The influence of fiber orientation and water absorption on fatigue crack growth resistance for cold cure acrylic (PMMA) reinforced by chopped and woven -glass-fibers were investigated. A weight of 2 g for chopped fibers and the same weight for woven -glass-fibers (one layer) were used to prepare samples. Some of these samples would storage in dry condition; the others were immersed in water for 15 days. Fatigue test was carried out. The results shows that, for PMMA, the initial bending stress for dry specimen was 3.392 N/cm2 and the number of cycles were 1364, the initial bending stress for wet samples was 4.20 N/cm2, and the number of cycles was 2411. The samples would cut in two pieces because of the cracks would propagated fast during the test. Reinforcement PMMA with different kinds of glass fibers would increase the initial bending stresses for all specimens. The cracks would appear slowly during the test, and the specimens will not separate during the test except the samples which reinforced by Woven-Glass-Fibers
Optimum allocation of water for restoration of Iraqi marshes is essential for different related authorities. Abo-Ziriq marsh area about 120 km2 is situated 40 km east of Al-Nassryia city. After comparing the measured annual water qualities with the Iraqi standards for surface water quality evaluation, Abo-Ziriq marsh water quality was in acceptable limit. Hydro balance computation were done for each month by using interface among the HEC-RAS, HEC-GeoRAS and ArcView GIS software and built a number of eco-hydro relationships to simulate the marsh ecosystem by using HEC-EFM program to estimate water allocation adequate for ecosystem requirement and constructs a GIS hydraulic reference map to show inundation area, depth grid and velocity dis
... Show More
(2)
Background: Poly propylene fibers with and without silane treatment have been used to reinforce heat cure denture base acrylic but, some mechanical properties like transverse strength, impact strength, tensile strength, hardness, wear resistance and wettability. Which are related to the clinical use of the prosthesis are not evaluated yet. The aim of the study is to identify the influence of incorporation of treated and untreated fibers on these properties Materials and methods: Eighty four heat cure acrylic specimens were constructed by conventional flasking technique. They were divided into six groups according to the tests and each group was subdivided into two subgroups control and experimental groups (seven samples for each subgroup
... Show MoreBackground: Smoking is the major environmental risk factor that has been associated with the pathogenesis and progression of periodontal diseases. Interleukin-8 (IL-8), has been associated with the immunopathology of periodontitis. Objectives: To determine the influence of smoking on salivary Interleukin-8 level from smokers and non-smokers with periodontitis and periodontally healthy control subjects.
Materials and Methods: Un-stimulated saliva samples were collected of 90 participants: 30 smokers and 30 non-smokers with chronic periodontitis, as well as 30 periodontally healthy control subjects. The clinical parameters such as the pocket depth, clinical attachment loss, plaque index, and gingiv
... Show More
(7)
(9)
The Sunnah of the Prophet has a great impact in building human behavior, and the formation of Islamic thought, has worked to spread science in all of Egypt, as it carried to the people of the eternal prophecy of the love of science, it was a source of knowledge and civilization. It is a generous source, a rich source of the Islamic nation, always tender, and renewed benefit, which is not only a source of legislation and language but is a source of guidance for thought and guidance of behavior, and the Hadith The importance is obvious In the integration of Islam, and show aspects of human integration in the personality of Mustafa , and the Muslims are interested in talking - collected and codification -, and made the effort of the cent
... Show MoreThe aim of this study is to evaluate the levels of trace elements Magnesium (Mg), Zinc (Zn), Copper (Cu), and Selenium (Se) in blood sera of asthmatic patients by Atomic Absorption Spectrophotometry (AAS). The concentrations of Mg, Cu, and Zn have been determined by Flame Atomic Absorption spectrophotometry (FAAS), and Se with flameless Graphite Furnace Atomic Absorption Spectrophotometry (GFAAS). The study involves (55) asthmatic patients as study group and (28) subjects as control from both genders. Serum levels of Mg, Cu, and Se were significantly higher (p<0.001 for all) in patients when compared with healthy subjects, while Zn level was relatively significant (p<0.05). Our observations confirm the efficacy and applicability of (AAS) in
... Show MoreOne of the most important phenomenon that occurs in sheet metal forming processes is the spring-back, which causes several geometrical alterations in the parts. The accurate prediction of springback after bending unloading is the key to the tool design, operation control, and precision estimate concerning the part geometry. This study investigated experimentally the effect of pretension in three rolling direction (0, 90, 45 degree) on the springback behavior of the yellow brass, sheet under V shape bending die. The pre-tension ranges from five different levels starting of 11% to 55% from the total strain in each rolling direction by regular increase of 11 %, then bent on a V-die 90 degree for the springback estimate. From experiment the
... Show MoreA particulate polymer composite material was prepared by reinforcing with the Aluminum Oxide (Al2O3) or Aluminum (Al) metallic particles with a particle size of (30) µm to an unsaturated Polyester Resin with a weight fraction of (5%, 10%, 15%, 20%).
Tensile test results showed the maximum value of elastic modulus reached (2400MPa.) in the case of reinforcing with (Al) particles with weight fraction (20%) and (1500 MPa.) in the case of reinforcing with (Al2O3) particles of the same weight fraction.
When the impact and the flexural strength tests were done, the results showed that flexural strength (F.S), maximum shear stress (τmax), impact strength
... Show MoreGranular carbon can be used after conventional filtration of suspended matter or, as a combination of filtration - adsorption medium. The choice of equipment depends on the severity of the organic removal problem, the availability of existing equipment, and the desired improvement of adsorption condition.
Design calculations on dechlorination by granular - carbon filters considering the effects of flow rate, pH , contact time, head loss and bed expansion in backwashing , particle size, and physical characteristics were considered assuming the absence of bacteria or any organic interface .
Erbil city is located in the northern Iraq with a population of over one million people. Due to water crises farmers usually use wastewater and well water for the agricultural production. In this study six stations were designed to sample waste water and three from well water to define waste water and ground water characteristics. In this study, Residual Na+ Carbonate, Mg++ hazard, salinity hazard, Kelley index, %sodium, total hardness, permeability index, potential salinity, sodium adsorption ratio, and Irrigation Water Quality Index (IWQI) were determined. The order of average cation concentrations in water was Mg2+> Ca2+ > Na+ > K+. While the proportion of main
... Show More
(3)
This study was performed by using the unsaturated polyester resin as matrix to the
composite materials with the rice husk as reinforced materials . The research included study
of wear test on the composite material The results show that the, wear is increased with the
increase of applied load and distance slipping and also with time increase . moreover the
shows that the higher value wear rate( 1.91gm/cm) from the load (20) N and the higher value
wear rate (1.43gm/cm) from the higher distance (4cm) and from the higher time (6min) higher
wear rate (5.33gm/cm).