A reseach is carried out by using Alumina material type α-Al2O3 which has partical size 63μm doped with different percentage weight of MgO (0.1%,0.3%and0.5%) and by using dry press method to prepare the samples ,A force press 50KN used and sintering to 1500oC with   soaking time  of  6 hours.        The physical properties were studied such as "Bulk density ,Porosity and water absorption "also the mechanical properties such as (hardness,compressive strength ), the result shows that the best ratio of maginsa(MgO) added to Alumina (Al2O3)is 0.5%and this  worked to improve   Physical and mechanical properties .

داء المشوكات الكيسي (CE) هو مرض وبائي يسبب مرضًا خطيرًا وخسائر اقتصادية في معظم بلدان العالم. MiRNAs هي عامل جيني ضروري لتنظيم الاستجابة المناعية من خلال قدرته على التدخل في التعبير الخلوي ؛ واحد هذه الحوامض النووية الدقيقة -146 أ. هدفت الدراسة الحالية تقييم إذا كان بإمكاننا استخدام microRNA 146a كمؤشر حيوي للكشف عن    CEو تحديد العلاقة بين التعبير الجيني microRNA 146a و IL-17 في مرضى CE.حيث اشتملت الدراسة على 50 مريضًا من CE تم إد

    A theoretical calculation of the reorganization energies is demonstrated for semiconductor (TiOâ‚‚, ZnO) and organic dye (safranine T, and coumarin) with a variety solvent such that (water,  1­propanol, Formamide, Acetonitrile and Ethanol).     The reorganization energy values for dye –semiconductor interface system are large in high polar solvent (water 741 .0  , Acetonitrile 708 .0  , Ethanol 669 .0  ) and small in low polar solvent(1­propanol 635 .0  . The reorganization energy in safranine T –semiconductor system is larger ( 635 741.0  )than in coumarin –semiconductor for with the same solvents ( 612

Theoretical calculations are achieved to study the effect of different deuterium pressures on various characteristics parameters for PF400J plasma focus using an international computer code.  Axial and radial velocities, voltage tube, plasma temperatures, and neutron yields at different operating deuterium pressures are computed. Neutron emission has been calculated in the device.  The maximum total neutron yield calculated is of the order of  and  neutrons per shot for entire pressure used. The computed results agree reasonably well with the published neutron yield curves.

   The modified Hummers method was applied to prepare graphene oxide (GO) from the graphite powder. Tin oxide nanoparticles with different loading (10-20 wt.%) supported on reduced graphene oxide were synthesized to evaluate the oxidative desulfurization efficiency. The catalyst was synthesized by the incipient wetness impregnation (IWI) technique. Different analysis methods like FT-IR, XRD, FESEM, AFM, and Brunauer-Emmett-Teller (BET) were utilized to characterize graphene oxide and catalysts. The XRD analysis showed that the average crystal size of graphene oxide was 6.05 nm. In addition, the FESEM results showed high metal oxide dispersions on the rGO. The EDX analysis shows the weight ratio of Sn is close to its theoretical weight.

Abstract

    Binary polymer blend was prepared by mechanical mixing method of unsaturated polyester resin with Nitrile Butadiene Rubber (NBR) with different weight ratios (0, 5, 10 and 15) % of (NBR). Tensile characteristics and wear rates of these blends were studied for all mixing ratios. The microstructure of fracture surfaces of the prepared samples were investigated by optical microscope. The results were showed that strain rates of the resin material increase after blending it with rubber while the ultimate tensile strength and Young’s modulus values of it will decrease. It is also noticed that the wear rate of resin decreases with increasing of (NBR) content.

Keywords:<

Four antimony compounds were used in this inves as additives to retard combustion of unsaturated polyester and epoxy resins, namely: 1. Tetraethyl ammonium tribromoethylantimonates (additive I). 2. Tetraethyl ammonium chlorodibromoethylantimonates (additive II). 3. Tetraethyl ammonium trichloroethylantimonates (additive III). 4. Tetraethyl ammonium bromodichloroethylantimonates (additive IV). The effects of these additives on flammability of unsaturated polyester and epoxy resins have been studied by using sheets of the resins with weight percentages of (0.5,1.0,1.5,2.0,2.5&3.0%) of the additives in dimensions of (150 X150X3)mm .Three standard test methods were used to measure the flame retardation which are: (ASTM:D -2863), (ASTM:D-635

The current study, which extended from February 2020 to June 2021 at the University of Thi- Qar\ College of Education for Pure Sciences, aimed to follow the changes in external morphological features at different Embryonic Developmental stages in pregnant mice treated with different doses of Rapamycin (Rapa). Use In this study, 32 pregnant mice were divided randomly into four groups, each of which had eight pregnant mice. Each group received different dose of Rapa via intraperitoneally injection at different gestation days until the end of the specified periods, whereas the control group received a DMSO. Mice were administered under the same circumstances and dosages were determined based on body weight, as specified in pharmaceutical const