Polymer composites were prepared using epoxy resin (EP) and unsaturated polyester (UPE) as a blend matrices, which were mixed together in different percentages (starting from 90:10) of (epoxy/polyester) respectively, and ending with (50:50) of (epoxy/polyester). The optimum mixing ratio (OMR) of the components was decided upon the results of the impact strength value of these blending ratio, which showed the highest value of (16.3) KJ/m2 for the blending ratio (80:20) of (EP/UPE) respectively.
The blend with (OMR) was chosen to be reinforced with three different weight fractions of reinforcement; the 1st one was reinforced with nano titanium oxide (TiO2) with a weight fraction (2% wt.), the 2nd one was reinforced with both nano (TiO2) and surface modified nano silica particles (SiO2) with weight fractions (2% & 0.5%) respectively, and the 3rd one was reinforced with nano (TiO2) and surface modified (SiO2) with weight fractions (2% & 1%) respectively. The tested mechanical properties were (flexural strength, impact strength, hardness, and water uptake).
Hand lay-up technique was used to prepare the samples, and a magnetic stirrer was used to ensure maximum homogeneity of the nano particles in the blend. All fabricated samples were exposed to water for 10 weeks to investigate the effect of nano powders addition on diffusivity and maximum water uptake, obvious degradation in mechanical properties of the composite consisting of (blend matrix/TiO2 reinforcement) and (blend matrix/TiO2+SiO2 reinforcement) were observed as a result of liquid uptake with less severe impact, but more effect on flexural strength and shore D hardness. Fick’s 2nd law was used to explain diffusion mechanism. All the results were discussed.
The research Reviews the sides of highlight importance of the Nano-Accounting which doing the accounting performance functions fully computerized without the intervention of an accountant, to solve the problem of not keeping up the rationalization of recording and accounting systems, with the rationalization of production which fully computerized.(be invisible and hidden accounting), resulting by linking or interaction of the accounting, additive production system represented three-dimensional printers, open source and recycling. That which result the rationalizing the facilities of production, organization and self-control which derived nanotechnology idea, which aims to minimize materials and change it properties, then view the a
... Show MoreBack ground: This in vitro study was carried out to investigate the effect of post space regions (coronal, middle and apical), Time and the mode of polymerization (dual, self-cured) of the cements used on the bond strength between translucent fiber post and root dentin by using push-out test. Materials and Methods: Forty eight extracted mandibular first premolars (single root) were instrumented with ProTaper Universal system files (for hand use) and obturated with gutta percha for ProTaper and AH26® root canal sealer following the manufacturer instructions, after 24 hours post space was prepared using FRC postec® plus drills no.3 creating 8 mm depth post space. The prepared samples were randomly divided into two main groups (24 samples ea
... Show MoreTwo different composite materials were prepared by stir casting method of AA 6061 alloy as a matrix reinforced with two addition different ceramic materials Al2O3 and B4C of grain size 20 µm by 2.5, 5, 7.5 and10% in weight. The composite material with aluminum alloy as a matrix possesses a unique mechanical properties such as: high specific strength and hardness, low density, and high resistance to corrosion and friction wear. This composite is widely used in automotive parts space and marine applications.
Pin-on-disc technique was used to calculate the wear rate for each addition of Al2O3 and B4C particles. Rockwell hardness test and
... Show More
Epoxy resins were modified by some thermosetting materials using unsaturated polyesters which were cured with styrene , MMA ,and MA . When unsaturated Polyester ( as thermosetting material ) was used , and cured with styrene showed better results than acrylic monomers . Thermal stability rised on modification of epoxy resins with unsaturated polyester . The new formulation had converted the epoxy resin from hard brittle material to hard and tough material .
Thermal analysis were studied using ( DSC ) and physicomechanical characteristics were measured .
This paper presents an experimental and numerical study which was carried out to examine the influence of the size and the layout of the web openings on the load carrying capacity and the serviceability of reinforced concrete deep beams. Five full-scale simply supported reinforced concrete deep beams with two large web openings created in shear regions were tested up to failure. The shear span to overall depth ratio was (1.1). Square openings were located symmetrically relative to the midspan section either at the midpoint or at the interior boundaries of the shear span. Two different side dimensions for the square openings were considered, mainly, (200) mm and (230) mm. The strength results proved that the shear capacity of the dee
... Show More
(9)
This paper presents an experimental and numerical study which was carried out to examine the influence of the size and the layout of the web openings on the load carrying capacity and the serviceability of reinforced concrete deep beams. Five full-scale simply supported reinforced concrete deep beams with two large web openings created in shear regions were tested up to failure. The shear span to overall depth ratio was (1.1). Square openings were located symmetrically relative to the midspan section either at the midpoint or at the interior boundaries of the shear span. Two different side dimensions for the square openings were considered, mainly, (200) mm and (230) mm. The strength results proved that the shear capacity of the dee
... Show More
(12)
(9)
This study investigated the applicability of iron oxide (Fe2O3) nanoparticles for the removal of cadmium metal from sewage water by using batch scale experiments. The iron oxide nanoparticles of 27.7nm were synthesized using a biological method and characterized by Atomic Force Microscope (AFM). The Box-Wilson design was used to conduct experiments with three parameters such as pH (2-6), time of adsorption (6-120min) and adsorbent dosage (5-25mg/L). The best conditions occurred at pH: 5.5; contact time: 95.8 min; and iron oxide nanoparticle dosage: 20.77 mg/L for maximum cadmium removal of (96.9%).
This study was performed by using the unsaturated polyester resin as matrix to the
composite materials with the rice husk as reinforced materials . The research included study
of wear test on the composite material The results show that the, wear is increased with the
increase of applied load and distance slipping and also with time increase . moreover the
shows that the higher value wear rate( 1.91gm/cm) from the load (20) N and the higher value
wear rate (1.43gm/cm) from the higher distance (4cm) and from the higher time (6min) higher
wear rate (5.33gm/cm).