The Synthesis of yttrium oxide nanoparticles have been achieved via calcination
of yttrium hydroxide produced from the reaction of aqueous solutions of yttrium
nitrate and sodium hydroxide at pH = 13 using hydrothermal and hydrothermal
microwave methods. Effect of heat treatment of the resulted yttrium hydroxide
powder on the morphology and crystallinity of the resulting oxide was studied at
calcination 500, 700 and 1000°C to obtain. The resulted products were
characterized by means of X-ray diffraction (XRD), scanning electron microscope
(SEM), atomic force microscope (AFM), Fourier transform infrared spectrometer
(FTIR) and thermal analyses (TG).

Background: Dental implants act as infrastructure for fixed restoration to look like as a natural tooth. Osseointegration is a biological events and considered as a base for success of dental implant. The aim of this study is to evaluate the bond strength between bone and Ti implant coated with mixture of nano hydroxyapatite-chitosan-collagen compared with Ti implants coated with nano hydroxyapatite implanted in rabbit tibia, after different period of implantation time (two and six weeks) by torque removal test. Material and methods: 36 screws of commercially pure titanium; 8mm in length and 3mm diameter , 18 screws coated with mixture of nano hydroxyapatite-chitosan-collagen and18 screws coated with nano hydroxyapatite by dip coating. St

Nasiriyah oilfield is located in the southern part of Iraq. It represents one of the promising oilfields. Mishrif Formation is considered as the main oil-bearing carbonate reservoir in Nasiriyah oilfield, containing heavy oil (API 25^o(. The study aimed to calculate and model the petrophysical properties and build a three dimensional geological model for Mishrif Formation, thus estimating the oil reserve accurately and detecting the optimum locations for hydrocarbon production.

Fourteen vertical oil wells were adopted for constructing the structural and petrophysical models. The available well logs data, including density, neutron, sonic, gamma ray, self-potential, caliper and resistivity logs were used to calculate the

The aim of this article is to solve the Volterra-Fredholm integro-differential equations of fractional order numerically by using the shifted Jacobi polynomial collocation method. The Jacobi polynomial and collocation method properties are presented. This technique is used to convert the problem into the solution of linear algebraic equations. The fractional derivatives are considered in the Caputo sense. Numerical examples are given to show the accuracy and reliability of the proposed technique.

       The current research aims to build a training program for chemistry teachers based on the knowledge economy and its impact on the productive thinking of their students. To achieve the objectives of the research, the following hypothesis was formulated:

   There is no statistically significant difference at (0.05) level of significance between the average grades of the students participating in the training program according to the knowledge economy and the average grades of the students who did not participate in the training program in the test of productive thinking. The study sample consisted of (288) second intermediate grade students divided into (152) for the control group

 In this work, the ligand was obtained from the reaction of diazonium salt of naphthyl amine with 1-amino-2-naphtol-4-sulfonic acid. The bidentate ligand  type (NO) donar atoms was reacted with 1,10-phenanthroline and matel salt in a 1:1:1 mole ratio to give the complexes, using NaOH as a base. Physical-chemical teqnichas were used to characteriz the prepared compounds FT-IR,U.V-Vis, fluorescence and 1HNMR spectroscopy, atomic absorption , chloride content along with conductivity and melting point measurements .Finally, thermal analysis was used to confirm the presence of coordination H2O molecule in the complexes structure. According to memtioned characterization methods, the general formula proposed for CoII ZnII, CdII and Hg

A new Turbidimetric method characterized by simplicity, accuracy and speed for determination of Hydronium ion by continuous flow injection analysis. The method was based on the formation of complex Zn3[Fe(CN)6] for Zinc(II) that was eluted by Hydronium ion from cation exchanger column with Potassium hexacyanoferrate(III) for the formation of a pale yellow precipitate and this precipitate was determined using homemade Linear Array Ayah-5SX1-T-1D continuous flow injection analyser. The optimum parameters were 2.7 mL.min-1 flow rate using H2O as a carrier stream, 1.7 mL.min-1 reagent stream, 110 L sample volume and open valve for the purge of the sample segment. Data treatment shows that linear range 0.01-0.1 mol.L-1 for each acids (HClO

This study uses an environmentally friendly and low-cost synthesis method to manufacture zinc oxide nanoparticles (ZnO NPs) by using zinc sulfate. Eucalyptus leaf extract is an effective chelating and capping agent for synthesizing ZnO NPs. The structure, morphology, thermal behavior, chemical composition, and optical properties of ZnO nanoparticles were studied utilizing FT-IR, FE-SEM, EDAX, AFM, and Zeta potential analysis. The FE-SEM pictures confirmed that the ZnO NPs with a size range of (22-37) nm were crystalline and spherical. Two methods were used to prepare ZnO NPs. The first method involved calcining the resulting ZnO NPs, while the second method did not. The prepared ZnO NPs were used as adsorbents for removing acid black 210