The present work aimed to synthesize new phenol resins via incorporation of structural modification through introducing new phenolic compounds containing cyclic imide moiety in reaction with formaldehyde. The synthesis of these new resins involved three steps. First, one of the three N-(hydroxyphenyl)tetrabromophtalamic acids 1-3 were processed via a reaction between tetrabromophthalic anhydride and aminophenols. Amic acids 1-3 were dehydrated in the second step by smelting, producing the identical N-(hydroxyphenyl)tetrabromophthalimides 4-6. The new imides represent the new phenolic component

2-Amino-5-aryl- 1,3-thiazole-4-carboxylic acid (A1-A3) were synthesized from the reaction of various aromatic aldehyde with dichloro acetic acid and thiourea. The synthesis of 2-[[(Saminosulfinim-idoyl)(aryl)methyl](benzoyl)amino]-5-aryl-1,3-thiazole-4-carboxylic acid (A22-A30) was perfomed starting from (A1-A3) by two steps using Schiff's base (A4-A12) prepared  from the reactant compounds (A1-A3) with different aromatic aldehyde. Finally two types of imide derivatives were obtained from reactant compounds (A1-A3) with malic anhydride (A31-A33) and phthalic anhydride (A34-A36) in the presence of glacial acetic acid. All proposed structures were supported by FT-IR and UV-Visible spectroscopic data.  
 

Activated carbon loading with metals oxides is new adsorbents and catalyst, which seem very promising for desulfurization process. The present study deals with the preparation of three metals oxides loaded on activated carbon (AC). The tri composite of ZnO/NiO/CoO/AC was characterized by X-Ray Diffraction (XRD), X-Ray florescence (XRF), N₂ adsorption for BET surface area, pore volume and Atomic Force Microscopy (AFM). The effect of calcination temperature is investigated. The best calcination temperature is 250^oC based on the presence of phase, low weight loss and keep at high surface area. The surface area and pore volume of prepared tri composite are 932.97m²/g and 0.6031cm³/g respec

In this paper a new series of morpholine derivatives was prepared by reacting the morpholine with ethyl chloro acetate in the presence triethylamine as a catalyst in benzene gave morpholin-N-ethyl acetate(1) which reacted with hydrazine hydrate in ethanol, and gave morpholin-N-ethyl acetohydrazide (2) . Morpholin-N-aceto semithiocarbazide (3) were prepared by reacting compound(2) with ammonium thiocyanate , concentrated hydrochloric acid and ethanol as a solvent .Compound (3) reacted with sodium hydroxide and hydrochloric acid to give 5-(morpholin-N-methylene)-1H-1,2,4-triazole-3-thiol (4) .The new series of 1,2,4-triazol derivatives (5-8) was synthesized by reaction of compound(4) with formaldehyde , DMF as a solvent and different

  In this study, Schiff's bases [S3,S4] were synthezied by condensation of N,N-dimethyl amino benzaldehyde with primary aromatic amine[N-(hydrazinyl methyl)benzamide]. These Sciff's bases were found to react with maleic anhydride and phthalic anhydride to give 1,3Oxazepine[S5,S6,S7,S8] in good yields.            The structures confired by m.p ,T.L.C.,FT.IR and 1H-NMR (of some of them).

A cermet (ceramic-metal) composite have been prepared from alumina (γ-Al2O3) reinforced with aluminum (Al) for the concentrations of (0, 10, 20, 30, 40, & 50) wt. %Al. The cermet was formed by single axial pressing, sintered in vacuum atmosphere. Compaction behaviors were studied in solid state sintering at sintering temperatures (400, 450, & 550) °C, sintering times (2, 4, & 6) hrs., and forming pressures (5, 10, 15) MPa, also in liquid phase sintering at (800 °C). The cermet was characterized by x-ray diffraction (XRD) and by scanning electron microscope (SEM), also physical and mechanical properties have been studied. SEM results showed the Al flowing inside the ceramic body due to uniform distribution of Al particles a

Well log analysis of selected sections in southern Iraq revealed that primary porosity is the most effective parameters. Secondary porosity seems to be related mainly to dissolution and dolomatization. The Hartha Formation has good water saturation and low production except in the eastern and central part of the study area. Two reservoir units were recognized in Mj-2 whereas only one in Ga-1.
The values of velocity deviation in most wells show high positive deviation, this may indicate relatively high velocity in regard to porosity where pores are commonly not connected such as in interaparticle or moldic porosity. A positive deviation also may indicate low permeability. Negative deviation zone (Only in Ak-1) may represent caving or i

     In this research, we prepared a polymer blend of polyvinylalcohol (PVA)/carrageenan/kaolinite by means of the solution cast approach. The composition of the blend was PVA in 1 gm by weight with 0.2 gm carrageenan as a plasticizer. The ratio of nanoclay varied between 1 and 5 wt%. Different properties were investigated in this study such as water vapor permeability, hardness, tear strength, color stability, thermal stability, and antibacterial activity. Water vapor permeability was decreased with increasing the ratio of nanoclay, while the values of hardness, tear strength, color stability, and thermal stability were increased. Also, the antibacterial activity examination with two types of bacteria, e.g.

The CIGS/CdS p-n junction thin films were fabricated and deposited at room temperature with rate of deposition 5, and 6 nm secG1 , on ITO glass substrates with 1mm thickness by thermal evaporation technique at high vacuum pressure 2×10G5 mbar, with area of 1 cm2 and Aluminum electrode as back contact. The thickness of absorber layer (CIGS) was 1 µm while the thickness of the window layer CdS film was 300 nm. The X-ray Diffraction results have shown that all thin films were polycrystalline with orientation of 112 and 211 for CIGS thin films and 111 for CdS films. The direct energy gaps for CIGS and CdS thin films were 1.85 and 2.4 eV, respectively. Atomic Force Microscopy measurement proves that both films CIGS and CdS films have nanostru