Increase in unconventional resources of calcium (Ca⁺²) for fowls, aquaculture and native animals was improved. This work was planned to define the most polymorph of calcium carbonate (CaCO₃) that take place in the two types of chicken eggshells (local and imported type). In this research, the comparative analysis of calcium carbonate (CaCO₃) content was approved for nominated eggshells of native strain and imported chicken via Field Emission Scanning Electron Microscope (FESEM), Transmission Electron Microscope (TEM), Fourier-Transform Infrared Spectroscopy (FTIR) and Powder X-Ray Diffraction (PXRD) analysis. The results demonstrate that native and imported chicken eggshells comprise calcite morph that ha

A low-cost reverse flow plasma system powered by argon gas pumping was built using homemade materials in this paper. The length of the resulting arc change was directly proportional to the flow rate, while using the thermal camera to examine the thermal intensity distribution and demonstrating that it is concentrated in the centre, away from the walls at various flow rates, the resulting arc's spectra were also measured. The results show that as the gas flow rate increased, so did the ambient temperature. The results show that the medium containing the arc has a maximum temperature of 34.1 ˚C at a flow rate of 14 L/min and a minimum temperature of 22.6 ˚C at a flow rate of 6 L/min.

The work done in this paper to study properties for nitrogen plasma generated by method electrical discharge when the aluminum was a target. Experimental study on the effect electrodes material, applied voltages on spectroscopic parameter for DC discharge plasma in Nitrogen gas using planner electrodes were done.

     The electron temperature, increase with increasing applied voltage from (700 to 1100) V. While the plasma density, calculate by Stark broadening effect, which increase with it.

     The peaks intensities for N2 transition (λ= 336.6 nm and 391.4 nm) increase with increasing applied voltage. The vibrational energy (TVib) for N2 molecular increase from 0.165 to 0.185 eV

     The goal of this work is to study plasma parameters for Fe plasma generated by exploding wire (EEW) in carbon nanotubes-water colloid with three current values (50, 100 and 150)A. In this research, the plasma electron temperature (T_e), the electron density (n_e), electron density (n_e), plasma frequency(f _p), Debye length (λ_D) and Debye number (N_D) were  found for Fe produced by Arc discharge plasma. Boltzmann plot was used to calculate the plasma electron temperature (T_e);electron density (n_e) was calculated from  Stark broadening. It was found that the electron temperature values increased from (0.4

Titanium alloy (Ti-6Al-4V) samples were nitrided in low pressure (1.3, 3 mbar) dc-glow discharge plasmas of nitrogen. The treating time was 5, 10 and 15 hour and the temperatures range of the samples during the nitriding process was close to 800oC. The obtained microstructures of the nitride layers were studied by x-ray diffraction and optical microscopy. The ε –Ti2N, ζ-Ti3N3-x and η-Ti3N2-x.phases were formed and addition to the solid solution of nitrogen in titanium, α (Ti,N). Micro hardness measurements exhibit an increment for the Ti-alloy specimens which nitrided at 800oC for 10 and 15h.Corrosion measurements were obtained for the Ti-6Al-4V alloy in Ringer solution after plasma nitriding. The clear improving in the corrosion r

       In this study, the surface of the epoxy/Al composite is treated using a dielectric barrier discharge (DBD) plasma in the presence of air. The epoxy composite was prepared by mixing 0.1g and 0.3 g aluminum powder with epoxy resin and its hardener in a ratio of 3:1. The surface epoxy/Al composite as a dielectric barrier layer (DB) is studied at an applied frequency of 8 kHz and at three exposure times 0, 2, and 4 min. The UV degradation process has been studied using UV-Visible spectroscopy, for these polymers. The absorbance intensity in the UV region (200–320 nm) was high. The absorbance level decreased after 2 minutes and increased after 4 min exposure time. Before exposure to plasma, the epoxy/Al composite at 0.1 g Al ha

     Cadmium Selenide (CdSe) thin films have been deposited on a glass substrate utilizing the plasma DC-sputtering method at room temperature at different deposition time in order to achieve different films thickness, and studied its sensitivity to the  carbon monoxide CO gas which are show high response as the film thickness increases, the DC-conductivity and photoconductivity are also studied and which are increased too as the film thickness increases, that indicates the good semiconducting behavior at room  temperature and light environments.

The method of powder technology has been utilized for fabrication of ceramic filters. Ceramic filters with interconnected porosity have been achieved via mixes of ceramic powders with addition of glass powders, therefore, interparticle glassy phase is introduced and act as a weld between the crystalline grains in a high porosity microstructure. Tow types of ceramic filters have been produced, the first with high silica content and the other is with high alumina content. Both physical and mechanical properties has been performed and discussed

This research investigates manganese (Mn) extraction from Electric Arc Furnace Steel Slag (EAFS) by using the Liquid-liquid extraction (LLE) method. The chemical analysis was done on the slag using X-ray fluorescence, X-ray diffraction, and atomic absorption spectroscopy. This work consisted of two parts: the first was an extensive study of the effect of variables that can affect the leaching process rate for Mn element from slag (reaction time, nitric acid concentration, solid to liquid ratio, and stirring speed), and the second part evaluates the extraction of Mn element from leached solution. The results showed the possibility of leaching  83.5 % of  Mn element from the slag at a temperature of 25°C, nitric acid co

    The efficiency of solar energy absorption in solar heaters is increased by the use of selective absorption coating that possesses high absorption of solar radiation in the UV-visible spectrum as well as low emission at the operating temperature in the infrared region. In this work, novel selective coatings were synthesized by improving the selectivity of chromium oxide (Cr₂O₃) nanoparticles by doping with carbon nanoparticles using the exploding wire technique for carbon rods by high current in suspended Cr₂O₃ particles. The structural properties and surface topography were studied by XRD and FE-SEM, which illustrate the carbon-coated Cr₂O₃ nanoparticles. The prepar