Background: One of the major problems in endodontics is micro-leakage of root canal fillings which might contribute to the failure of endodontic treatment. To avoid this problem, a variety of sealers have been tested. The objective of this, in vitro, study was to evaluate the shear bond strength of four resin based sealers (AH plus, silver free AH26, RealSeal SE and Perma Evolution permanent root canal filling material) to dentin. Materials and Methods: Forty non-carious extracted lower premolars were used. The 2mm of the occlusal surfaces of teeth were sectioned, to expose the dentin surface. The exposed dentin surfaces of teeth were washed with 5ml of 2.5% NaOCl solution followed by 5ml of 17 % EDTA then rinsed by deionized water to remov

With the advent of the globalization, the rapid development in technology and the intensity of competition companies attemptto maintain competition advantages and retain customers. The traditional methods in managerial accounting become irrelevance to achieve the objectives of these companies especially with the rapid changes in modern manufacturing environment .Thus there is a need to new tools in accounting such as lean accounting, which is considered as a costing method that support creating value for the customer by costing the entire value stream, eliminating waste in the accounting process, reduced lead time, improved quality, lowered time delivery and increased available capacity. Using value stream focuses not only on the waste&n

A new mode of methodology was adopted in the assay of PM- HCL based on the use of water crystal gel bead made of poly acrylic acid in which the gel beads were left to absorbe persulphate solution that is necessary for the oxidation of PM- HCL in aqua media . The water crystal act as a reserviour for S2O82- . Optimum parameters were studied giving to specify the chemical and physical parameters. Two line manifold was used .The flow rates of 1.5 and 1.2 ml.min-1 was used , 3 gel beads , 120 μL sample volume , a linear dynamic range extend from 0.01- 18 mmol.L-1. A correlation coefficient (r) of 0.9991while the percentage linearity (r2%) of 99.82% with R.S.D% at 8 mmol.L-1 promethazine-HCl is less than 0.5% (ten replicates) and a detection

Portland Cement is manufactured by adding 3% gypsum to clinker which is produced by grinding, pulverizing, mixing, and then burning a raw mix of silica, and calcium carbonate. Limestone is the main source of carbonates, while clay collected from arable land is the main source of silica. The marl in the Euphrates Formation was studied as an alternative to arable lands. Nine boreholes drilled and penetrated the marl layer in selected locations at the Kufa cement quarry. Forty-one samples of marl from boreholes and four samples of limestone from the closed area were collected. The chemical content of the major oxides and the hardness of the marl layer was very encouraging as a raw material for Portland Cement as they are SiO2 (17.60),

From a large number of bacterial samples collected from different hospital in Iraq in central  health laboratory ,only ten isolates were identified primary as Vibrio. A number of  morphology and biochemical test were carried out to complete this identification that showed all bacterial isolates were related to Vibrio cholerae .In this study  all Vibrio isolates were investigated for Bio typing and the result showed that all (10) isolate were related to (Eltor biotypes) .Also, the susceptibility test towards eight antibiotics were carried  out .

Results shows that  ciprofloxacin , Norfloxacin, Erythromycin, Ampicillin,  ceftriaxone  and Amikacin were the most effective

The main factors that make it possible to get the corrosion of reinforcing steel in concrete are chloride ions and the absorption of carbon dioxide from the environment, and each of them works with a mechanism which destroys the stable immunity of rebar in the concrete. In this work the effect of carbon dioxide content in the artificial concrete solution on the corrosion behavior of carbon steel reinforcing bar (CSRB) was studied, potentiostatically using CO₂ stream gas at 6 level of concentrations;  0.03 to 2.0  weight percent, and the effect of rising electrolyte temperature was also followed  in the range 20 to 50^ᴼ C. Tafel plots and cyclic polarization procedures were obeyed to investigate the c

Taguchi experimental design (TED) is applied to find the optimum effectiveness of aqueous Red Pomegranate Peel (RPP) extract as a green inhibitor for the corrosion of mild steel in 2M H₃PO₄ solution. The Taguchi methodology has been used to study the effects of changing, temperature, RPP concentration and contact period, at three levels. Weight-loss measurements were designed by construction a L₉ orthogonal arrangement of experiments.   Results of the efficiencies of inhibition were embraced for the signal to noise proportion & investigation of variance (ANOVA).  The results were further processed with a MINITAB-17 software package to find the optimal condition

The impact of a Schiff base namely 2-((thiophen-2-ylmethylene)amino)benzenethiol  to corrode mild steel in 1 M HCl  resolved was evaluated using different weight loss technique and scanning electron microscopy (SEM).different weight measurements to expand that the 2-((thiophen-2-ylmethylene) amino) benzenethiol  inhibits  the corrosion of mild steel through adsorbing  of  top for mild steel and block the active locality. The inhibitive impacts of 2-((thiophen-2-ylmethylene)amino)benzenethiol  increase with increasing concentration and decrease with increasing temperature. SEM to checking revealed that the alloy surface was quite unaffected and formed protective film on its surface. The investigated

The galvanic corrosion of the (Cu - Fe), (Cu - Zn) and (Fe - Zn) couples have been investigated in 3.5% NaCl solution, 40ºC, different velocities (Re = 5000, 10000 and 15000) and different area ratio’s of cathode to anode (AR= 0.5,1 and 2), by using commercial metal pipe (cylindrical tube).The Zero Resistance Ammeter has been used to measure the galvanic current (Ig) and galvanic potential (Eg) with time. The galvanic current density increases with increasing velocity (Re) and the area ratio (AR). The galvanic potential (Eg) is shifted to less negative with increasing velocity (Re) and the area ratio (AR). A statistical relations for the galvanic current density and galvanic potential as a function of (Re). and the area ratio had been