoparticles crystallization has been
studied; the crystalline structure appears Face center Cubic. The optical properties of
silver nanoparticles are strongly affected by the Local Surface Plasmon Resonance
(LSPR). The wavelength of maximum absorption band for an Ag NPs have a range
(~350nm-550nm).

In this study, In2O3 was prepared by Solvothermal technique in autoclave device, which is a simple and inexpensive technique to indicate the best condition. The reaction took place between indium chloride and urea. In(OH)3 as-prepared annealing at 100°C and convert to In2O3 at annealing temperatures 300, 500, 700 °C for 90 min .The physical properties of nanoparticles were characterized by XRD, SEM, AFM, UV/Visible and FTIR spectroscopy measurements. The examination results of XRD for In2O3 powder annealed at different temperature showed the formation of a cubic phase of nanoparticles with high intensity of plane (222). The lattice constant decreases with the increase of annealing temperature (from 10.07 to 10.04 Ǻ). AFM indicated an

Nanoparticles are defined as an organic or non-organic structure of matter in at least one of its dimensions less than 100 nm. Nanoparticles proved their effectiveness in different fields because of their unique physicochemical properties. Using nanoparticles in the power field contributes to cleaning and decreasing environmental pollution, which means it is an environmentally friendly material. It could be used in many different parts of batteries, including an anode, cathode, and electrolyte. This study reviews different types of nanoparticles used in Lithium-ion batteries by collecting the advanced techniques for applying nanotechnology in batteries. In addition, this review presents an idea about the advantages and d

This study was conducted to investigate the antibacterial activity of green synthesized copper oxide nanoparticles (CuO NPs) using Aloe vera. Initially, bacteria were collected from clinical samples of patients having otitis media infection and the isolates were identified at the species level following biochemical tests. Copper oxide nanoparticles were prepared by green synthesis using Aloe vera leaves and characterized using UV- visible spectroscopy at 260 nm peak. The shape and size were determined by using transmission electron microscopy (TEM) and the dimensions of the particles were more precisely determined by using scanning electron microscopy (SEM) and x-ray diffraction (XRD). Different concentrations of nanopa

Background. Nanocoating of biomedical materials may be considered the most essential developing field recently, primarily directed at improving their tribological behaviors that enhance their performance and durability. In orthodontics, as in many medical fields, friction reduction (by nanocoatings) among different orthodontic components is considered a substantial milestone in the development of biomedical technology that reduces orthodontic treatment time. The objective of the current research was to explore the tribological behavior, namely, friction of nanocoated thin layer by tantalum (Ta), niobium (Nb), and vanadium (V) manufactured using plasma sputtering at 1, 2, and 3 hours on substrates made of 316L stainless steel (SS),