Study of the heat treatment effect on electrical and porosity of Cermet Coating layers (Zro2 – Y2O3) prepared by Thermal Spraying
...Show More Authors

The technical of Flame Thermal Spray had been used in producing a cermet
composite based on powders of stabilized zirconium oxide containing amount of
Yatteria oxide (ZrO2- 8Y2O3) reiforced by minerals powders of bonding material
(Ni-Cr- Al- Y) in different rates of additions (25, 35, 50) on stainless steel base type
(304) after preparing it by the way of Grit Blasting.
Before heat treatment, the coated cermet layers were characterized for porosity
and electric resistivity. All samples were heat treated in vacuum furnace at different
temperature and times. The physical tests had been operated after heat treatment
and gave best results especially porosity, which found to be reduced dramatically
and producing high hardness. The best thickness of coating with bonding material
(25%) was (1.5 mm). The resistivity was found to increase after heat treatment but
it reduces with increasing the amount of self bonding additions

View Publication Preview PDF
Quick Preview PDF
Publication Date
Fri Jan 03 2020
Journal Name
Chalcogenide Letters
THE EFFECT OF Ag CONTENT AND HEAT TREATMENT ON STRUCTURAL AND MORPHOLOGICAL PROPERTIES OF THIN (Cu1-xAgx)2 ZnSnSe4 FILMS
...Show More Authors

(Cu1-x,Agx)2ZnSnSe4 alloys have been fabricated with different Ag content(x=0, 0.1, and 0.2) successfully from their elements. Thin films of these alloys have been deposited on coring glass substrate at room temperature by thermal evaporation technique under vacuum of 10-5Torr with thickness of 800nm and deposition rate of 0.53 nm/sec. Later, films have been annealed in vacuum at (373, and 473)K, for one hour. The crystal structure of fabricated alloys and as deposited thin films had been examined by XRD analysis, which confirms the formation of tetragonal phase in [112] direction, and no secondary phases are founded. The shifting of main polycrystalline peak (112) to lower Bragg’s angle as compared to Cu2ZnSnSe4 angle refers to incorpora

... Show More
Preview PDF
Publication Date
Sun Feb 03 2019
Journal Name
Iraqi Journal Of Physics
Morphology and electrical properties of Cu X Zn1-XO thin films prepared by PLD technique
...Show More Authors

Cu X Zn1-XO films with different x content have been prepared by
pulse laser deposition technique at room temperatures (RT) and
different annealing temperatures (373 and 473) K. The effect of x
content of Cu (0, 0.2, 0.4, 0.6, 0.8) wt.% on morphology and
electrical properties of CuXZn1-XO thin films have been studied.
AFM measurements showed that the average grain size values for
CuXZn1-xO thin films at RT and different annealing temperatures
(373, 473) K decreases, while the average Roughness values increase
with increasing x content. The D.C conductivity for all films
increases as the x content increase and decreases with increasing the
annealing temperatures. Hall measurements showed that there are
two

... Show More
View Publication Preview PDF
Crossref
Publication Date
Sun Feb 03 2019
Journal Name
Iraqi Journal Of Physics
Electrical properties of pure NiO and NiO:Au thin films prepared by using pulsed laser deposition
...Show More Authors

The electrical properties of pure NiO and NiO:Au Films which are
deposited on glass substrate with various dopant concentrations
(1wt.%, 2wt%, 3wt.% and 4wt.%) at room temperature 450 Co
annealing temperature will be presented. The results of the hall effect
showed that all the films were p-type. The Hall mobility decreases
while both carrier concentration and conductivity increases with the
increasing of annealing temperatures and doping percentage, Thus,
indicating the behavior of semiconductor, and also the D.C
conductivity from which the activation energy decrease with the
doping concentration increase and transport mechanism of the charge
carriers can be estimated.

View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Sun Apr 22 2018
Journal Name
Al-nahrain Journal For Engineering Sciences
Numerical Analysis of the Effect of Scanning Speed on the Temperature Field Distribution for Laser Heat Treatment Applications
...Show More Authors

One of the unique properties of laser heating applications is its powerful ability for precise pouring of energy on the needed regions in heat treatment applications. The rapid rise in temperature at the irradiated region produces a high temperature gradient, which contributes in phase metallurgical changes, inside the volume of the irradiated material. This article presents a comprehensive numerical work for a model based on experimentally laser heated AISI 1110 steel samples. The numerical investigation is based on the finite element method (FEM) taking in consideration the temperature dependent material properties to predict the temperature distribution within the irradiated material volume. The finite element analysis (FEA) was carried

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Tue Mar 26 2019
Journal Name
Iraqi Journal Of Science
Study the Effect Some of Electrodeposition Parameters on Wear Resistance for Cu-MWCNT Composite Coating
...Show More Authors

