Lithium–Manganese ferrites having the chemical formula (Li0.5-0.5x Mnx Fe2.5-0.5x O4), (0 ≤ x ≤ 1) were prepared by double sintering powder processing. The density of the ferrite increased with Mn content while the porosity was noticed to decrease. The dielectric constant was found to increase at high frequencies more rapidly than the low ones. The dielectric constant found to decrease with Mn content. The decrease in loss factor with frequency agreed with Deby’s type relaxation process. A maximum of dielectric loss factor was observed when the hopping frequency is equal to the external electric field frequency. Manganese substitution reduced the dielectric loss in ferrite. The variation of tanδ with frequency shows a similar na

The present experimental work is conducted to examine the influence of adding Alumina (Al₂O₃) nanoparticles and Titanium oxide (TiO₂) nanoparticles each alone to diesel fuel on the characteristic of the emissions. The size of both Alumina and Titanium oxide nanoparticles which have been added to diesel fuel to obtain nano-fuel is about 20 nm and 25 nm respectively. Three doses of (Al₂O₃) and (TiO₂) were prepared (25, 50, and 100) ppm. The nanoparticles mixed with gas oil fuel by mechanical homogenous (manual electrical mixer) and ultrasonic processor. The study reveals that the adding of Aluminum oxide (Al₂O₃) and Titanium oxide (TiO₂) to g

    This work is an experimental study conducted to study the effects of iron oxide dust particles (Fe₂O₃) on the characteristics of DC discharge plasma in argon gas under vacuum. Electron temperature ( ) and electron density (n_e) were calculated by Boltzmann plots and Stark broadening, respectively. The results show that both the electron density and plasma frequency ( ) increased with the operating pressure. While,  and Debye length ( ) decreased with pressure. The glow discharge is more stable with the Fe₂O₃-dust particles; all dust plasma parameters have lower values  than those of the dust-free plasma.

In this research, a sensor for chemical solutions was designed and formed using optical fiber-based on a surface Plasmon resonance technology. A single-mode optical fiber with three different diameters (25, 45 and 65) µm was used, respectively.  The second layer of the low refractive fiber was replaced by gold, which was electrically deposited at 40 µm thickness. For each of the three types of optical fiber, different saline concentrations (different index of refraction) were used to evaluate the performance of the refractive index sensor (chemical sensor) by measuring its sensitivity and resolutions. The highest values we could get for these two parameters were 240mm/RIU, and 6*10^-5 RIU respectively, when the diameter of a

The study aimed to measure the concentration of some heavy metal elements and represented by (Pb, Cd,Cu) through the use of atomic absorption spectrometer Flame AAS-7000 type SHIMADZU underwent a process modeling to twelve samples from the soil of electricity Dezlat al Jadiriyah station in the Baghdad University compound at a depth of 30-60 cm from the surface and divided the samples into two groups first included six samples from inside the station while the second included six samples from outside the station. For the element of Pb was higher concentration reached by 29.32ppm and less concentration 17.56ppm. were elements Cd and Cu are growing and less and proportions of certain while the highest concentration of copper 9.69 ppm and le

This research presents a new study in reactive distillation by using consecutive reaction: the saponification reaction of diethyl adipate (DA) with sodium hydroxide solution .

The effect of three parameters were studied through a design of experiments applying 2³ factorial design . These parameters were : the mole ratio of DA to NaOH solution (0.1 and 1) , NaOH solution concentration (3 N and 8 N) , and batch time (1.5 hr. and 3.5 hr.) . The conversion of DA to sodium monoethyladipate(SMA)(intermediate product) was the effect of these parameters which was detected . Also , the percentage purity of the intermediate product was recorded . The results showed that increasing mole ratio of DA to NaOHsolutio