In this study the thermal conductivity of the epoxy composites were characterized as function of volume fraction, particle size of fillers and the time of immersion(30,60,90)days in water .Composites plates were prepared by incorporating (bi-directional) (0º-90º) glass fiber and silicon carbide (SiC) particles of (0.1,0.5,1)mm as particle size at (10%,20%,30%,40%) percent volume in epoxy matrix.
The composites shows slightly increase of the thermal conductivity with increasing volume fraction, particle size and increase with increasing the days of immersion in water. The maximum thermal conductivity (0.51W/m.K) was obtained before the immersion in water at 90 days for epoxy reinforcement by bi-directional glass fiber and SiC particles with volume fraction 40% and particle size 1mm
In this work, a composite material was prepared from Low-density polyethylene (LDPE) with different weight percent of grain and calcinations kaolin at temperature of (850oC) using single screw extruder and a mixing machine operated at a temperature between (190-200oC). Some of mechanical and physical properties such as tensile strength, tensile strength at break, Young modulus, and elongation at break, shore hardness and water absorption were determined at different weight fraction of filler (0, 2, 7, 10 and 15%). It was found that the addition of filler increases the modulus of elasticity, elongation at break, shore hardness and impact strength; on other hand, it decreases the tensile strength and tensile strength
... Show MoreBackground: This in vitro study compares a self-etch primer (SEP) to an etch-and-rinse (EaR) for bonding sapphire brackets by evaluation of the enamel etch-pattern, shear bond strength, amount of remnant adhesive and enamel surface damage following thermal and fatigue cyclic loading. Material and Methods: Ceramic (sapphire) brackets were bonded to 80 extracted human premolars using two enamel etching protocols: conventional EaR using 37% phosphoric acid (PA) gel (control), and a SEP (Transbond Plus). Each group was subdivided into two subgroups (n=20 teeth) according to the time of bracket debonding: after 24 h water storage or following 5000 thermo-cycles plus 5000 cycles fatigue loading, to determine the shear bond strength (SBS), adhesiv
... Show More
(18)
(2)
(2)
THE EFFECT OF SPREACL of KNOWLEDGE ON ETHICS
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
... Show More
(8)
(10)
Blades of gas turbine are usually suffered from high thermal cyclic load which leads to crack initiated and then crack growth and finally failure. The high thermal cyclic load is usually coming from high temperature, high pressure, start-up, shut-down and load change. An experimental and numerical analysis was carried out on the real blade and model of blade to simulate the real condition in gas turbine. The pressure, temperature distribution, stress intensity factor and the thermal stress in model of blade have been investigated numerically using ANSYS V.17 software. The experimental works were carried out using a particular designed and manufactured rig to simulate the real condition that blade suffers from. A new cont
... Show More
(2)
Background: This study was formulated to compare the effect of 5%hydrofluoric acid in comparison to 37%phosphoric acid with and without the application of silane on bond strength of composite to porcelain. Materials and Methods: Specimen preparation was divided in to two phases, metal-disks fabrication (8mm-diameter and 4mm-thickness) and ceramic veneering. Thirty two specimens were prepared, sandblasted with 50 μm aluminum oxide, and divided into four groups of eight samples. Groups I and III were etched with 37%phosphoric acid while groups II and IV were etched with 5%hydrofluoric acid; and groups I and II were silaneted while groups III and IV were not. Heliobond, and resin composite were applied to each specimen using a plastic transpa
... Show MoreGenerally the a.c. conductivity shows a power law in frequency s () where the exponent s ≤ 1. As the frequency goes to zero the conductivity become frequency independent. The a.c. conductivity was studied for the Ge1-xSex thin films to see how the selenium contents affect the permittivity and the permeability for the Ge1-x Sex. The thin films prepared by thermal evaporation at room temperature and under vacuum (~2 x10-5toor) using Edward coating unit model 306A. From the relation between ln conductivity and ln w, the effect of selenium contents in Ge1-x Sex thin films on the exponent value, the relaxation time and the maximum barrier height. An algebric fitting method for circles and circular arcs was used to find the permit
... Show More
(16)
(14)