A Copper- Mullet walled Carbon Nanotube Cu/MWCNT composite coatings prepared by direct and pulse electrodeposition with various contents of MWCNT particles, using electrodeposition method from acidic sulfate bath. The effect of the current density, pulse frequency and  particle loading (PL) of MWCNT particle in the electrolyte on the morphology and volume fraction Vol% of MWCNT in deposit were investigate. The experimental results indicated that the depositing condition affect on the microstructure of deposited copper and MWCNT Vol% in deposit. Also, the Vol% of MWCNT increases in deposit with particle loading (PL) increasing in the bath and increased with increased current density. Increasing MWCNTs in electrolyte produced increase

... Show More
View Publication Preview PDF
Publication Date
Mon Feb 04 2019
Journal Name
Iraqi Journal Of Physics
Electrical, thermal and optical characteristics of plasma torch
...Show More Authors

Non thermal argon plasma needle at atmospheric pressure was constructed. The experimental set up was based on simple and low cost electric components that generate electrical field sufficiently high at the electrodes to ionize various gases which flow at atmospheric pressure. A high AC power supply was used with 9.6kV peak to peak and 33kHz frequency. The plasma was generated using two electrodes. The voltage and current discharge waveform were measured. The temperature of Ar gas plasma jet at different gas flow rate and distances from the plasma electrode was also recorded. It was found that the temperature increased with increasing frequency to reach the maximum value at 15 kHz, and that the current leading the voltage, which demonstra

... Show More
View Publication Preview PDF
Crossref
Publication Date
Mon Apr 10 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Fabrication of Photodetector and Study of Its Structural and Optical Properties of Cadmium Oxide Thin Films Prepared by Vacuum Thermal Evaporation Method
...Show More Authors

     The fabricated Photodetector n-CdO /-Si factory thin films Altboukaraharara spatial silicon multi- crystallization of the type (n-Type) the deposition of a thin film of cadmium and at room temperature (300K) and thickness (300 ± 20nm) and the time of deposition (1.25sec) was antioxidant thin films cadmium (Cd) record temperature (673k) for one hour to the presence of air and calculated energy gap optical transitions electronic direct ( allowed ) a function of the absorption coefficient and permeability and reflectivity by recording the spectrum absorbance and permeability of the membrane record within the wavelengths (300 1100nm). was used several the bias ranged between 1-5 Volts. The results showed that this

... Show More
View Publication Preview PDF
Publication Date
Sun Mar 01 2020
Journal Name
Iraqi Journal Of Physics
The DC electrical Conductivity of prepared pure polypyrrole and polypyrrole /graphene (PPY/GN) nanocomposite by in-situ polymerization
...Show More Authors

Abstract

 In this work, pure Polypyrrole (PPy) and Polypyrrole (PPy)/Graphene (GN) was synthesized by in-situ polymerization in different weight percentages (0.1, 0.3, 0.5, 1, 3 and 5 wt.% (g)) of GN nano particles using chemical oxidation method at room temperature. The FTIR, SEM and electrical properties were studies for the nano composites. The result show that when concentration of GN Nano particle increase, the electrical conductivity increased and the graphene sheets were merging to form a continuous area of the GN through the polypyrrole base material. The FTIR spectra shows that the characteristics absorption peaks of polypyrrole that is, 1546.80, 1463.87 and 3400.27 cm-1(stretching vibration in the pyrrol

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Sun Apr 30 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Study the Effect of Thickness on the Electrical Conductivity and Optical Constant of Co3O4 Thin Films
...Show More Authors

 In this research the Cobalt Oxide (Co3O4) films are prepared by the method of chemical spray pyrolysis deposition at different thicknesses such that (250, 350, 450, and 550) ± 20 nm.      The optical measurement shows that the Co3O4 films have a direct energy gap, and they in general increase with the increase of the thickness. The optical constants are investigated and calculated such as absorption coefficient, refractive index, extinction coefficient and the dielectric constants for the wavelengths in the range (300-900) nm.     The electrical conductivity (σ) and the activation energies (Ea1, Ea2) have been investigated on (Co3O4) thin films as a function of thickness. The films

... Show More
View Publication Preview PDF
Publication Date
Sun Sep 07 2008
Journal Name
Baghdad Science Journal
Study the effect of thickness and annealing temperature on the Electrical Properties of CdTe thin Films
...Show More Authors

The electrical properties of polycrystalline cadmium telluride thin films of different thickness (200,300,400)nm deposited by thermal evaporation onto glass substrates at room temperature and treated at different annealing temperature (373, 423, 473) K are reported. Conductivity measurements have been showed that the conductivity increases from 5.69X10-5 to 0.0011, 0.0001 (?.cm)-1 when the film thickness and annealing temperature increase respectively. This increasing in ?d.c due to increasing the carrier concentration which result from the excess free Te in these films.

View Publication Preview PDF
Crossref