The current experiment was conducted to explore the effect of soil crude oil ( crude oil ) pollution on some wood properties of   Casuarina equisetifolia.      Four levels of pollution were applied on 40 (one-year) old seedlings . Measurements were taken by cutting the trees after two growth seasons from date of pollution .The studied Properties were fiber length, diameter, wall thickness, and specific gravity of external and internal wood.  Results showed an adverse effect of pollution on fiber diameter more than on fiber length. While wall thickness did not affect.  Fiber dimensions of external wood showed higher values  than that of internal one, especially for fiber

   This study included preparation for the unsaturated polyester samples before and after reinforced by the Alumina oxide powder of different volume fraction amounting (2%,4%,6%).    And this research included the study of some of mechanical properties such as (Hardness,compressive,wear).     The results showed that the increase of the hardness and compressive strength after the reinforced and the increase with the volume fraction increase.   As the wear test shows that the wear rate increases with applied load increase(5,10,15) from  (10.6-18.6) gm/cm befor reninforced and from(5.4-15.2)gm/cm,(4.7-12.9)gm/cm,(48.1)gm/cm,after reinforced from the different volume fraction, and t

     In this study the as-deposited and heat treated at 423K of conductive blende graphene oxide (GO) / poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) thin films was prepared with different PEDOT:PSS concentration (0, 0.25, 0.5, 0.75 and 1.0)wt% on pre-cleaned glass substrate by spin coating technique. The energy dispersive X-ray Analysis (EDX) show the existence of higher amount of carbon and oxygen related to hydroxyl and carbonyl  groups. X-ray diffraction (XRD) analysis of the as-deposited and annealed GO/PEDOT:PSS thin films blend indicated that the film prepared  show broad peak around 8.24 corresponding to the (001) level refers to GO, this peak shifted to the lower 2θ with increasing PEDOT:PSS concentr

In this work, a composite material was prepared from Low-density polyethylene (LDPE) with different weight percent of grain and calcinations kaolin at temperature of (850^oC) using single screw extruder and a mixing machine operated at a temperature between (190-200^oC). Some of mechanical and physical properties such as tensile strength, tensile strength at break, Young modulus, and elongation at break, shore hardness and water absorption were determined at different weight fraction of filler (0, 2, 7, 10 and 15%). It was found that the addition of filler increases the modulus of elasticity, elongation at break, shore hardness and impact strength; on other hand, it decreases the tensile strength and tensile strength

     Group action on the projective space PG(3,q)  is a method which can be used to construct some geometric objects for example cap. We constructed new caps in PG(3,13)  of degrees 2, 3, 4, 7,14 and sizes 2, 4, 5, 7, 10, 14, 17, 20, 28, 34, 35, 68, 70, 85, 119, 140, 170, 238, 340, 476, 595, 1190. Then the incomplete caps are extended to complete caps. 

This work evaluated the effect of Alpha, Gamma  irradiation and Nd:YAG,  He-Ne laser on  Staphylococcus epidermidis and  Leishmania tropica  in vitro. The experiment included five replicate  of   S. epidermidis , L. tropica  in vitro exposed to effect of Alpha , Gamma  irradiation by ²⁴¹Am  isotopes , in two  doses

In this paper, we have provided a very thorough analysis of a new novel chelate metal ion complex of [Cu(II),Ag(I)] prepared via the interaction with the ligand{ 2-amino-8-((4-chloro-3-hydroxyphenyl) diazenyl)azo]guanine} [LAAG], which is synthesized by diazo coupling of the 5-amino-2-chlorophenol with amino acid guanine. The ligand and its complexes are identified by a variety of techniques, like [HNMR, FTIR, and Uv-vis] spectral, thermal analysis (TGA), and element analyses (CHN). The molar ratio was achieved so that the Cu(II) complex has (1:2) (M:L) with octahedral geometry; however, the Ag(I) complex has (1:1) (M:L) with tetrahedral geometry, and the ligand acts as neutral N,N-bidentate; as well as the ligand (LAAG) and its complexe