The purpose of this study is the activation of natural Iraqi bentonite that has been obtained from Wadi Bashira region, in the Western Desert of Iraq, to obtain the Nano particle sized then Nano-Quartz was extracted. This method included bentonite nano particles preparation by purification with HCl solution, calcination, the planetary ball mill to get bentonite in nanometer size and centrifugation to obtain the Nano-quartz. Results of quartz purification process were characterized by Fourier transforms infrared spectroscopy (FTIR), energy dispersive X-ray spectroscopy (EDS) and scanning electron microscope (SEM), particle size analyzer (PSA) and the X-rays diffraction (XRD). All tests have shown almost a clear decline in the proportion of the high-calcium in crude Iraqi bentonite in conjunction with an increase in high rates of silica in Quartz phase.
The corrosion behavior of low carbon steel in washing water of crude oil solution has been studied potentiostatically at five temperatures in the range ( 303 –343 )K, at pH ( 4 ) and at pH (4,6,7,9,11 ) at (343K)..The corrosion potential shifted to more negative values with increasing temperature and the corrosion current density increased with increasing temperature, the corrosion current density (icorr) decreased with increasing pH in the rang ( 4 – 7 ) and it increased with increasing pH in the rang ( 9 – 11 ) at ( 343 K ), while the corrosion potential generally variation with increasing pH in the rang (4-11)at(343K. From the general results for this study can be seen that thermodynamic and kinetic function were
... Show MoreBackground: Aluminium (Al) intoxication was recognised as a causal agent in p a t i ent s undergoing haemodialysis and then was linked to Alzheimer's disease. Nevertheless, environmental pollution with Al is mainly v i a drinking water, particularly when acidic rain falls on Al containing soil and bedrock. In addition, aluminium utens i l s are widely used for cooking. Therefore, an increasing concern is emerging for the role of pH in the absorption of aluminium from ingested food.
Materials and methods: The objective of this study was to establish the effect of acidification with1 ml/dL of concentrated acetic acid on the absorption of aluminium from a 5 mM a l u mi n i u m sulphate\ solution taken orally
In this work, some of new 2-benzylidenehydrazinecarbothioamide derivatives
have been prepared by condensation of thiosemicarbazide and different substituted
aromatic benzaldehydes in presence of glacial acetic acid to give compounds (1-6),
these compounds have characterized by its physical properties and spectroscopic
methods. This work also included theoretical study to prove the ability of these
compounds as corrosion inhibitors; The program package of Gaussian 09W with its
graphical user interface GaussView 5.0 had used for this purpose; the methods of
Density Functional Theory (DFT) with basis set of 6-311G (d,p) / hybrid function of
B3LYP and semiempirical method of PM3 have been used, the study included
t
The present research was conducted to synthesis Y-Zeolite by sol-gel technique using MWCNT (multiwalled carbon nanotubes) as crystallization medium to get a narrow range of particle size distribution with small average size compared with ordinary methods. The phase pattern, chemical structure, particle size, and surface area were detected by XRD, FTIR, BET and AFM, respectively. Results shown that the average size of Zeolite with and without using MWCNT were (92.39) nm and (55.17) nm respectively .Particle size range reduced from (150-55) nm to (130-30) nm. The surface area enhanced to be (558) m2/g with slightly large pore volume (0.231) km3/g was obtained. Meanwhile, degree of crystallization decrease
... Show MoreThis study was undertaken to prepare Nano zinc oxide (ZnO) by precipitation and microemulsion methods. Scanning electron microscopy (SEM), X-ray diffraction (XRD), FTIR spectrometry, atomic force microscopy (AFM), and Brunauer Emmett Teller (BET) surface area were the techniques employed for the preparation. The particle size of prepared nano ZnO was 69.15nm and 88.49nm for precipitation and microemulsion methods, respectively, which corresponded to the BET surface area 20.028 and 16.369m2/g respectively. The activity of prepared nano ZnO as a photocatalyst was estimated by the removal of ampicillin (Amp) under visible light. This study, therefore, examined the effect of pH in the range of 5-11, initial concen
... Show MoreUsing three-point bending experiments, the effect of the particle size of SiO2 on the flexural properties of epoxy composites was investigated. Young modulus and flexural strength were studied for different weight percentage of filler (2,4,6,8 and 10) wt%.The size of SiO2 particles varied from micro (100um) to nano (12nm) .
Flexural strength and Young modul were found to increase with the filler content, but when the particle size decreased to the nanoscale, the Young module increased. Flexural strength was higher for microcomposites than nanocomposites.
This study includes the preparation of the ferrite nano ferrite CuxAl0.3-XNi0.7Fe2O4 (where: x = 0, 0.05, 0.1, 0.15, 0.2, 0.25, 0.3) M using the auto combustion method (sol-gel), and citric acid was used as fuel for auto combustion. The ferrite samples were checked by X-ray diffraction (XRD), Field Emission Scanning Electron Microscopes (FE-SEM), and energy dispersive X-ray analyzer (EDX). They showed that the prepared compound has a face-centered cubic structure (FCC). The lattice constant increases with an increase in the percentage of doping of the copper ions, and a decrease for the aluminum ion and that the compound is porous and its grains are spherical, and there are no other
... Show MoreThe wear behavior of alumina particulate reinforced A332 aluminium alloy composites produced by a stir casting process technique were investigated. A pin-on-disc type apparatus was employed for determining the sliding wear rate in composite samples at different grain size (1 µm, 12µm, 50 nm) and different weight percentage (0.05-0.1-0.5-1) wt% of alumina respectively. Mechanical properties characterization which strongly depends on microstructure properties of reinforcement revealed that the presence of ( nano , micro) alumina particulates lead to simultaneous increase in hardness, ultimate tensile stress (UTS), wear resistances. The results revealed that UTS, Hardness, Wear resistances increases with the increase in the percentage of
... Show MoreThe aim of this study was extraction of jojoba oil using different solvents. A mixture of waterhexane and water-ethanol are used as solvents to extract jojoba oil in a batch extraction process and compared with a pure solvent extraction process. The effects of particle size of crushed seeds, solvent-to-water ratio and time on jojoba oil extraction were investigated. The best recovery of oil was obtained at the boiling temperature of the solvent and four hour of extraction time. When seed particle size was 0.45 mm and a pure ethanol was used (45% yield of oil extraction), whereas, it was 40% yield of oil at 25% water-hexane mixture. It was revealed that the water-ethanol and water-hexane mixtures have an effect on the oil extraction yield. T
... Show MoreCassava, a significant crop in Africa, Asia, and South America, is a staple food for millions. However, classifying cassava species using conventional color, texture, and shape features is inefficient, as cassava leaves exhibit similarities across different types, including toxic and non-toxic varieties. This research aims to overcome the limitations of traditional classification methods by employing deep learning techniques with pre-trained AlexNet as the feature extractor to accurately classify four types of cassava: Gajah, Manggu, Kapok, and Beracun. The dataset was collected from local farms in Lamongan Indonesia. To collect images with agricultural research experts, the dataset consists of 1,400 images, and each type of cassava has