Glassy polymers like Poly Mathyel Metha Acrylate are usually classified as non-porous materials; they are almost considered as fully transparent. Thin samples of these materials reflect color changing followed by porous formation and consequently cracking when exposed to certain level of ?-irradiation. The more the dose is the higher the effect have been observed. The optical microscope and UV-VIS spectroscopy have clearly approved these consequences especially for doped polymers.

In this work, electrochemical process was presented to polymerized eugenol on Gr.2 and Gr.5 titanium alloys before and after treated by Micro Arc Oxidation (MAO), where Gr.2 is commercial pure titanium and Gr.5 is Ti-6Al-4V dental alloys. The deposited layers were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR). The adhesion strength of polymeric thin-film was estimation by using pull-off adhesion test and the result was the adhesion strength of PE was (1.23 MPa) on Gr.2 before MAO and increase to (1.98 MPa) on Gr.2 after MAO treatment. The corrosion behavior of Gr.2 and Gr.5 alloy in artificial saliva environment at

BACKGROUND: Clavicle fractures are common injuries in young active individuals, the mid third of the clavicle is most commonly fractured part(80% of clavicle fracture) OBJECTIVE: To compare the outcomes of operative and non operative management of displaced and or comminuted closed fracture of the mid third of clavicle in young adults PATIENTS AND METHODS: This prospective observational study of 24 patients of fracture of the mid third of the clavicle was conducted in Alkindy teaching hospital from July 2015 to January 2017 and divided into two groups; one managed by operative treatment with plate and screws and the other by non operative sling immobilization after taking the consent and the patients were seen at 2, 4, 6 weeks,3, 6, and 9 m

The main objective of this study is to understand the work of the pile caps made of lightweight aerated foam concrete and study the many factors affecting the ability and the capacity of the shear. The study was done by analyzing previous practical and theoretical experiences on the reinforced concrete pile caps. The previous practical results indicated that all specimens failed by shear diagonal compression or tension modes except one specimen that failed flexural-shear mode. Based on test specimens' practical results and behavior, some theoretical methods for estimating the ultimate strength of reinforced concrete pile caps have been recommended, some of which evolved into the design documents available on the subject.

Background: White spot lesions are esthetic problems caused by subsurface enamel demineralization that seen as white opacity. Aim of the study: This study aimed to evaluate and to compare the color change after the treatment of the white spot lesions with resin ‹nϔ‹Žtrƒt‹on and micro abrasion. Materials and Methods: rt‹ϔ‹…‹ƒŽ white spot lesions were generated on 48 premolar teeth by the use of a demineralization solution. The teeth were randomly divided using the Diagnodent into three study groups (16 teeth for each group) depending on the depth of the induced lesions: outer enamel, inner enamel and outer dentine. Then each group was fatherly subdivided into two groups (8 teeth for each group) the ϔ‹rst group was treated wit

Two simple, rapid, and useful spectrophotometric methods were suggest or the determination of sulphadimidine sodium (SDMS) with and without using cloud point extraction technique in pure form and pharmaceutical preparation. The first  method was based on  diazotization of the Sulphdimidine Sodium drug by sodium nitrite at 5 ºC, followed by coupling with α –Naphthol in basic medium to form an orange colored product . The product was stabilized and its absorption was measured at 473 nm. Beer’s law was obeyed in the concentration range of (1-12) μg∙ml^-1. Sandell’s sensitivity was 0.03012 μg∙cm^-1, the detection limit was 0.0277 μg∙ml^-1, and the limit of Quantitation was 0.03605μg

4-methylaniline and its Schiff base derivative were intercalated into the Bentonite clay interlayers in a solid state reaction followed by a condensation reaction to produce two organo-clay composites. X-ray diffraction was used to identify the changes in basal spacing of montmorillonite layers which exhibited noticeable alteration before and after the formation of the composites. FT-IR spectra, on the other hand, were utilized for identifying the structural compositions of the prepared materials as well as the formation of the intercalated Schiff base derivative. The surface morphology of the composites was examined by Scanning Electron Microscopy SEM and Atomic Force Microscope AFM, which reflected some differences in the surface of prepa

The present research was conducted to reduce the sulfur content of Iraqi heavy naphtha by adsorption using different metals oxides over Y-Zeolite. The Y-Zeolite was synthesized by a sol-gel technique. The average size of zeolite was 92.39 nm, surface area 558 m²/g, and pore volume 0.231 cm³/g. The metals of nickel, zinc, and copper were dispersed by an impregnation method to prepare Ni/HY, Zn/HY, Cu/HY, and Ni + Zn /HY catalysts for desulfurization. The adsorptive desulfurization was carried out in a batch mode at different operating conditions such as mixing time (10,15,30,60, and 600 min) and catalyst dosage (0.2,0.4,0.6,0.8,1, and 1.2 g). The most of the sulfur compounds were removed at 10 min for all catalyst ty

Background: Even the wide use of dental implants, still there is a proportion of implants are failed due to infection. Much considerable attention has been paid to modify the implant surface. Coating of dental implant with a biocomposite material of suitable properties can improve osseointegration. And this is the main concern of this study. The aim of present study was to evaluate the use of a biocomposite coating of dental implant with (ceramic nano Al2O3 and metalic AgNo3) on the bond strength at bone – implant interface and tissue reaction. Materials and methods: A total number of forty-eight screws, CpTi dental implant used in this study. Half of these screws were coated with a biocomposite material of nano (Al2O3and AgNo3), thi