Thin films of microcrystalline and nanocrystalline -silicon carbide and silicon, where deposited on glass substrate with substrate temperature ranging from 350-400C, with deposition rate 0.5nm per pulse, by laser induced chemical vapor deposition. The deposition induced by TEACO2 laser. The reactant gases (SiH4 and C2H4) photo decompose throughout collision associated multiple photon dissociate. Such inhomogeneous film structure containing crystalline silicon, silicon carbide and amorphous silicon carbide matrix, give rise to a new type of material nanocrystalline silicon carbide in which the optical transmittance is governed by amorphous SiC phase while nanocrystalline grain are responsible for the conduction processes. This new material is promised for many new applications, lick high efficiency solar cell.
X-ray diffraction patterns and scanning microscope images revealed that nanocrystalline SiC and Si films grew at substrate temperature above 400C, while completely amorphous films grew at substrate temperature 350C.
In this work, p-n junctions were fabricated from highly-pure nanostructured NiO and TiO2 thin films deposited on glass substrates by dc reactive magnetron sputtering technique. The structural characterization showed that the prepared multilayer NiO/TiO2 thin film structures were highly pure as no traces for other compounds than NiO and TiO2 were observed. It was found that the absorption of NiO-on-TiO2 structure is higher than that of the TiO2-on-NiO. Also, the NiO/TiO2 heterojunctions exhibit typical electrical characteristics, higher ideality factor and better spectral responsivity when compared to those fabricated from the same materials by the same technique and with larger particle size and lower structural purity.
in this work many amide polymers were prepared according to the modification reaction of polyacryloyl chloride or poluacrulic acid with different primary amines to mesuringninizing hormone were investgaited prior tq surgery in 10 postmenopaisal women with benign and 10 postmenopausal women with maliganant healthy
MM Al-Waiz, AA Al-Nuaimy, HA Aljobori, MJ Abdulameer, Annals of Saudi Medicine, 2006 - Cited by 1
An approach is depended in the recent years to distinguish any author or writer from other by analyzing his writings or essays. This is done by analyzing the syllables of writings of an author. The syllable is composed of two letters; therefore the words of the writing are fragmented to syllables and extract the most frequency syllables to become trait of that author. The research work depend on analyzed the frequency syllables in two cases, the first, when there is a space between the words, the second, when these spaces are ignored. The results is obtained from a program which scan the syllables in the text file, the performance is best in the first case since the sequence of the selected syllables is higher than the same syllables in
... Show More
Phenol oxidation by Fenton's reagent (H2O2 + Fe+2) in aqueous solution has been studied for the purpose of learning
more about the reactions involved and the extent of the oxidation process, under various operating conditions. An initial
phenol concentration of 100 mg/L was used as representative of a phenolic industrial wastewater. Working temperature
of 25C was tested, and initial pH was set at 5.6 . The H2O2 and the Fe+2 doses were varied in the range of
(H2O2/Fe+2/phenol = 3/0.25/1 to 5/0.5/1). Keeping the stirring speed of 200 rpm.
The results exhibit that the highest phenol conversion (100%) was obtained under (H2O/Fe+2/phenol ratio of 5/0.5/1)
at about 180 min. The study has indicated that Fenton's oxidation i
Physical adsorption by nitrogen gas was studied on seven commercial platinum reforming catalysts (RG-402, RG-412, RG-432, RG-451, RG 422,RG-482, PS-10), four prepared platinum catalysts (0.1%Pt/alumina, 0.2 %Pt/alumina, 0.45 %Pt/alumina and 0.55% Pt/alumina), and -alumina support. Physical adsorption was carried out by using Accelerated Surface Area and Porosimetry (ASAP 2400 device) at 77 K . The results indicate that the surface area in genaral decreases with increasing platinum percentage, high platinum loaded (0.45% and 0.55%) it was found that the percent increasing in surface area was lower than those obtained for low platinum loaded catalysts , and at very higher platinum loading 0.6 %Pt , some reduction in surface area was
... Show MoreDuring 2019-2020, the experiment was conducted in the laboratory of the Department of Field Crop Sciences, Faculty of Agricultural Engineering Sciences - Baghdad University, to investigate the impact of soaking wheat seeds produced during the 2016 agricultural season with three plant extracts (licorice root extract 2%, 4% and 6%, Acadian and Humic(500, 1000, & 1500 mg L-1). Aside from the two control treatments (soaking in distilled water with dried seeds). The results show that the soaking treatment with licorice root extract outperformed the other therapies in conventional laboratory germination, root length, and seedling vigor index (95 percent and 3.42 cm 1207) compared to the two control treatments (soaking with distilled w
... Show More
(6)
(1)
A research was conducted to determine the feasibility of using adsorption process to remove boron from aqueous solutions using batch technique. Three adsorbent materials; magnesium, aluminum and iron oxide were investigated to find their abilities for boron removal. The effects of operational parameters on boron removal efficiency for each material were determined.
The experimental results revealed that maximum boron removal was achieved at pH 9.5 for magnesium oxide and 8 for aluminum and iron oxide. The percentage of boron adsorbed onto magnesium,aluminum and iron oxide reaches up to 90, 42.5 and 41.5% respectively under appropriate conditions. Boron concentration in effluent water after adsorption via magnesium oxide comply with th