Polymer composites were prepared using epoxy resin (EP) and unsaturated polyester (UPE) as a blend matrices, which were mixed together in different percentages (starting from 90:10) of (epoxy/polyester) respectively, and ending with (50:50) of (epoxy/polyester). The optimum mixing ratio (OMR) of the components was decided upon the results of the impact strength value of these blending ratio, which showed the highest value of (16.3) KJ/m2 for the blending ratio (80:20) of (EP/UPE) respectively.
The blend with (OMR) was chosen to be reinforced with three different weight fractions of reinforcement; the 1st one was reinforced with nano titanium oxide (TiO2) with a weight fraction (2% wt.), the 2nd one was reinforced with both nano (TiO2) and surface modified nano silica particles (SiO2) with weight fractions (2% & 0.5%) respectively, and the 3rd one was reinforced with nano (TiO2) and surface modified (SiO2) with weight fractions (2% & 1%) respectively. The tested mechanical properties were (flexural strength, impact strength, hardness, and water uptake).
Hand lay-up technique was used to prepare the samples, and a magnetic stirrer was used to ensure maximum homogeneity of the nano particles in the blend. All fabricated samples were exposed to water for 10 weeks to investigate the effect of nano powders addition on diffusivity and maximum water uptake, obvious degradation in mechanical properties of the composite consisting of (blend matrix/TiO2 reinforcement) and (blend matrix/TiO2+SiO2 reinforcement) were observed as a result of liquid uptake with less severe impact, but more effect on flexural strength and shore D hardness. Fick’s 2nd law was used to explain diffusion mechanism. All the results were discussed.
The transfer of chemical pollutants from bottled water into water due to heat, sunlight and poor storage is one of the most serious threats to human health around the world, the objective of this study was to estimate the pH value and the transport of heavy metals from plastic bottles to water, for this purpose, 30 bottles of water for 10 local brands were collected and divided into three groups, the first was left at room temperature 25°C, The second was placed in a heat oven at 25°C and the third in another oven at 50°C for two weeks. The results showed significant differences at (P<0.05) between water samples, pH value and concentrations of heavy metals (Sb, Pb, Ni, Cu, Cr, Cd and Fe) we
... Show MoreWe have studied the synthesis environment of ambient pressure silica aerogels influence on their resulting morphological and optical properties. Transparent nanoporous silica aerogel was synthesized at ambient pressure using tetraethylorthosilicate precursor via a sol-gel process. Effect of drying control chemical additives and catalyst on physical properties was investigated. Trimethylchlorolsilane was employed as a hydrophobic reagent in the surface modification process. All aerogel samples were prepared utilizing a subcritical procedure under reactant pH fixed at 8.3, using just ammonium hydroxide or together with ammonium fluoride as catalyst. The effects catalyst types as well as drying control chemical additives on the physical pro
... Show More
(4)
(3)
Background: The polymethyl methacrylate is the most reliable material for the construction of complete and partial dentures, despite satisfying esthetic demand itsuffered from having unsatisfactory properties like impact strength and transverse strength. This study was designed to improve the impact strength and transverse strength of heat cure acrylic resin by adding untreated and oxygen plasma treated polypropylene fibers and investigate the effect of this additive on some properties of acrylic resin materials. Materials and methods: Untreated and oxygen plasma treated polypropylene fibers was added to PMMA powder by weight 2.5 %. Specimens were constructed and divided into 5 groups according to the using tests; each group was subdivided
... Show MoreCr2O3 thin films have been prepared by spray pyrolysis on a glass substrate. Absorbance and transmittance spectra were recorded in the wavelength range (300-900) nm before and after annealing. The effects of annealing temperature on absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of dielectric constant and optical conductivity were expected. It was found that all these parameters increase as the annealing temperature increased to 550°C.
(1)
This experiment was conducted in the orchard of the Department of Horticulture,college of Agriculture,Baghdad University during the growing season of 2007 To study the effects of spray with three concentration of cultar(0,500,1000 mg.L-1) ,tow concentration of K2SO4(0,5g.L-1), and salinity of irrigation water with three concentration (1,2,3dS.m-1) on some characteristics of vegetative growth of two cultivars of apricot trees (Labib1 and Zienni).The age of trees was four years .The tree grafted on original of seed apricot . Afactorial trail was carry out according to randomized complete block design with arrangement of split-split with three replications. Salinity of irrigation water took main plot, potassium took sub plot and cultar took s
... Show More
In this research we investigated the corrosion behavior of the commertialy pure titanium and Ti-6Al-4V alloy that coated with hydroxyapatite by electrochemical deposition with applied voltage (6,9,12) Volt from aqueous solution containing Ca(NO3)2.H2O =7.0 gm/l , (NH4)2HPO4 =3.5 gm/l , Na(NO3)2 = 8.5 gm/l in order to improve the bonding strength of hydroxyapetite and medical metals and alloys and increasing the biocompatibility. The coating layer morphology was investigated by XRD, Optical microscope , and SEM tests, the corrosio tests was made by use senthesys simulated body fluid (SBF) , and we found that the propreate voltage for coatint on Ti was 9 Volt and for Ti-6Al-4Vwas12Volt.