Four batches of sertraline HCl microspheres were prepared using a poly (D-L-lactide-co-glycolide) (PLGA) polymer ( Mw. 9, 27, 30 and 83 KDa) as  a delivery system. The microspheres were prepared by a dispersion/solvent extraction-evaporation method and characterized for drug loading by UV, particle size by laser diffractometry and surface morphology by scanning electron microscopy (SEM). The in vitro sertraline HCl release was studied. Spherical microspheres with a mean diameter of 21 to 26 µm loaded with 24.6 – 38.2% were produced. The in vitro drug release was shown to be depend on polymer molecular weight and also on the drug loading. Differential scanning calorimetry (DSC) was employed to investigate the physical state

Iraqi kaolin was used for the preparation and characterization of NaY zeolite for biodiesel production via esterification reaction. Oleic acid was used usually as a typical simulated feedstock of high acid number for the esterification reaction.

   The chemical composition for the prepared Nay zeolite is as following:  (Ca₂.6Na₁.K_0.1)(Al₆.3Si₁₇.₇)O₄₈.16H₂O, the silica to alumina ratio in the prepared catalyst was found equal to 2.6 and Na₂O content was 12.26 wt. %, with relative crystallinity equal to 147.4 % obtained by the X-ray diffraction. The surface area result shows that the prepared catalyst has 330 m²

    The LiCoMnO₄ spinel compound was prepared by a sol–gel method. Structural measurements were utilized to investigate the characteristics of LCMO powder. The powder crystallizes in the space group Rd-3m, with a trigonal crystallinity structure, according to XRD analysis (hexagonal axes). SEM images showed that the crystalline grains sizes were about 200 nm - 350 nm, which provides large surface area. The sample had soft magnetic characteristics, according to hysteresis behaviour analysis in the Vibrating Sample Magnetometer (VSM). The prepared material is thought to be a candidate for the applications of energy storage in lithium-ion batteries.

In this study, crop residues from rice husks were used to enhance the properties of the prepared
wood-plastic composites (W.P.C) are made from epoxy (EP) and unsaturated polyester (UPE) at
a ratio of (50:50) and reinforced with scales in different proportions, both types are fine
(300μm≤) and coarse (300μm>). These blends were undergoing (wear, impact, hardness,
differential scanning calorimetry (DSC), and thermal conductivity) tests and the results showed
the best weight fraction. is the fine particle weight fraction at 25% and coarse at 15%, depending
on the studied tribological characteristics. The results showed by thermal properties of glass
transition temperatures (Tg). For each of the (EP,

In this research four steps of the new derivatives of Naproxen drug have been made which are known as a high medicinal effectiveness; the first step involved converting Naproxen into the corresponding ester (A) by reaction Naproxen with methanol absolute in presence H2SO4. While the second step involved treatment methyl Naproxen ester (A) with hydrazine hydrate 80% in presence of ethanol .The third reaction requires synthesis of Schiff bases (C1-C10) by condensation. of Naproxen hydrazide (B) with many substituted aromatic aldehydes . Finally, the fourth step synthesized new tetrazole derivatives ( D1- D10) by the reaction of the prepared Schiff bases (in the third step) with Sodium azide in THF as a solvent .The prepared compounds wer

The composites were manufactured and study the effect of addition of filler (nanoparticles SiO2 treated with silane) at different weight ratios (1, 2, 3, 4 and 5) %, on electrical, mechanical and thermal properties. Materials were mixed with each other using an ultrasound, and then pour the mixture into the molds to suit all measurements. The electrical characteristics were studied within a range of frequencies (50-1M) Hz at room temperature, where the best results were shown at the fill ratio (1%), and thermal properties at (X=3 %), the mechanical properties at the filler ratio (2%).

 In this study, Mn-Ni Ferrite was prepared by using two composites of manganese ferrite ( MnFe2o4 )  and Nicle Ferrite ( NiFe2O4) tested by X-Ray diffraction (XRD) method. The dielectric constant (𝜀̅) and the dielectric loss tangent (𝑡𝑎𝑛 𝛿) were studied for the ferrite system prepared at different frequencies (100, 200… and 5000 kHz). It was found that the values of (𝜀̅) and (𝑡𝑎𝑛 𝛿) decrease with the  increase of frequencies.

Bromelain is a proteolytic enzyme rich in cysteine proteases, extracted from the stem and fruit of pineapple (Ananas comosus). There are several therapeutic applications of the bromelain enzyme, where it has anti-inflammatory, anti-cancer, and antimicrobial activity, reduces joint pain, and accelerates wound healing. In the current study, bromelain enzyme was loaded on silver nanoparticles (Br-AgNPs) prepared using the citrate-reduction Turkevich method. Different characterization analyses were performed, including UV-Vis spectrophotometers, FTIR, SEM, and XRD analyses. Moreover, the antioxidant activity of prepared Br-AgNPs was evaluated by DPPH assay. The results of UV-Vis showed a peak at 434 nm, which referred to the AgNPs f

The utilization of metal oxide nanoparticles, especially zinc oxide, is of a great importance in the medical field because of its physical and chemical properties as well as its antimicrobial potential effects. In our study, the ZnO nanoparticles were synthesized by the precipitation method where pH=14. ZnO nanoparticles were characterized by ultraviolet–visible spectroscopy, X-ray diffraction (XRD), transmission electron microscopy (TEM) and atomic force microscope (AFM). Antifungal activity of the ZnO was tested against candida albicans. The results showed that C. albicans (15 samples) became resistant to the fungal activity after testing its sensitivity to several types of fungal antibiotics. UV-vis spectroscopy, XRD, TEM and A

     The ferric oxide nanoparticles (Fe₂O₃) which are deposited at interface which is related to hole collecting buffer layer [poly(3,4-ethyl-enedioxythiophene): poly(styrene-sulfonate) (PEDOT: PSS)] as well as regioregular poly(3-hexyl-thiophene): Zinc oxide nanoparticles (P3HT): (ZnO) active layer have been considerable increasing the performance of solar cell. Also, the solar cell devices have been fabricated with a weight ratio of 1:0.7, 1:0.8, 1:0.9 and 1:1 of P3HT and ZnO, respectively. In addition, photo physical characteristics regarding such devices with different value of the weight ratio were examined. This work is indicating that the absorption spectrum related to blend will be broad