Objective(s): The aim of this study is to compare the impact strength of a heat cured denture-base acrylic resin
reinforced with metal wire and glass fibers.

Methodology: Forty five specimens were prepared from pink heat cure acrylic resin. Specimens were grouped into;
group-I (control group) which consists of 15 specimens with no reinforcement, group-II which consists of 15 specimens
reinforced with metal wire, and group-III consists of 15 specimens reinforced with glass fibers. Specimens were tested
by using charpy impact machine.

Results: The result showed that there was a highly significant difference in impact strength value among the testing
groups at (P < 0.001).

Conclusion: The impact str

Introduction: The present study was performed to evaluate the influence of a 1064 nm fiber laser on shear bond strength (SBS) at the interface of titanium and resin cement. Methods: Forty titanium discs of 6 mm × 3 mm (diameter and thickness respectively) were categorized into four groups (n=10): control group without any surface treatment and three groups treated with a fiber laser with 81 ns pulse duration, 30 kHz frequency, 10000 mm/s scanning speed, 0.05 mm spot size, and different average power values (3, 5 and 7 W) depending on the tested group. Titanium disc characterization was performed by the scanning electron microscope (SEM) and surface roughness tester. Phase analysis was achieved using an X-ray diffractometer (XRD). F

Background: Denture cleansing was an important step that could prevent the spread of infection and improve a patient's health, the durability of the dentures, and the overall quality of life; therefore, it was necessary to choose a suitable cleanser that, in addition to being effective, did not have an unfavorable effect on the qualities of the denture base resin itself when used for an extended period. For this purpose, this study aimed to evaluate the effect of tea tree oil (TTO) on Candida albicans adhesion and the surface roughness property of poly(methyl methacrylate) denture material after immersion in TTO. Methods: A total of 55 heat-cured acrylic resin specimens were used for C. albicans adherence and surface roughness tests. The

Reservoir characterization is an important component of hydrocarbon exploration and production, which requires the integration of different disciplines for accurate subsurface modeling. This comprehensive research paper delves into the complex interplay of rock materials, rock formation techniques, and geological modeling techniques for improving reservoir quality. The research plays an important role dominated by petrophysical factors such as porosity, shale volume, water content, and permeability—as important indicators of reservoir properties, fluid behavior, and hydrocarbon potential. It examines various rock cataloging techniques, focusing on rock aggregation techniques and self-organizing maps (SOMs) to identify specific and

Background: Dental implants act as infrastructure for fixed restoration to look like as a natural tooth. Osseointegration is a biological events and considered as a base for success of dental implant. The aim of this study is to evaluate the bond strength between bone and Ti implant coated with mixture of nano hydroxyapatite-chitosan-collagen compared with Ti implants coated with nano hydroxyapatite implanted in rabbit tibia, after different period of implantation time (two and six weeks) by torque removal test. Material and methods: 36 screws of commercially pure titanium; 8mm in length and 3mm diameter , 18 screws coated with mixture of nano hydroxyapatite-chitosan-collagen and18 screws coated with nano hydroxyapatite by dip coating. St

The research was conducted in one of the fields of the Department of Plant Production in the desert region (tomato development project) affiliated with the Directorate of Agriculture of the Holy Karbala Governorate for the purpose of studying the effect of spraying the shoots of the Kohlrabi plant (hybrid) with the Nano biopolymer (Chitosan) and the Azotobacter bio inoculum on the roots of the plant seedlings in terms of growth indicators and yield for the autumn agricultural season. 2023-2024 ,The means were compared according to the Duncan multiple ranges test at significant to level of 0.05.with R.C.B.D . The first factor was spraying the shoots with Nano- Chitosan at a concentration of (0, 1, and 2) g L-1, two weeks after transplanting,

The present studies are focused on the modification of the properties of epoxy resin with different additives namely aluminum, copper by preparing of composites systems with percentage (20%, 40% and 50%) of the above additives. The experimental results show that the D.C of conductivity on wt% filler content at ( 293-413 ) K electrical conductivity of all above composites increased with temperature for composites with filler contact and find the excellent electrical conductivity of copper and lie between (2.6*10-10 - 2.1*10-10)?.cm . The activation energy of the electrical conductivity is determined and found to decrease with increasing the filler concentration.

Objective: The aim of this work was to detect terpenes other than boswellic acid derivatives in olibanum of Boswellia Serrata found in Iraq. Methods: The olibanum of Boswellia Serrata was macerated in methanol for one day, then filtration. Filter at was concentrated till reddish brown syrupy residue was gained, (3%) potassium hydroxide was added till basification. This basic solution was stirred continuously until a uniform emulsion was formed, then extracted with chloroform in a separatory funnel; the chloroform fraction was analyzed by GC /MS spectrometry. Results: GC /MS analysis reveal the presence of terpenes and non-terpenes constituents. Conclusion: Most of the detected terpenes were sesquiterpenes and the least one was di-terpenes.

According to different types of democracy Indexes, hybrid regimes or those in the gray zone, make up the majority of regime transformations in the third wave of democracy. However, after nearly three decades, conceptual confusion about hybrid regimes persists and grows, while obstructing the accumulation of knowledge about the nature of hybrid regimes. This leads to significant political repercussions for democratization. This Paper attempts to provide a clearer view of different and overlapping concepts and classifications in this complex field, and sustain development in literature on democratic transformation. To achieve this, we followed an approach based on the classification of concepts and terms in three distinct categories, b