In this work, Soda Lime Glass (S.L.G.) powder was used ,as
fluxe in traditional porcelain instead of feldspar. Two ceramics
porcelain were compared; commercial or traditional porcelain that
content of 50wt % kaolin, 25wt % quartz, and 25wt % feldspar.
Feldspar mass was substituted by scraps soda lime glass yielding a
new porcelain composition, to determine the softening points and
then the effect of glass addition on porcelain firing process.
Eight samples, for each patch, were prepared and 8wt % water
was added. The resulting composite blends were then die pressed at
2N, to produce disk specimens with diameter of 1.5 cm, and then
they were sintered at (1000, 1100, 1200, 1250,1300,1350,1400 and
1450) ˚C, for 2 hours in an electric furnace with a digital controller.
Physical parameters, such as density, water absorption, and
shrinkage were measured. It was concluded that the sintering
process and physical properties were improved by heat treatment.
However, the firing results showed that the addition of S.L.G.
replacing feldspar lowers the melting points of porcelain and the
addition of scrap powder has a positive effect on the quartz
dissolution
Various of 2,5- disubstituted 1,3,4-oxadiazole (Schiff base, ?- lactam and azo) were synthesized from 2,5-di (4,4?-amino-1,3,4-oxadiazole which usequently synth-esized from mixture of 4- amino benzoic acid and hydrazine arch of polyphosphorus acid. The synthesized compounds were cherecterized by using some spectral data (UV, FT-IR , and 1H-NMR)
(1)
Background : Carpal tunnel syndrome (CTS) is the most common entrapment neuropathy of upper extremities and Open carpal tunnel release is the most frequent surgical procedure and the gold standard for cases that do not respond to conservative treatment. Aims :This study is used to evaluate the functional outcome of limited palmar mini-incision of carpal tunnel release. This study aims to determine the safety and symptomatic and functional efficacy of median nerve decompression with limited incision in carpal tunnel syndrome surgery. Patients and methods:Carpal tunnel release with a 1.5-2 cm limited palmar incision was performed on 20 patients. Patients were evaluated initially at one month after treatment according to symptom severity
... Show MoreThe extraction of Eucalyptus oil from Iraqi Eucalyptus Camadulensis leaves was studded using water distillation methods. The amount of Eucalyptus oil has been determined in a variety of extraction temperature and agitation speed. The effect of water to Eucalyptus leaves (solvent to solid) ratio and particle size of Eucalyptus leaves has been studied in order to evaluate the amount of Eucalyptus oil. The optimum experimental condition for the Eucalyptus oil extraction was established as follows: 100˚C extraction temperature, 200 rpm agitation speed; 0.5 cm leave particle size and 6:1 ml: g amount of water to eucalyptus leaves Ratio.
(10)
(6)
Tillage appearance device is mechanical, electric-electronic design, getting Patent from the Central Organization for Standardization and Quality Control – Industrial Property Department - Ministry of Planning – The Republic of IRAQ under number Patent 3876 in 20 / 4 / 2014, calculates the number of clods per area by Tillage appearance device, This is done through the generation electrical impulses are sent to the controlled accurate calculates number clods required space and shows the result on the screen in order to see the tillage view per area. Three factor used in these experiment, first factor represents forward speed of tractor three levels (3.5, 4.5, and 5.5 km/h), second factor represent soil moisture content at two levels (14
... Show More
(11)
(5)
This study thoroughly investigates the potential of niobium oxide (Nb2O5) thin films as UV-A photodetectors. The films were precisely fabricated using dc reactive magnetron sputtering on Si(100) and quartz substrates, maintaining a consistent power output of 50W while varying substrate temperatures. The dominant presence of hexagonal crystal structure Nb2O5 in the films was confirmed. An increased particle diameter at 150°C substrate temperature and a reduced Nb content at higher substrate temperatures were revealed. A distinct band gap with high UV sensitivity at 350 nm was determined. Remarkably, films sputtered using 50W displayed the highest photosensitivity at 514.89%. These outstanding optoelectronic properties highlight Nb2O5 thin f
... Show More
(2)
In this study, the effect of fire flame on the punching shear strength of steel fiber reinforced concrete flat plates was experimentally investigated using nine half-scale specimens with dimensions of 1500×1500 mm and a total thickness of 100 mm. The main investigated variables comprised the steel fiber volume fraction 0, 1, and 1.5% and the burning steady state temperature 500 and 600 °C. The specimens were divided into three groups, each group consists of three specimens. The specimens in the first group were tested with no fire effect to be the reference specimens, while the others of the second and third groups were tested after being exposed to fire-flame effect. The adopted characteristics of the fire test were; (one hour) b
... Show More
(3)
Thermomechanical analysis (TMA) and differential scanning calorimetry (DSC) are used to investigate the effect of molding and annealing of polyester on the behavior of thermal expansion and crystallization since these factors play role in the reprocessing or recycling of the polymer. The dynamic mode of the TMA provides enhanced characterization information about the polyester since it separates the transitions into reversible and irreversible signals, and also reveals the progress of the amorphous regions as the polyester loses strength with the increasing temperature approaching melting. Slow cooling after annealing brings crystallization that may be attributed to molecular chain straightening due to orientation.