A cermet (ceramic-metal) composite have been prepared from alumina (γ-Al2O3) reinforced with aluminum (Al) for the concentrations of (0, 10, 20, 30, 40, & 50) wt. %Al. The cermet was formed by single axial pressing, sintered in vacuum atmosphere. Compaction behaviors were studied in solid state sintering at sintering temperatures (400, 450, & 550) °C, sintering times (2, 4, & 6) hrs., and forming pressures (5, 10, 15) MPa, also in liquid phase sintering at (800 °C). The cermet was characterized by x-ray diffraction (XRD) and by scanning electron microscope (SEM), also physical and mechanical properties have been studied. SEM results showed the Al flowing inside the ceramic body due to uniform distribution of Al particles a

     In this research, we prepared a polymer blend of polyvinylalcohol (PVA)/carrageenan/kaolinite by means of the solution cast approach. The composition of the blend was PVA in 1 gm by weight with 0.2 gm carrageenan as a plasticizer. The ratio of nanoclay varied between 1 and 5 wt%. Different properties were investigated in this study such as water vapor permeability, hardness, tear strength, color stability, thermal stability, and antibacterial activity. Water vapor permeability was decreased with increasing the ratio of nanoclay, while the values of hardness, tear strength, color stability, and thermal stability were increased. Also, the antibacterial activity examination with two types of bacteria, e.g.

Due to the specific characteristic of porcelain, the insertion of Beryllium oxide has been studied. The basic materials and quantities were selected carefully. In this work, porcelain containing 32 wt% feldspar, 24 wt% quartz and 44 wt% clay was synthesized and  beryllium oxide (BeO) (1 wt.%, 3 wt.%, 5 wt% and 7wt%) were add. The basic and new composition porcelain powders were uniaxially compacted into standard samples dimensions and fired at various sintering temperatures, 1100°C, 1300°C, and 1450°C then  held for 2 hour in a furnace.

The effects of sintering temperatures and beryllium oxide content on mechanical, electrical and structural properties were studied. The increasing of sintering temperature on the basi

The family found itself confused any of the methods of dealing (Control - democracy) follow to reach the best level in education, what was favorite yesterday about a father dealing with his children control which showed generations characterized by high levels of self-esteem and decision-making, today rejected and opposed it. As some believe that a sense of control generates a negative represented by fear and frustration.
Find the goal of preparing the current scale of the father control when junior high students.
To achieve this goal, has been preparing a tool to measure the father control after that, the researcher extract the validity and reliability of the scale, and then applied to a sample of 500 students from junior high sch

Spin coating technique used to prepare ZnPc, CdS and ZnPc/CdS blend thin films, these films annealed at 423K for 1h, 2h and 3h. Optical behavior of these films were examined using UV-Vis. and PL. The absorption spectrum of ZnPc shows a decreasing in absorption with the increase of annealing time while CdS spectrum give a clearly absorption peak at~510 nm. Energy gap of ZnPc increases from 1.41 to 1.52 eV by increasing the annealing time. E_g of CdS decrease by increasing annealing time, from 2.3 eV to 2.2 eV. The intensities of the peaks obtained from PL spectra were strongly dependent on annealing time and confirmed the results obtained from UV-Vis. D.C. conductivity measurement showed that all the thin films have two differen

In this research we prepared nanofibers by electrospinning
from poly (Vinyl Alcohol) / TiO2. The spectrum of the solution
(Emission) was studied at 772 nm. Several process parameter were
Investigated as concentration of PVA, the effect of distance from
nozzle tip to the grounded collector (gap distance), and final the
effect of high voltage. We find the optimum condition to prepare a
narrow nanofibers is at concentration of PVA 16gm, the fiber has
20nm diameter

Abstract:In this research we prepared nanofibers by electrospinning from poly (Vinyl Alcohol) / TiO2. The spectrum of the solution (Emission) was studied at 772 nm. Several process parameter were Investigated as concentration of PVA, the effect of distance from nozzle tip to the grounded collector (gap distance), and final the effect of high voltage. We find the optimum condition to prepare a narrow nanofibers is at concentration of PVA 16gm, the fiber has 20nm diameter.

Iraqi kaolin was used for the preparation and characterization of NaY zeolite for biodiesel production via esterification reaction. Oleic acid was used usually as a typical simulated feedstock of high acid number for the esterification reaction.

   The chemical composition for the prepared Nay zeolite is as following:  (Ca₂.6Na₁.K_0.1)(Al₆.3Si₁₇.₇)O₄₈.16H₂O, the silica to alumina ratio in the prepared catalyst was found equal to 2.6 and Na₂O content was 12.26 wt. %, with relative crystallinity equal to 147.4 % obtained by the X-ray diffraction. The surface area result shows that the prepared catalyst has 330 m²

In this work, silver (Ag) self-metallization on a polyimide (PI) film was prepared through autocatalytic plating. PI films were prepared through the solution casting method, followed by etching with potassium hydroxide (KOH) solution, sensitization with tin chloride (SnCl₂), and the use of palladium chloride (PdCl₂) to activate the surface of PI. Energy-dispersive X-ray analysis (EDX) showed the highest peak in the (Ag) region and confirmed the presence of AgNPs. The diffraction peaks at 2θ = 38.2^°, 44.5^°, 64.6^°, and 78.2^° represented the 111, 200, 220, and 311 planes of Ag, respectively. The FT–IR an