In the present study, gold nanoparticles (AuNPs) were prepared using a simple low cost method synthesized cold plasma at different exposure time . The nanoparticles were characterized using UV-Visible spectra, X-ray diffraction (XRD). The prepared AuNPs showed surface Plasmon resonance centered at 530, 540,and 533 nm. The XRD pattern showed that the strong intense peaks indicate crystalline nature and face centered cubic structure of gold nanoparticles for all samples were prepared .The average crystallite size of the AuNPs was 20-40 nm. Morphology of the AuNPs were carried out using FESEM. Observations show that the AuNPs synthesized we well dispersed with and particle sizes ranging from 9 to 31 nm with spherical shapes which are cle

Alloys of InxSe1-x were prepared by quenching technique with
different In content (x=10, 20, 30, and 40). Thin films of these alloys
were prepared using thermal evaporation technique under vacuum of
10-5 mbar on glass, at room temperature R.T with different
thicknesses (t=300, 500 and 700 nm). The X–ray diffraction
measurement for bulk InxSe1-x showed that all alloys have
polycrystalline structures and the peaks for x=10 identical with Se,
while for x=20, 30 and 40 were identical with the Se and InSe
standard peaks. The diffraction patterns of InxSe1-x thin film show
that with low In content (x=10, and 20) samples have semi
crystalline structure, The increase of indium content to x=30
decreases degree o

The largest use of x-ray in medical by dentists, employers or persons that needed by patients with specific conditions, lead to higher exposure of x-ray that may cause many diseases. In the present work radiography films have been used in evaluating the efficiency of using unsaturated polyester polymer reinforced with lead oxide (PbO) as shield material for medical x-ray devices, many parameters studied like concentration and thickness that they are increasing the attenuation of x-ray in them. The results show that the attenuation of X-ray increasing with concentration of reinforced material and with thickness, and the optical density decreases with increasing concentration from 0% to 50%, we chose 30% as suitable concentration to increase

Cadmium oxide (CdO) thin films were deposited using the sequencing ion layer adsorption and reaction (SILAR) method. In this study, the effect of the pH value of an aqueous solution of cadmium acetate at a concentration of 0.2 mol of the cadmium oxide film was determined. The solution source for the cadmium oxide film was cadmium ions and an aqueous ammonia solution. The CdO films were deposited on glass substrates at a temperature of 90 ℃. The cadmium oxide film thickness was determined by the weight difference method at pH values ​​(7.2, 8.2). X-ray diffraction (XRD) and scanning electron microscopy (SEM) showed that the size of the crystals increased with the increase in the solution (pH). While the UV-visible spectra of the fil

Background: Bone mineral density (BMD) has been assessed using Dual-Energy X-ray absorptiometry (DEXA). This procedure is considered to be of vital importance in assessing the general condition of individuals concerning their skeletal mineralization. BMD is measured according to the results of the DEXA examination of the vertebral column and pelvis. Although diabetes mellitus (D.M.)is known to affect BMD, the information regarding this relationship is not currently particularly clear. Objective: This study concentrates on the point that the assessment of BMD for the vertebral column is insuffi-cient to give a realistic and correct picture of the mineralization of the remaining part of the skeleton. Besides, this study elicited a gen

     Bacillus subtilis, an isolate of bacillus genus, was obtained from the laboratories of Ministry of Science and Technology. The best efficient Bacillus subtilis isolate in cellulose and semi-cellulose hydrolysis was treated with Dielectric-barrier Discharge (DBD). Atmospheric cold plasma technique (non-thermal) was used by exposing them at different times (2, 3, 4 and 5 mins) separately as a first stage, and then 60 seconds after any treatment separately as a second stage. After 48 hours, the difference between the plasma source and the sample was fixed at 0.5 cm. The results showed a variation in the growth of the isolate according to the exposure time by the appearance of culture turbidity and the estimation o

In the present work, the effect of isolated dust particles (FeO) with radius of the grain 0.1μm - 0.5μm of main plasma characteristics are investigated experimentally in direct current system by using magnetic field. The present of dust particle in the air plasma did effect on Paschen minimum and on the plasma properties in low pressure region. The effect of dust particles on discharge voltage, discharge current, plasma potential, floating potential, electron density, electron temperature and Debye length was investigation by using magnetic field. The measurements of parameters are taken by four cylindrical Langmuir probes. The results show the present of dust causes decreasing in discharge voltage with increase pressure while the disc

This study illustrates effect of cold plasma CAP on the mineral blood components in vivo. the mineral blood component (Ca, Na, Cl, K and Fe) are used. Floating Electrode-Dielectric Barrier Discharge (FE-DBD) system of probe diameter 4cm is used for this purpose, and variable voltage (0-20) kV and variable frequency (0-30) kHz, the output power was ranged from (10 - 70) W. the effect of cold atmospheric plasma on mineral blood is studied with different exposure durations (30,45,60) sec. As the plasma exposure duration increases, the calcium, potassium and iron components in the blood increased, while The sodium and chlorine elements decreased. These results give an indication of the cold plasma receptor to be used to treat many disea

Background: Bone mineral density has been assessed using Dual-Energy X-Ray Absorptiometry. Bone mineral density is measured according to the results of the Dual-Energy X-Ray Absorptiometry examination of the vertebral column and pelvis. Although diabetes mellitus type II (DM) is known to affect bone mineral density, at the present time this particular relationship is not clear. Objective: The aim of current study was to evaluate the effects of type II diabetes mellitus on bone mineral density of the upper and lower limbs as well as gender differences. Patients and Methods: This study involved 165 patients complaining of bone pain (85 males and 80 females), 85 patients of who suffered from diabetes, involving both genders. In addition,