Thin films of pure and doped nano titanium dioxide (TiO2) were prepared using a chemical pyrolysis technique (CPS), with different nanosize graphene oxide (GO) concentrations in the range (3-9)wt%. The structural, morphological andoptical characteristics of these films were investigated. X-ray diffraction (XRD) technique measurements revealed that the structure properties of TiO2have polycrystalline structure with anatase phase. AFM analysis showed the grain size of TiO2 films with different concentrations was decreased after doping with high concentration of GO ratio. Roughness of these films decreased too after adding of GO impurity for all films from (7.65-5.6)nm except 5wt% percentage where increased to 13.7nm. Optical

Background: Although bleaching is typically considered a safe procedure, various investigations have found minor negative effects and changes in mineral composition. The aim was to Evaluate and compare the efficacy of using Nanohydroxyapatite serum on surface microhardness of enamel surface before and after bleaching with chemically cured Boost bleaching. Material and methods: ten sound human permanent upper and lower premolar teeth were used and their roots were removed 2 mm apically to the cementoenamel junction, the crowns were sectioned mesiodistally into two halves buccal and lingual/palatal, the buccal surface was further subdivided into two halves. The samples were embeded in an acrylic resin, resulting in 30 specimens divide

Background: to evaluate the effect of different dentifrices on the surface roughness of two composite resins (nanofilled-based and nanoceramic – based composite resins). Materials and methods: Forty specimens (diameter 12 mm and height of 2mm) prepared from different composite resin materials: Z350 (nanofilled composite, and Ceram-X (nanoceramic) .they were subjected to brushing simulation equivalent to the period of 1 year. The groups assessed were a control group brushed with distilled water (G1), Opalescence whitening toothpasteR (G2), Colgate sensitive pro-relief (G3) and Biomed Charcoal Toothpaste (G4). The initial and final roughness of each group was tested by surface roughness tester. The results were statistically analyzed using

Background: Facial disfigurement can be the result of a congenital anomaly, trauma or tumor surgery, in many cases the prosthetic rehabilitation is indicated. Maxillofacial prosthetic materials should have desirable and ideal physical, aesthetic, and biological properties and those properties should be kept for long period of time in order to reach patient acceptance. Silicone elastomer are the most commonly used material for facial restoration because of its favorable properties mechanically and physically as the biocompatibility and good elasticity. Aim of this study: This study aimed to evaluate the effect of addition of Aluminum oxide (Al2O3) Nano fillers in different concentrations on tear strength and hardness of VST 50F room tempe

A successful synthesis of mesoporous Santa Barbara amorphous (SBA-15) with nanoparticle size was attempted using prepared sodium silicate from Iraqi high silica sand. EO20PO70EO20 copolymer was used as a template at highly acidic conditions (pH < 2). The effect of crystallization temperature of (100, 110, 120, and 130 0C), and crystallization time of (24, 48, 72, and 120 h) on surface properties was studied. The experiments were characterized using XRD, FTIR, AFM, BET, and FESEM. The XRD and FTIR tests represent amorphous SBA-15 without any impurities. Decreasing average particle size distribution increased the surface area, and decreased the porosity (pore volume, and pore size) in all experiments. The texture properties were su

‎ Sixteen new complexes with the general formula [M(L)2(H2O)2] were ‎prepared resulting from the reaction of the two new Schiff base ligands, which ‎are‏: -‏ L1= (E)-5-((2-hydroxybenzylidene)amino)-2-phenyl-2,4-dihydro-3H-pyrazol-3-one)‎ L2 = (E)-5-((2-hydroxy-3-methoxybenzylidene)amino)-2-phenylpyrazolidin-3-one) ‎ ‎ With divalent metal ions (manganese, cobalt, nickel, copper, zinc, cadmium, ‎mercury) and (tetravalent platinum).‎‏ ‏ ‎ Ligands was derived from the reaction of the amine (5-amino-2-phenyl-2,4-‎dihydro-3H-pyrazol-3-one) with Salicylaldehyde and ortho-vanillin, which is ‎linked to the metal ions via the nitrogen atoms are the isomethene group and ‎the oxygen is the hydroxide group of t

In this study, polymeric composites were prepared from unsaturated polyester as a base material with glass powder (fluorescent) in different weight ratios (4, 6, 8, 10,and 11%) as a support material and after comparison before and after reinforcement of the prepared composites, an increase was found. In the values ​​of mechanical properties (hardness, compressive strength), the shock resistance values ​​decreased, but an increase in temperature leads to an increase in the values ​​of shock resistance, as well as the values ​​of compressive strength And it reduces the hardness value.