The objective of this work is to study the influence of α-amylase enzymatic solution immersion, soil burial and water immersion on the biodegradability behavior of polyvinyl alcohol (PVA) /Corn Starch (CS) blend films Polyvinyl alcohol (PVA) /Corn Starch (CS) blend films were prepared by solution casting method with different weight percentages of PVA(0%,10%,30%,50%,70% and 90%) . The biodegradability of the films has been investigated by determination the weight loss of the tested films. It was noticed that the films containing corn starch were highly biodegraded under above influences. The weight loss of the tested films decreased with increasing PVA content and increased with immersion time in enzymatic solution and water and soil burial time
The aim of this study was to use low cost adsorbents, which consist of corn cobs as plant wastes adsorbents in treatment of Industrial waste water by fixed bed column technique and study the effect of two variables (pH value and contact time). The sample of plant waste (Corn cobs) was tested to determine its activity which gives the best performance in heavy metals removal and other pollutants (TSS, TDS and COD). Adsorption tests showed the corn cobs adsorbents had significant heavy metal removal efficiency. The best removal efficiency 95.05% of Cr was occurred at pH 5.4 and 4.18hr. Higher removal efficiency 99.90% of Ni was occurred at pH 6.5 and 2.38hr. While, lower removal efficiency 91.35% for Zn obtained at pH 6.5 and 0.15hr. Remova
... Show MoreBackground: Because of the demands for aesthetic orthodontic appliances have increased, aesthetic archwires have been widely used to meet patient's aesthetic needs. The color stability of aesthetic archwires is clinically important, any staining or discoloration will affect patient’s acceptance and satisfaction. This study was designed to evaluate the color stability of different types of aesthetic archwires after immersion into different types of mouth washes. Materials and methods: Four brands of nickel titanium coated aesthetic arch wires: Epoxy coated (Orthotechnology and G&H) and Teflon coated (Dany and Hubit) were evaluated after 1 week, 3 weeks and 6 weeks of immersion into two types of mouthwashes (Listerine with alcohol and
... Show MorePolyacetal was synthesized from the reaction of PVA with para-methyoxy benzaldehyde. Polymer metal complexwas prepared by reaction with Cu, polymer blend with Chitosan was prepared through the technique of solution casting method.All prepared compounds have been characterized through FT-IR, DSC, SEM as well as the Biological activity. The FT-IR results indicated the formation of polyacetal. The DSC results indicated the thermal stability regarding prepared polymer, polymermetal complex and Chitosan polymer blends. Antibacterial potential related to synthesized polyacetal, its metal complex andChitosan blend against four types of bacteria namely, Staphylococcus aureas, Psedomonas aeruginosa, Bacillus subtilis, Escherichia coli was examined a
... Show MoreThe current study aimed to investigate the viability of biofilm formation klebsilla pneumoniae and Staphylococcus aureus. 440 urine samples were collected from patients suffering from urinary tract infection (UTI) from those who were admitted and visitors to Al-Ramadi Teaching Hospital, Al-Yarmouk Teaching Hospital, Al-Ramadi Teaching Hospital for women and children and , Teaching Laboratories in the Medical City for both genders for a period extended from 5 July, 2017 to 10 October, 2017. Samples were diagnosed by culturing them on a selective media and by biochemical testes , also, diagnosis was ensured by using VITEK-2 compact system. Results showed that K.pneumoniae isolation ratio was 17.1%(68) and S.aureus ratio was 13.1%(52). Thei
... Show MoreThe study effect irradiation on optical properties of film (PVA: CuCL2) prepared by casting method, with thickness of (30±1) μm. And used Cs137 to obtained Gamma ray with energy (662)keV and time irradiation(5,6 and 7) weeks and affectivity (4.3) ci. The spectra absorbance and transmittance register in range (300-1100) nm .
Results show that the optical band gap for (PVA: CuCl2) decreasing after irradiation with gamma ray from (3.2,3.1,3 and 2.7)eV, urbach energy values increase with the increasing time radiation. And the absorption constants (α,k,n,) and the optical conductivity are changing after irradiated with gamma ray .
The polymeric hydrogels composed of poly vinyl alcohol (m.wt 72000) and glutaraldehyde(5%,8% and 10%) , have been thermally prepared for the purpose of studying their swelling and drug release behavior . The swelling ratio was measured for all the hydrogel samples at 37°C, in three different media pH (1.2, 4.7 and 6.8) as a function of time. The results show that the maximum swelling ratios were arranged as follows :pH =6.8 > pH =4.7 > pH =1.2 hydrogels cross linked PVA showed a typical pH responsive behavior such as high pH has maximum swelling while low pH shows minimum swelling.
The polymeric hydrogels composed of poly vinyl alcohol (m.wt 72000) and glutaraldehyde(5%,8% and 10%) , have been thermally prepared for the purpose of studying their swelling and drug release behavior . The swelling ratio was measured for all the hydrogel samples at 37°C, in three different media pH (1.2, 4.7 and 6.8) as a function of time. The results show that the maximum swelling ratios were arranged as follows :pH =6.8 > pH =4.7 > pH =1.2 hydrogels cross linked PVA showed a typical pH responsive behavior such as high pH has maximum swelling while low pH shows minimum swelling.
Background: In dentistry, dentist takes the advantages of soft lining materials due to the viscoelastic properties. The major problem is the adhesion of the soft liner with the denture base material. Materials and Methods: Heat cured of high impact acrylic resin specimens prepared with dimensions 75x13x13mm for shear bond strength test, soft lining material (Refit and Mollosil) with a 3-mm thickness and used to join each two acrylic blocks. Also four specimens with the same previous dimensions utilized for chemical and physical surface analysis. The specimens grouped as control (without plasma) and experiment (with oxygen plasma) treated high impact acrylic specimens. Results: Plasma treatment increased the shear bond strength for both Refi
... Show MoreThis work investigates experimentally the effect of using a skirt with a square foundation of 100 mm width resting on dry gypseous soil (i.e., loose soil with 33% relative density), and subjected to an inclined load. Previous works did not study the use square skirted foundation rested on gypseous soil and subjected to inclined load. The investigated soil was brought from Tikrit city with 59% gypsum content. Standard physical and chemical tests on selected soil were carried out. Model laboratory tests were carried out to determine the effect of using a skirt with a square foundation on the load-settlement behavior of gypseous soil and subjected to inclined load with various Skirt depth (Ds) to foundation width (B) ratio
... Show MoreThe Rock Wool Board (RWB) is widely used in the building exterior insulation all over world. As polymer affects hardening of plate, meaning it acted as a basic binder in this work and gave a smooth texture, ease of carrying and workmanship in different sizes and shapes. PVA was studied at the rates of PVA %4, %5, %6.66, %10, %20, results showed that 6.66% is the best percentage, through tensile and bending tests, this percentage was use with polyurethane with rates of PU 1, 0.5, 0.333, 0.25, 0.2 It is found that the ratio 0.333 is the best ratio to give good mechanical properties of bending, tensile and elongation. This percentage was fixed on different percentages of polymer (PU/PVA) as %2.5, %5, %10, %15, %20 and examinations