Fabrication of porous clay refractory insulating specimens from Iraqi kaolin with different percentage of Expanded Polystyrene (EPS) waste crumbs additions were investigated. After mixing and forming by hand molding, the specimens was dried and fired at 1300 oC. The structural, physical, mechanical and thermal properties of the refractory insulating products were measured. Maximum addition of EPS (1.25 wt%) lead to reduce the linear shrinkage to less than 1.7% and increased apparent porosity up to 50 %. As well as, the density, Modulus of rupture and thermal conductivity were reduced to 1.39 g/cm3, 4.1 MPa and 0.21 W/m.K, respectively. The final outcome, addition of EPS showed good results in the formation of pores without distorting the dimensions of specimens and without any cracks. In addition, it is possible to use these thermal insulators at temperatures up to 1300 oC.
The varied applications of polystyrene in various fields of life led to examining the cause of radiation influence on some rheological behavior of commercial Polystyrene (PS) solution in the chloroform (CHCl3) solvent. Polystyrene grains shape samples were irradiated using the radioactive element Cesium- 137 with (9 µci) activity for 10, 20, and 30 minutes. The viscosity of the polymer solution depends on the concentration and size (i.e. molecular weight) of the dissolved polymer. Experimental data showed that the radiation dose affected the value of viscosity (shear, relative, specific, and reduced). The viscosity value significantly reduced at 10 min radiation dose and when increasing the dose, the viscosity value increased
... Show MoreThe aim of this work is to detect the best operating conditions that effect on the removal of Cu2+, Zn2+, and Ni2+ ions from aqueous solution using date pits in the batch adsorption experiments. The results have shown that the Al-zahdi Iraqi date pits demonstrated more efficient at certain values of operating conditions of adsorbent doses of 0.12 g/ml of aqueous solution, adsorption time 72 h, pH solution 5.5 ±0.2, shaking speed 300 rpm, and smallest adsorbent particle size needed for removal of metals. At the same time the particle size of date pits has a little effect on the adsorption at low initial concentration of heavy metals. The adsorption of metals increases with increas
... Show MoreThis study was carried out in Baghdad (Al-Jadiriya) in 2006 by detecting ability of aquatic reed plant to remove heavy metals (Chromium) from waste water by batch process of adsorption with considering that acidic solution is best selection for such process with constant initial chromium concentration(60 mg/l),speed of shaking(300 rpm), temperature (30 Co) and constant contact time (4 h) but with different weights of adsorbent (reed) (0.5 ,1 ,2 ,3 and 4 )gm for each 100 ml volume of sample . The results showed that the percentage of the removed chromium were ( 8% ,17.5% ,31% ,40% and 50%) respectively for each sample according to the mass of adsorb
... Show MorePhosphorus is usually the limiting nutrient for eutrophication in inland receiving waters; therefore, phosphorus concentrations must be controlled. In the present study, a series of jar test was conducted to evaluate the optimum pH, dosage and performance parameters for coagulants alum and calcium chloride. Phosphorus removal by alum was found to be highly pH dependent with an optimum pH of 5.7-6. At this pH an alum dosage of 80 mg/l removed 83 % of the total phosphorus. Better removal was achieved when the solution was buffered at pH = 6. Phosphorus removal was not affected by varying the slow mixing period; this is due to the fact that the reaction is relatively fast.
The dosage of calcium chloride and pH of solution play an importa
The use of bio-fruit waste has more attention in recent years because of the low cost of bio-fibers and the protection of the environment. In this study, the epoxy was reinforced with fruit residues (cantaloupe peel powder) in proportions (1%, 2%, 3%, 4%, 5%, 7.5%, and 10% by weight) as results of mechanical tests such as impact, hardness, flexural and compression.
Adding sub microns particle size cantaloupe peels particles with a weight ratio of 7.5% improves the epoxy mechanical properties, like impact strength, hardness, flexural strength, and compression strength by 59.43%, 5.8%, 45.7%, and 118.2%, respectively.
Using X-ray diffraction, the crystallite size ( D) of cantaloupe peel the powder was about (3 nm).
In
... Show MoreBiodiesel is an environmentally friendly fuel and a good substitution for the fossil fuel. However, the purity of this fuel is a major concern that challenges researchers. In this study, a calcium oxide based catalyst has been prepared from local waste eggshells by the calcination method and tested in production biodiesel. The eggshells were powdered and calcined at different temperatures (700, 750, 800, 850 and 900 °C) and periods of time (1, 2, 3, 4 and 5 hr.). The effect of calcination temperature and calcination time on the structure and activity of the solid catalyst were examined by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), and Brunaure-Emmett-Teller (BET). The optimum catalyst performance was obtained at 900 °C
... Show MoreThe aim of this research is to benefit from recycl the aircraft waste oils which is discarded in sewage network, to be used in preparation of greases for industrial purposes and to reduce the environmental pollution. In this research synthetic greases were prepared with special specifications by mixing the waste oils after treating with (silica gel as adsorbent agent, and filtration to precipitate impurities then heated to 110 C? to get rid of water) bentonite produced in Iraq which is available and cheap with existence of high density polyethylene at specific conditions of ( heating and mixing) . The best weight proportion were reached, then paraffin wax and additives were added to improve the properties of grease and give the
... Show More