Pure and doped TiO 2 with Bi films are obtained by pulse laser deposition technique at RT under vacume 10-3 mbar, and the influence of Bi content on the photocvoltaic properties of TiO 2 hetrojunctions is studied. All the films display photovoltaic in the near visible region. A broad double peaks are observed around λ= 300nm for pure TiO 2 at RT in the spectral response of the photocurrent, which corresponds approximately to the absorption edge and this peak shift to higher wavelength (600 nm) when Bi content increase by 7% then decrease by 9%. The result is confirmed with the decreasing of the energy gap in optical properties. Also, the increasing is due to an increase in the amount of Bi content, and shifted to 400nm when annealed at 523

Background: To evaluate the ISO depth of cure of bulkfill composites and depth of cure which determined by Vickers microhardness test. Materials and Methods: Bulkfill resin composite specimens (n=150) were prepared of three bulkfill composite materials (TetricEvo Ceram, Quixfil and SDR) and light cured by Flash max p3 for 3, 10, 20 seconds and by wood pecker for 10, 20 seconds respectively, a mold was filled with one of the three bulkfill composites and light cured. The specimens removed from the mold and scraped by plastic spatula and the remaining length (absolute length) was measured which represent the ISO depth of cure. After that the specimens were returned into the mold and a microhardness indentation device applied on the specimen

Aim: To evaluate the effect of two bonding systems and two curing systems on sealing ability of class V composite restorative materials. Materials and methods: This study was performed in vitro on 40 caries free upper first premolar teeth. The Standardized class V cavity preparation on buccal and lin- gual surfaces of each tooth was done. Then the teeth were randomly divided into two major groups each of twenty. 40 cavities were performed on these teeth and the first group7th generation bonding agent (i Bond) were applied according to the manufacturer instructions and single increment of univer- sal composite (XRV Herculite) from kerr were applied and twenty of the cavities were cured with con- ventional light cure device (astralis-5) and t

This study examines the species composition, biodiversity, zoogeography, and ecology of freshwater gastropods of 12 springs in Andijan region of Uzbekistan. The study used generally accepted malacological, faunistic, ecological, analytical, and statistical methods. As a result of research in the springs, 14 species of freshwater gastropods belonging to 2 subclasses, 5 families, and 10 genera were recorded. 7 of them are endemic to Central Asia. When indicators of biodiversity of mollusks were analyzed according to the Shannon index, it was found that the highest value was recorded in the springs besides the hills. According to the biotope of distribution and bioecological features, they were divided into cryophilic, phytophilic, pelophil

Aim: This abstract aims to highlight the critical nature of climate change as a pressing challenge facing humanity in the 21st century. It underscores the severe consequences it poses to essential facets of human existence, including water and energy resources, agricultural production, and the broader environmental systems. Method: The abstract primarily utilizes a descriptive approach to emphasize the impact of climate change on the Middle East, particularly the Arab region. It relies on a review of existing knowledge and data related to climate change and its effects on ecosystems and drought patterns. Results: The abstract outlines the direct and indirect repercussions of climate change on human life and the environment. It draws atten

In the cuurent article, the photophysical properties of 3,6-bis(5-bromothiophen-2-yl)-2,5-bis(2-ethylhexyl)-2,5-dihydropyrrolo[3,4-c]pyrrole-1,4-dione were investigated. The visible absorption bands at 527, 558 and 362 nm in propylene carbonate and the compound was found to be fluorescent in solution and in the plastic film with emission wavelengths between 550- 750 nm. The Stokes Shift of P.C., acetonitrile, diethyl ether, Tetrahydrofuran THF, cyclohexane, dibutyl ether, and dichloromethane DCM  are 734, 836, 668, 601, 601, 719, and 804 cm^-1 in respectively. The Stokes Shift Δ was less in THF and cyclohexane, than the solvents, which indicates that the energy loss is less between the excitation and fluorescence states. The

The photooxidative degradation process of plastics caused by ultraviolet irradiation leads to bond breaking, crosslinking, the elimination of volatiles, formation of free radicals, and decreases in weight and molecular weight. Photodegradation deteriorates both the mechanical and physical properties of plastics and affects their predicted life use, in particular for applications in harsh environments. Plastics have many benefits, while on the other hand, they have numerous disadvantages, such as photodegradation and photooxidation in harsh environments and the release of toxic substances due to the leaching of some components, which have a negative effect on living organisms. Therefore, attention is paid to the design and use of saf

Background: This study was formulated to compare the effect of 5%hydrofluoric acid in comparison to 37%phosphoric acid with and without the application of silane on bond strength of composite to porcelain. Materials and Methods: Specimen preparation was divided in to two phases, metal-disks fabrication (8mm-diameter and 4mm-thickness) and ceramic veneering. Thirty two specimens were prepared, sandblasted with 50 μm aluminum oxide, and divided into four groups of eight samples. Groups I and III were etched with 37%phosphoric acid while groups II and IV were etched with 5%hydrofluoric acid; and groups I and II were silaneted while groups III and IV were not. Heliobond, and resin composite were applied to each specimen using a plastic transpa

      The effect of fiber volume fraction of the carbon fiber on the thermal conductivity of the polymer composite material was studied. Different percentages of carbon fibers were used (5%, 10%, 15%, 20%, and 25%). Specimens were made in two groups for unsaturated polyester as a matrix and carbon fibers, first group has parallel arrangement of fibers and the second group has perpendicular arrangement of fibers on the thermal flow, Lee's disk method was used for testing the specimens. This study showed that the values of the of thermal conductivity of the specimens when the fibers arranged in parallel direction was higher than that when the fibers arranged in the perpendicular direction  

 &nbsp