Objective: The current investigation focused on Acinetobacter baumannii (A. baumanni), due to its growing significance as a hospital infection-causing pathogen and its resistance to several medications.Material and Method: Sixty-five isolates of A. baumannii were isolated from wound samples of patients admitted to different hospitals in Baghdad between January and April of 2023. Two types of methods were used in the detection of biofilm formation: the first one was Congo red agar method and the second one was microtiter plate method. Genotypic detection of various virulence factors associated with A. baumannii was performed using monoplex, multiplex, and ERIC-PCR.Result and Discussion: To use the PCR method to examine

TiO2 thin films have been deposited at different concentration of
CdO of (x= 0.0, 0.05, 0.1, 0.15 and 0.2) Wt. % onto glass substrates
by pulsed laser deposition technique (PLD) using Nd-YAG laser
with λ=1064nm, energy=800mJ and number of shots=500. The
thickness of the film was 200nm. The films were annealed to
different annealing (423 and 523) k. The effect of annealing
temperatures and concentration of CdO on the structural and
photoluminescence (PL) properties were investigated. X-ray
diffraction (XRD) results reveals that the deposited TiO2(1-x)CdOx
thin films were polycrystalline with tetragonal structure and many
peaks were appeared at (110), (101), (111) and (211) planes with
preferred orientatio

Rare-earth metal oxides (REMOs) exhibit distinctive properties, among which cerium oxide (CeO2) displays numerous industrial, technological, and medical applications. However, the inclusion of hafnium (Hf) at the cerium (Ce) site to form the (Ce1-ₓHfₓO2) lattice system at a concentration of x = 0.25 would have an impact on enhancing the physical properties of the simulated configuration. Density functional theory (DFT) was used to perform the calculations, supported by the Hubbard correction factor (U). The generalized gradient approximation (GGA-PBE) was employed to analyze the electronic, structural, optical, and mechanical properties at hydrostatic pressures (P = 0, 25, 50, 75, and 100 GPa). The ground state geometry of the pristine

In this work, pure and Ag-doped nickel oxide (NiO) thin films were deposited on glass substrates with different dopant concentrations (0.1, 0.2, 0.3 and 0.4 wt.%) by pulsed-laser deposition (PLD) technique at room temperature. These films were annealed at temperature of 450 °C. The structural and optical properties of the prepared thin films were studied. It was found that annealing process has lead to increase the transmittance of the deposited films. Also, the transmittance was found to increase with doping concentration of silver in the deposited NiO films. The optical energy gap was decreased from 3.5 to 3.2 eV as the doping concentration was increased to 0.4 %.

This thesis aims to study the effect of addition polymer materials on mechanical properties of self-compacting concrete, and also to assess the influence of petroleum products (kerosene and gas oil) on mechanical properties of polymer modified self-compacting concrete (PMSCC) after different exposure periods of (30 ,60 ,90 ,and 180 days).

Two type of curing are used; 28 days in water for SCC and 2 days in water followed 26 days in air for PMSCC.

The test results show that the PMSCC (15% P/C ratio) which is exposed to oil products recorded a lower deterioration in compressive strength's values than reference concrete. The percentages of reduction in compressive strength values of PMSCC (15% P/C ratio) was

Pure and doped TiO 2 with Bi films are obtained by pulse laser deposition technique at RT under vacume 10-3 mbar, and the influence of Bi content on the photocvoltaic properties of TiO 2 hetrojunctions is studied. All the films display photovoltaic in the near visible region. A broad double peaks are observed around λ= 300nm for pure TiO 2 at RT in the spectral response of the photocurrent, which corresponds approximately to the absorption edge and this peak shift to higher wavelength (600 nm) when Bi content increase by 7% then decrease by 9%. The result is confirmed with the decreasing of the energy gap in optical properties. Also, the increasing is due to an increase in the amount of Bi content, and shifted to 400nm when annealed at 523