Poly methyl methacrylate PMMA polymer has been used continually in dental application during the recent years. Yet, it is commonly known for its poor strength properties for long periods under pressure. The aim of this research was to improve the performance of PMMA denture base through the addition of different nanoparticles selected from artificial and natural sources. For comparison, Nano -particles from Al2O3 and crushed pistachio shell were utilised. (1%, 2% and 3%) were the weight fraction used in this study for both reinforcement types. In this work, a study and evaluation in of Compression Strength (C.S.) as well as Young’s Modulus (Y) was done before and after exposure for special liquids. The new prepared composites were immerse

In this work, biocompatible gold nanoparticles were synthesized by reducing the chloroauric acid with ascorbic acid as a reducing agent. Colloidal gold nanoparticles were stabilized through nontoxic acacia gum sodium hydroxide .Synthesizing gold nano particle is confirmed by the change in color of chloroauric acid from yellow to ruby red and brown color depending on the stabilizers. The gold nanoparticles were characterized by UV-Visible spectrophotometer. Where the peak of the absorbance of surface plasmon resonance (SPR) was observed between the wave length 526 and 535 nm. The results of zeta potential were found in rang (-19, -40 mv), AFM and TEM images show two different shapes, hexagonal and spherical and the size of gold nanopartic

In this research, a Co-polymer (Styrene / Allyl-2.3.4.6-tetra-O-acetyl-β-D-glucopyranoside) was synthesized from glucose in four steps using Addition Polymerization according to the radical mechanism using Benzoyl Peroxide (BP) as initiator. Initially, Allyl-2.3.4.6-tetra-O-acetyl-β-D-glucopyranoside monomer was prepared in three steps and the reaction was followed by (HPLC, FT-IR, TLC), in the fourth step the monomer was polymerized with Styrene and the structure was determined by FT-IR and NMR spectroscopy. The reaction conditions (temperature, reaction time, material ratios) were also studied to obtain the highest yield, the relative, specific and reduced viscosity of the prepared polymer was determined, from which the viscosity ave

Background: Polymethylmethacrylate (PMMA) has relatively unsatisfactory mechanical properties such as low flexural strength and impact strength also dimensional instability. Material and method: Zirconium silicate nanoparticles were coated with a layer of trimethoxysilylpropylmethacrylate (TMSPM) before sonication in monomer (MMA) with the percentages 1% and 1.5% by weight then mixed with powder using conventional procedure, (150) samples were prepared and divided into three groups, each group consisted of (50) samples, the first group prepared from PMMA without addition (control), another group with the addition of 1% wt Zrsio4 nanoparticles (experimental) and the third one with 1.5% wt Zrsio4 nanoparticles (experimental). Each group

The possibility of using zero-valent iron as permeable reactive barrier in removing lead from a contaminated groundwater was investigated. In the batch tests, the effects of many parameters such as contact time between adsorbate and adsorbent (0-240 min), initial pH of the solution (4-8), sorbent dosage (1-12 g/100 mL), initial metal concentration (50-250 mg/L), and agitation speed
(0-250 rpm) were studied. The results proved that the best values of these parameters achieve the maximum removal efficiency of Pb+2 (=97%) were 2 hr, 5, 5 g/100 mL, 50 mg/L and 200 rpm respectively. The sorption data of Pb+2 ions on the zero-valent iron have been performed well by Langmuir isotherm model in compared with Freundlich model under the studied

Background: The geriatric patients wearing removable partial dentures are increasing in proportion. At the same time, the root caries prevalence accompanied by gingival recession is increasing. A variety of vehicles can deliver fluoride into the oral cavity, including fluoride mouth-rinse, fluoride dentifrice, topical fluoride, and fluoride-releasing restorative materials, all of which effectively prevent root caries and suppress recurrent caries. This study aimed to evaluate the effect of sodium fluoride addition on some mechanical properties of heat cure acrylic denture base material. Material and method: A total of 90 samples were prepared in this study, then divided into three main groups according to the type of test used (hardness, te