The Non-thermal plasma has a wide range of applications in different areas. In this study, the oxidation of a model fuel containing organo-sulfur compounds (benzothiophene and dibenzothiophene) was investigated using plasma. The process involved ozone generation through dielectric barrier discharge, followed by extraction using acetonitrile. The results demonstrated the efficient oxidation and removal of dibenzothiophene and benzothiophene by non-thermal plasma. The desulfurization efficiency reached 93.78% under the optimum conditions, including a voltage of 11Kv, temperature of 50ºC, duration of 4 hours, and a flow rate of 75 ml/min.

The purpose of this study is to investigate the biostimulation effect of 532 nm CW laser on the metabolism of Saccharomyces cerevisiae yeast. Cells were irradiated by 532 nm Nd:YAG laser using 0.153 W/cm2 power density at 30, 45, 60,180 and 300 seconds exposure times in their respective orders. Intrafluorescence parameters were measured by detection the autofluorescence intensity, proliferation rate and Imaging the fluorescent mitochondria using confocal laser scanning microscope. The results showed that the 30 and 45 second exposure times seem to have stimulated changes in the cells that led to increase proliferation, viability and mitochondrial activity. Autofluorescence of cells increased after 45 and 60 seconds exposure time. After 3

Background/purpose: Dental implantology involves different treatments that have been used in conjunction with dental implant surgery to increase implant stability and bone regeneration process. Photobiomodulation( PBM) can be one of these techniques. The objective of this study was to evaluate the bone density around implants. Materials and methods: in this study, 10 individuals had 20 implants inserted in the posterior of their mandibles. each patient received two implants the left side served as the control whereas the right side served as the study group with a diode laser (same patients). measurements were made for each implant. Measurements were obtained using cone-

Background: Polymethyl methacrylate (PMMA) is the most commonly used material in denture fabrication. The material is far from ideal in fulfilling the mechanical requirements, like low impact and transverse strength, poor thermal conductivity. The purpose of this study was to evaluate the effect of addition a composite of surface treated Nano Aluminum oxide (Al2O3) filler and plasma treated polypropylene fiber (PP) on some properties of denture base material. Materials and methods: One hundred fifty prepared specimens were divided into 5 groups according to the tests, each group consisted of 30 specimens and these were subdivided into 3 groups (unreinforced heat cured acrylic resin as control group),reinforced acrylic resin with( 0.5%wt Nan

Abstract: Tin oxide thin films were deposited by direct current (DC) reactive sputtering at gas pressures of 0.015 mbar – 0.15 mbar. The crystalline structure and surface morphology of the prepared SnO2 films were introduced by X-ray diffraction (XRD) and atomic force microscopy (AFM). These films showed preferred orientation in the (110) plane. Due to AFM micrographs, the grain size increased non-uniformly as the working gas pressure increased.

Titanium alloy (Ti-6Al-4V) samples were nitrided in low pressure (1.3, 3 mbar) dc-glow discharge plasmas of nitrogen. The treating time was 5, 10 and 15 hour and the temperatures range of the samples during the nitriding process was close to 800oC. The obtained microstructures of the nitride layers were studied by x-ray diffraction and optical microscopy. The ε –Ti2N, ζ-Ti3N3-x and η-Ti3N2-x.phases were formed and addition to the solid solution of nitrogen in titanium, α (Ti,N). Micro hardness measurements exhibit an increment for the Ti-alloy specimens which nitrided at 800oC for 10 and 15h.Corrosion measurements were obtained for the Ti-6Al-4V alloy in Ringer solution after plasma nitriding. The clear improving in the corrosion r