In this work, Soda Lime Glass (S.L.G.) powder was used ,as
fluxe in traditional porcelain instead of feldspar. Two ceramics
porcelain were compared; commercial or traditional porcelain that
content of 50wt % kaolin, 25wt % quartz, and 25wt % feldspar.
Feldspar mass was substituted by scraps soda lime glass yielding a
new porcelain composition, to determine the softening points and
then the effect of glass addition on porcelain firing process.
Eight samples, for each patch, were prepared and 8wt % water
was added. The resulting composite blends were then die pressed at
2N, to produce disk specimens with diameter of 1.5 cm, and then
they were sintered at (1000, 1100, 1200, 1250,1300,1350,1400 and
1450) ˚C, for 2 hours in an electric furnace with a digital controller.
Physical parameters, such as density, water absorption, and
shrinkage were measured. It was concluded that the sintering
process and physical properties were improved by heat treatment.
However, the firing results showed that the addition of S.L.G.
replacing feldspar lowers the melting points of porcelain and the
addition of scrap powder has a positive effect on the quartz
dissolution
The research entitled (The Visual Illusion in American Contemporary Ceramics) includes four chapters، the first chapter of which includes the methodological framework for the research، which contains the research problem focused on the following question: Has the American potter succeeded in achieving the artistic and aesthetic In the art of ceramics، as in the art of drawing and graphics، the fact that the art of ceramics has its advantages and limits in terms of material and technology? The aim of the research was to identify visual illusions in visual art in the works of a selected group of American potters. While the importance of the research was evident in that it sheds light on the methods and techniques of optical art in cont
... Show More
Special exercises in individual games are an important pillar in learning their basic skills. The aim of the research is to prepare special exercises using tools and their effect on learning the skill of landing with Salto backward tucked to stand - knowing the effect of special exercises using tools and their effect on learning the skill of landing with Salto backward tucked to stand on the horizontal bar. Either the research assumes the existence of significant differences in the pre- and post-tests in learning the skill of landing with Salto backward tucked to stand on the horizontal bar in favor of the post-test. The researchers used the experimental method with a single sample design to suit the research problem, as the researc
... Show More
(12)
(1)
Background: The purpose of this study was to evaluate the effect of addition of surface treated silicon dioxide Nano filler (SiO2) on some properties of heat cured acrylic resin denture base material (PMMA). The properties were impact strength, transvers strength, and surface hardness. Materials and methods: In addition to controlled group SiO2 powder was added to PMMA powder by weight in three different percentages 3%, 5% and 7%, mixed by probe ultra-sonication machine.120 specimens were constructed and divided into 3 groups according to the test (each group consist of 40 specimens) and each group was subdivided into 4 sub-groups according to the percentage of added SiO2 (finally each subgroup consist of 10 specimens). The tests conducte
... Show MoreSpray pyrolysis technique was subjected to synthesized (SnO2)1-x (TiO2: CuO) x Thin films on different substrates like glass and single crystal silicon using. The structure of the deposited films was studied using x-ray diffraction. A more pronounced diffraction peaks of SnO2 while no peaks of (CuO , TiO2 ) phase appear in the X-ray profiles by increasing of the content of (TiO2 , CuO) in the sprayed films. Mixing concentration (TiO2 , CuO) influences on the size of the crystallites of the SnO2 films ,the size of crystallites of the spray paralyzed oxide films change in regular manner by increasing of (TiO
... Show More
(4)
(1)
(13)
(1)
Recent research has examined the improvement of physical and dielectric properties of BaTiO3 ceramic material by small addition of excess TiO2 or BaCO3. The prepared samples sintered at different temperatures and varying soaking time. The results show that increasing the sintering temperature within 1350°C and soaking time of 10 hrs give better electrical and physical properties, which indicate the reaction is complete at higher temperature and period.
(Cu1-x,Agx)2ZnSnSe4 alloys have been fabricated with different Ag content(x=0, 0.1, and 0.2) successfully from their elements. Thin films of these alloys have been deposited on coring glass substrate at room temperature by thermal evaporation technique under vacuum of 10-5Torr with thickness of 800nm and deposition rate of 0.53 nm/sec. Later, films have been annealed in vacuum at (373, and 473)K, for one hour. The crystal structure of fabricated alloys and as deposited thin films had been examined by XRD analysis, which confirms the formation of tetragonal phase in [112] direction, and no secondary phases are founded. The shifting of main polycrystalline peak (112) to lower Bragg’s angle as compared to Cu2ZnSnSe4 angle refers to incorpora
... Show More