Magnesium aluminum silicate of glass ceramic having different amounts of magnesium fluoride in the range (0-13.2)%. Thermal expansion coefficient and micro hardness of the base glass and glass ceramic samples are seen to be interdependent but due to the multi – component system, the behaviour is seen to be somewhat complex, with an increase in Mg F2 content. The thermal expansion coefficient increase and micro harness decrease, numerical simulation of thermal expansion and hardness is useful in this study, L2 – regression is used to calculate the two parameters associated with each glass component, by comparing the measured parameters and the calculated parameters ,it is useful to use such a method to calculate the quantity

Porous Silicon (PS) layer has been prepared from p-type silicon by electrochemical etching method. The morphology properties of PS samples that prepared with different current density has been study using atom force measurement (AFM) and it show that the Layer of pore has sponge like stricture and the average pore diameter of PS layer increase with etching current density increase .The x-ray diffraction (XRD) pattern indicated the nanocrystaline of the sample. Reflectivity of the sample surface is decrease when etching current density increases because of porosity increase on surface of sample. The photolumenses (PL) intensity increase with increase etching current density. The PL is affected by relative humidity (RH) level so we can use

The operating characteristics of optoelectronic devices depend critically on the properties physical of the constituent materials, interesting compound has been focused on this research formed from group III and V of the periodic table. Thin film n-InSb heterjuntion were successfully fabricated on p-Si substrates by thermal evaporation technique at different annealing temperature (as prepared, 400,500,600) °C. The effect of annealing temperature on the structural, surface morphology, optical and optoelectronic properties of InSb films were investigated and studied. The crystal structure of the film was characterized by X-ray diffraction and techniques. AFM techniques inspect the surface morphology of InSb films, the study presented the val

In this research, we have added nano anatase TiO₂ as a partial replacement of Portland cement by a weight percentage of (0.25 to 1%) for the development of properties for protection against bacteria. The control mix was made by using "the cement to sand" proportion about (1: 2.75) with the "water to cement" proportion of (0.5) to study the structure, porosity, water absorption, density, mechanical properties, as well as anti-bacterial behavior. Inspections have been done such as scanning electron microscopy (SEM), and atomic force microscope (AFM) for mortar. Experimental results showed that after the addition of Nano powders in cement mortar, the structural properties improved significantly with the development of hydration o

Although the number of implants has increased gradually and consistently over the years to around one million per year globally, there is still far more potential for advancement in the field of dental implantology which is typically growing quickly. This study investigates the effect of nanofiller reinforcement high-performance polymer matrix to enhance mechanical and physical characteristics. Calcium silicate (CS)/Polyetherketoneketone (PEKK) biomedical composite (G0 as a control group) is reinforced with different weight percentages (G1-G4) of tellurium dioxide nanoparticles (TeO₂NPs) ( n = 5). This research uses ethanol as a binder for mixing various weight percentages (wt%) of TeO₂NPs w

This work is focused on studying the effect of liquid layer level (height above a target material) on zinc oxide nanoparticles (ZnO and ZnO₂) production using liquid-phase pulsed laser ablation (LP-PLA) technique. A plate of Zn metal inside different heights of an aqueous environment of cetyl trimethyl ammonium bromide (CTAB) with molarity (10^-3 M) was irradiated with femtosecond pulses. The effect of liquid layer height on the optical properties and structure of ZnO was studied and characterized through UV-visible absorption test at three peaks at 213 nm, 216 nm and 218 nm for three liquid heights 4, 6 and 8 mm respectively. The obtained results of UV–visible spectra test show a blue shift accomp