In the present work, polymeric composites were prepared for coating floors and swimming pools in dark colors. This was achieved through the use of a polymer coating solution added to fine cement with weight percentage (wt%) values of 5, 10, 15, 20, and 25 to obtain dark-colored (gray) composites. Mortar samples were prepared using the adhesion test. The contact angle and adhesion strength were studied for the prepared samples concerning the effect of changing the weight ratio of additive cement on water absorption. Also, the antibacterial activity was tested for the prepared coatings. The results showed that the contact angle increases with increasing the weight ratios of additive cement, which indicates that the

Polyaniline Multi wall Carbon nanotube (PANI/MWCNTs) nanocomposite thin films have been prepared by Plasma jet polymerization at low frequency on glass substrate with preliminary deposited aluminum electrodes to form Al/PANI-MWCNT/Al surface-type capacitive humidity sensors, the gap between the electrodes about 50 μm and the MWCNTs weight concentration varied between 0, 1, 2, 3, 4%. The diameter of the MWCNTs was in the range of 8-15 nm and the length 10-55 μm. The capacitance-humidity relationships of the sensors were investigated at humidity levels from 35 to 90% RH. The electrical properties showed that the capacity increased with increasing relative humidity, and that the sensitivity of the sensor increases with the increase of the

In the present study, the structural properties which included the X-rays diffraction, and DSC, the mechanical properties, which include tensile test, threepoint bending test (Bending Test), hardness test and thermal conductivity of the polymers reinforced with calcite (PVC/CaCO3) at different temperature (25-40-80-
120-160-200-220) °C. The research results showed that the XC degree of X-ray diffraction decreased at high temperatures (220 ˚C), while the inter-polymerized polymer (PVC / CaCO3) increased at high temperatures. The DSC test results showed that the degree of crystallinity (XC) decreases at high temperatures (220 ˚C). The mechanical test results, their values were found to decrease at (

   This study aimed to synthesize a novel amide prodrug of metformin with aspirin by amide bond. The structure was characterized by (FTIR, 1H-NMR, 13C-NMR and CHNO) ,Purification of the prepared compound was using column chromatography.          Using of 40 rabbit having the same weight and devided into 4 groups (4x10) the first group (G1): (the control healthy group) was given drink water and didn’t give any material, second group(G2):( the control infected group) was given hydrogen peroxide concentration  % 0.5 until infecting diabetes  mellitus,  third group(G3): was given hydrogen peroxide concentration as in (G2) and ( 250 mg/kg) of aspirin and (348.8 mg/kg

Background: Dental erosion is a common oral condition which results due to consumption of high caloric and low pH acidic food such as carbonated drinks and fruit juices. It is expected that these food types can cause irreversible damage to dental hard tissues and early deterioration of the dental restorations. So, this study aimed to evaluate and compare the erosive potential effects of orange fruit juice and Miranda orange drink on the microhardness of an orthodontic composite material. Materials and methods: Thirty discs with a thickness of 2 mm and a diameter of 10 mm were prepared from orthodontic bonding composite. The prepared discs were equally divided into three groups (n=10). Microhardness analysis was carried out both prior to

The objective of this research is to study the possibility of reducing the reflectivity of the front surface of a silicon cell (Si / Si) by using a theoretical design for a single-layer Antireflection Coatings with a thickness of one quarter of the design wavelength. Then, Mathematical programs in MATLAB (10) were designed to study the quantitative efficiency of the cell as a function of the change in the particle size of the coating within the range (400 - 700 nm) wavelength of the visible state of the vertical and oblique state at the (45°) angle. (Ge) was used as an anti-reflective material. It was found that the highest quantitative efficiency was (96.9004%) at design wavelength (λ0= 550 nm)

   The present research was conducted to synthesis Y-Zeolite by sol-gel technique using MWCNT (multiwalled carbon nanotubes) as crystallization medium to get a narrow range of particle size distribution with small average size compared with ordinary methods. The phase pattern, chemical structure, particle size, and surface area were detected by XRD, FTIR, BET and AFM, respectively. Results shown that the average size of Zeolite with and without using MWCNT were (92.39) nm and (55.17) nm respectively .Particle size range reduced from (150-55) nm to (130-30) nm. The surface area enhanced to be (558) m²/g with slightly large pore volume (0.231) km³/g was obtained. Meanwhile, degree of crystallization decrease

Spin coating technique has been applied in this work to prepared Xerogel films doped with Rhodamine 6G laser dyes. The solid host of laser dye modifies its spectroscopic properties with respect to liquid host. During the spin coating process the dye molecules suffer from changing their environment. The effects of three parameters were studied here: the spinning speed, multilayer coating and formaldehyde addition

The paper presents an investigation to the flutter speed of composite wing for different ply orientation. Structurally the composite wing was idealized as a composite beam load carrying structure. Theodorsen’s expression was used to get the 2- dimension unsteady lifting force and pitching moment in the limit of incompressible flow and subsonic speed which were integrated over the wing span. A free vibration analysis was first carried out to get the natural frequencies and mode shapes .The velocity-damping (V-g) method was used to calculate the flutter speed and the flutter frequency. A wing of unmanned aerial vehicle was manufactured from woven glass and polyester resin where the flutter speed was calculated experimentally by the wind