The Corrosion protection effectiveness of Alimina(Al2O3,50nm)and Zinc oxide (ZnO,30nm) nanoparticales were studied on carbon steel and 316 stainless steel alloys in saline water (3.5%NaCl)at four temperatures: (20,30,40,50 OC)using three electrodes potentiostat. An average corrosion protection efficiencies of 65 %and 80% was achieved using Al2O3 NP's on carbon steel and stainless steel samples respectively, and it seems that no effect of rising temperature on the performances of the coated layers. While ZnO NP'S showed protection efficiency around 65% for the two alloys and little effected by temperature rising on the performanes of the coated layers. The morphology of the coated spesiemses was examined by Atomic force microscope.

             The synthesis of nanoparticles (GNPs) from the reduction of HAuCl₄ ^.3H₂O by aluminum metal was obtained in aqueous solution with the use of Arabic gum as a stabilizing agent. The GNPs were characterized by TEM, AFM and Zeta potential spectroscopy. The reduction process was monitored over time by measuring ultraviolet spectra at a range of λ 520-525 nm. Also the color changes from yellow to ruby red, shape and size of GNP was studied by TEM. Shape was spherical and the size of particles was (12-17.5) nm. The best results were obtained at pH 6.

Hydrogen sulfide removal catalyst was prepared chemically by precipitation of zinc bicarbonate at a controlled pH. The physical and chemical catalyst characterization properties were investigated. The catalyst was tested for its activity in adsorption of H₂S using a plant that generates the H₂S from naphtha hydrodesulphurization and a unit for the adsorption of H₂S. The results comparison between the prepared and commercial catalysts revealed that the chemical method can be used to prepare the catalyst with a very good activity.

It has observed that the hydrogen sulfide removal over zinc oxide catalyst follows first order reaction kinetics with activation energy of 19.26 kJ/mole and enthalpy and e

Background: It was stated in scientific literatures that the entire craniofacial complex is influenced by the growth of the cranial base structures. Nevertheless, many times this is not the case, and this point is subject to great controversy so the aim of this study is to evaluate the possible differences in cranial base shape and flexure between different skeletal classes for both genders and to investigate any possible correlation between cranial base variables and other skeletal base variables. Materials and Methods: The sample include 75 lateral cephalometric radiographs of Iraqi adults aged between 18-25 years (39 males, 36 females), collected from patients and undergraduate students in the orthodontic department of College of Dentist

This article reviews the construction of organic solar cell (OSC) and characterized their optical and electrical properties, where indium tin oxide (ITO) used as a transparent electrode, “Poly (3-hexylthiophene- 2,5-diyl) P3HT / Poly (9,9-dioctylfluorene-alt-benzothiadiazole) F8BT” as an active layer and “Poly(3,4-ethylenedioxythiophene)-poly (styrene sulfonate)” PEDOT: PSS which is referred to the hole transport layer. Spin coating technique was used to prepared polymers thin film layers under ambient atmosphere to make OSC.  The prepared samples were characterized after annealing process at (80 ͦ C) for (30 min) under non-isolated circumference. The results show a value of filling factor (FF) of (2.888), (0.233) and (0.28

In this study, polymeric composites were prepared from unsaturated polyester as a base material with glass powder (fluorescent) in different weight ratios (4, 6, 8, 10,and 11%) as a support material and after comparison before and after reinforcement of the prepared composites, an increase was found. In the values ​​of mechanical properties (hardness, compressive strength), the shock resistance values ​​decreased, but an increase in temperature leads to an increase in the values ​​of shock resistance, as well as the values ​​of compressive strength And it reduces the hardness value.

     In the present study, pure Poly(viny1 alcohol) (PVA) and  pyromellitic dianhydride (PMDA) cross linked PVA with (0,5,10,15 and 20)wt.% and doped with different molarity (5,9)M of sulfuric acid (H₂SO₄) were prepared by the solution casting method and were characterized as a function of  frequency in the range (1-100) KHz.

     The FT-IR results showed that the strong broad band observed at 3738.05 and 3857.63 cm^-1 may be assigned to O-H stretching due to the strong hydrogen bond of intramolecular and intermolecular type in PVA film.  When PVA is doped with 5M and 9M H₂SO₄,  a new peak was noticed at 813 cm^-1, this peak may be due to the fo

أدى التغير السريع في البيئة الخارجية للمنظمة إلى  ظهور حالة من التنافس الشديد مما زاد تخوف الشركات من فقدان الحصة السوقية والخسارة . مما حدا بالمنظمات إلى الاهتمام بوجود مدير يحمل صفات وخصائص قيادية لما فيه من ميزات في تنظيم الإنتاج  ومقابلة الطلب وتقليل التكاليف وتطوير الأداء للحصول على ميزة تنافسية تحافظ او تزيد من حصتها السوقية وإرباحها .

تسعى الدراسة الى تحديد عدد من الاهداف كان اهمها معرفة الع

A new Mannich base ligand was prepared by reacting the 2-chloro.-N-(5-mercapto-1, 3, 4-thiadazol -2-yl) acetamide and Piperidine in the presence (formaldehyde) (L) ligand. A series of ligand complexes were prepared from (L) with the metal ion Co (II), Ni (II), Cu (II), Pd (II), Pt (IV), and Au (III). Various spectroscopic techniques such as C.H.N.S, FTIR, UV-VIS, , ¹HNMR, ¹³CNMR, Magnetic moment, and molar conductivity successfully characterize the obtained compounds. The M: L ratio was determined using the molar ratio method in solution. All prepared compounds' antibacterial and antifungal activity was studied against two types of bacteria and one type of fungi at a rate of 0.02M. The standard ΔH°